The formation of nearly wavelength-sized laser-induced periodic surface structures (LIPSS) on
single-crystalline silicon upon irradiation with single (N = 1) and multiple (N ≤ 1000) linearly
polarized femtosecond (fs) laser pulses (pulse duration τ = 130 fs, central wavelength λ = 800 nm)
in air is studied experimentally. Scanning electron microscopy (SEM) and optical microscopy are
used for imaging of the ablated surface morphologies, both revealing LIPSS with periodicities close
to the laser wavelength and an orientation always perpendicular to the polarization of the fs-laser
beam. It is experimentally demonstrated that these LIPSS can be formed in silicon upon irradiation
by single fs-laser pulses—a result that is additionally supported by a recent theoretical model.
Two-dimensional Fourier transforms of the SEM images allow the detailed analysis of the
distribution of the spatial frequencies of the LIPSS and indicate, at a fixed peak fluence, a
monotonous decrease in their mean spatial period between ~770 nm (N = 1) and 560 nm (N
= 1000). The characteristic decrease in the LIPSS period is caused by a feedback-mechanism acting
upon excitation of surface plasmon polaritons at the rough silicon surface which is developing under
the action of multiple pulses into a periodically corrugated surface.
Glass bricks are important transparent building materials. They are produced by joining two halves of glass pressings at 600700 °C. During this production process alkali oxides evaporate and are redeposited at the cooler inner front surfaces of the bricks. This surface layer reacts with H2O and CO2 from the residual brick atmosphere, leading to the formation of an alkali-rich silicate-hydrate layer of ≥50 nm thickness, which could be evidenced leading to a reduced nano-hardness of similar thickness, and from which NaHCO3 crystals can finally grow. Climate chamber experiments (repeated cooling between at -8 and -14 °C and reheating to 0 to 15 °C) resulted in reversible NaHCO3 crystallization and redissolution, presumably influenced by water evaporation or condensation and driven by the NaHCO3 supersaturation of the silicate-hydrate layer. Depending on the timetemperature schedule, different crystal morphologies became visible in this closed system, e.g. isolated spherical crystals, crystals arranged in chains and in double-chains, respectively, which can limit already the transmittance of the glass bricks. When a crack occurs or the brick is opened, the hygroscopic NaHCO3 crystals take up more H2O from the ambient, react irreversibly with the glass surface, finally leading to a total loss of transmittance.
In this paper the characterisation of functionally graded materials is elucidated by several different methods. These methods described here are used for the quantitative analysis of materials with a local dependence of microstructure parameters. Using X-ray microscopy (computed tomography) for 3D-measurements and optical microscopy on polished sections for 1D and 2D measurements on the same sample, a ceramic filter consisting of sintered spherical particles, various mathematical evaluation methods are described and compared.