Due to the recent widespread application of nanomaterials to biological systems, a careful consideration of their physiological impact is required. This demands an understanding of the complex processes at the bio–nano interface. Therefore, a comprehensive and accurate characterization of the material under physiological conditions is crucial to correlate the observed biological impact with defined colloidal properties. As promising candidates for biomedical applications, two SiO2-based nanomaterial systems were chosen for extensive size characterization to investigate the agglomeration behavior under physiological conditions. To combine the benefits of different characterization techniques and to compensate for their respective drawbacks, transmission electron microscopy, dynamic light scattering and asymmetric flow field-flow fractionation were applied. The investigated particle systems were (i) negatively charged silica particles and (ii) poly(organosiloxane) particles offering variable surface modification opportunities (positively charged, polymer coated). It is shown that the surface properties primarily determine the agglomeration state of the particles and therefore their effective size, especially under physiological conditions. Thus, the biological identity of a nanomaterial is clearly influenced by differentiating surface properties.
The acid catalyzed solgel type synthesis of polyorganosiloxane core-shell nanoparticles with removable PDMS core in aqueous dispersion leads to the inherent formation of a bimodal size distribution with smaller spheres having approximately 26 nm radii and larger nanoparticles with 60 nm in radius. The origin of the self-organized bimodality is investigated and finally attributed to a combination of stabilization of the growing particles due to i) a miniemulsion-type stabilization by the ultrahydrophobe PDMS and ii) by surface co-stabilization by the employed surfactant. The significant influence of temperature, pH, stirrer speed and amount of the surfactant on the particle sizes allows for the design and fine-tuning of different nanoparticles sizes and distributions.
Here, we present the synthesis, characterization and magnetic separation of magnetic polyorganosiloxane nanoparticles. Magnetic iron oxide nanoparticles with average particle radii of 3.2 nm had been synthesized by a simple coprecipitation process of iron(II) and iron(III) salt in basic solution. Afterwards, the particles were successfully incorporated into a polyorganosiloxane network via a polycondensation reaction of trimethoxymethylsilane (T), diethoxydimethylsilane (D) and the functional monomer (chloromethylphenyl)trimethoxysilane (ClBz-T) in aqueous dispersion. A core–shell system was chosen to increase the flexibility of the system concerning size, composition and functionalization possibilities. The magnetic nanocapsules with particle radii below 60 nm were separated from non-magnetic material with a high effectiveness by the use of commercially available separation columns which are commonly used for isolation of microbeads and subsequently characterized via transmission electron microscopy (TEM), asymmetrical flow field-flow fractionation (AF-FFF), superconducting quantum interference device (SQUID) and Mössbauer spectroscopy.