Using 22 metal triflates as catalysts, ε-caprolactone is polymerized at 22 °C in bulk. Only five relatively acidic triflates prove active. Three triflates, including the neutral Sm3+, are active using water as initiator. A very low content of cyclics is found in all the experiments. With Ce3+ and Ce4+, polymerizations are performed in CH2Cl2 and in bulk at 2 °C and 22 °C. Low dispersities (down to 1.1) are obtained. At 22 °C, Ce4+ and, even better, Ce3+ also catalyze syntheses of CO2H- and CH2OH-terminated polycaprolactones, whereby higher dispersities and larger fractions of cyclics are obtained. Further polymerizations and polycondensations are catalyzed with protic acids. The results can be explained by a proton-catalyzed activated monomer mechanism.
Poly(alkylene isophthalate)s were prepared by different methods, either in solution or in bulk. The SEC measurements were evaluated in such a way that all oligomers were included. In solution (monomer conc. 0.10.7 mol/L) large fractions of rings were formed and high dispersities (up to 12) were obtained, which disagree with theoretical predictions. Polycondensations in bulk did neither generate cyclics by 'back-biting' nor by end-to-end cyclization, when the maximum temperature was limited to 210 °C. The dispersities of these perfectly linear polyesters were again higher than the theoretical values. Regardless of the synthetic method monomeric cycles were never observed. Furthermore, SEC measurements performed in tetrahydrofuran and in chloroform and SEC measurements performed in three different institutes were compared. Finally, SEC measurements of five samples were performed with universal calibration and a correction factor of 0.71 ± 0.02 was found for normal calibration with polystyrene.
Using three different catalysts, water-initiated polymerizations of ε-caprolactone were conducted in bulk with variation of the monomer/water ratio. The resulting CH2OH and CO2H- terminated polylactones were subjected in situ to azeotropic polycondensations. With Bi-triflate and temperatures, the polycondensations were not much successful and involved side reactions. With ZnCl2, and especially SnCl2, considerably higher molar masses were achieved. The substitution of toluene for chlorobenzene for refluxing gave better results. The polycondensations broadened the molar mass distribution of the ROP-based prepolymers, and polydispersities between 1.4–1.8 were obtained. The MALDITOF mass spectra revealed that the polycondensations significantly enhanced the fraction of rings due to efficient 'end-biting' reactions. By comparison with copolymerization experiments and Sn methoxide-initiated polymerizations, it was demonstrated that equilibration reactions, such as the formation of rings by 'back-biting,' did not occur.
Various copolyesters of lactide, isosorbide, and terephthalic acid are prepared by a two-step process performed in a 'one-pot' procedure, beginning with an isosorbide-initiated oligomerization of L-lactide followed by polycondensation with terephthaloyl chloride using SnCl2 as a catalyst for both steps. The SEC data show the formation of random copolyesters with high polydispersities as a consequence of the relatively high fraction of cyclics proved by matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOF MS). The glass-transition temperatures (89–180 °C) obey an almost linear trend with the molar composition. The thermostability decreases with increasing lactide content. The successful incorporation of phenyl phosphate results in copolyesters of lower inflammability.
Using SnCl2, ZnCl2, Zn-lactate or Zr-acetylacetonate as catalysts ʟ-lactide was oligomerized in bulk with isosorbide as initiator. The ratio isosorbide/lactide was varied from 8/2 to 2/8. The resulting oligomers were in situ polycondensed with isophthaloyl chloride in various aromatic solvents. In chlorobenzene homogeneous reaction mixtures were obtained, whereas molten copolyesters precipitated from toluene and xylene. The obtained average molecular weights indicated high polydispersities. According to MALDI-TOF MS the low molar mass reaction products (<4 kDa) almost exclusively consisted of cyclics with a composition depending on the feed ratio. The glass-transition temperatures (Tg) varied between the values of poly(ʟ-lactide (64 °C) and poly(isosorbide isophthalate) (180 °C). Four polyesters prepared from 5-tert-butyl isophthalic acid displayed higher Tg values. Differential thermoanalysis evidenced that the thermostability decreases with higher fractions of lactide, but processing from the melt seems to be feasible up to temperatures of 260 °C without risking degradation.
Poly(ether sulfone)s were prepared by polycondensation of silylated 4-tert-butylcatechol and 4,4?-difluorodiphenylsulfone in N-methylpyrrolidone. The feed ratio and the reaction time were varied to study the influence of stoichiometry and conversion on molecular weight and extent of cyclization. Molecular weights and molecular weight distributions (MWD)s were characterized by SEC measurements calibrated with polystyrene. Light scattering confirmed that calibration with polystyrene gives reasonable results and revealed a tendency towards a bimodal MWD for the samples rich in cycles. The MALDI-TOF mass spectrometry indicated that the extent of cyclization increased with higher conversion and with optimization of the stoichiometry. This interpretation was confirmed by 1H NMR endgroup analyses. For the samples with the highest molar masses only mass peaks of cycles were found, which were detectable up to 20 000 Da before and up to 27 000 Da after fractionation. Via the pseudo-high dilution method low molar mass poly(ether sulfone) containing more than 95 mol% of cycles were prepared, and even these low molar mass samples had broad MWDs. DSC measurements indicated that the glass transition temperatures depend on the structure of the endgroups and increase with higher fractions of cycles.
Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates
(2014)
Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition.
Various dibutyltin derivatives were polycondensed with aliphatic ,-dicarboxylic acids having chain lengths from 4 (succinic acid) to 22 carbon atoms. White crystalline products were obtained from all experiments, and the structure of the products was independent of the synthetic method. Viscosity measurements revealed low molecular weights (n 1 500 Da) in all cases. Vapor pressure osmometry (VPO) measurements and matrix-assisted laser desorption time-of-flight (MALDI-TOF) mass spectrometry proved that cyclic dimers and trimer were formed from dicarboxylic acids having 6 to 16 carbons, but mainly the monomeric cycle from docosane dioic acid. Heating to 250°C did not change the structure. Therefore, the results indicate that the macrocycles are the result of a thermodynamically controlled ring-closing polycondensation. This means that linear high-molecular weight poly(dibutyltin dicarboxylate)s cannot exist above room temperature.