A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′ -phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 〈011〉{111} octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′ -reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2 〈011〉 mobile dislocations and knitting of new networks.
Kirkendall porosity that forms during interdiffusion in a diffusion couple of nickel-base superalloy CMSX-10 with pure nickel is investigated. The diffusion experiments are conducted at a temperature of 1250 °C, where the strengthening ƴ'-phase ist partially dissolved. The porosity is studied by X-ray sub-μ tomography with a spatial resolution of about 0.35³ μm³ at the European Synchrotron Radiation Facility (ESRF) in Grenoble, France. It is found that depending on the distance from the interface the Kirkendall pores take different shapes: octahedral, rounded pyramidal, drop shaped, dendritic, pear shaped, and joint shapes. Such a variety of pore morphologies indicates a complex multistage process of porosity nucleation and growth under vacancy supersaturation of different degrees. The experimental findings are interpreted on the basis of the results of diffusion modeling. It is shown that the kinetics of porosity growth is essentially influenced by the dissolution of the ƴ'-phase.
Dissimilar metal weld overlays of nickel-base alloys on low-alloy steel components are commonly used in the oil and gas, petrochemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service Environments and temperatures. Traditionally, dissimilar weld overlays are produced using cold or hot wire gas tungsten arc welding.
This study aims to identify and evaluate potential advantages of low heat input gas metal arc welding processes over the conventional gas tungsten arc welding in the production of such overlays. Parts I and II of this publication series described characteristics of the heat-affected zone and the transition zone region of alloy 625 on grade 22 steel overlays. These results indicate a good resistance against hydrogen-assisted cracking, which is being verified within this third part of the publication series. To determine the hydrogen-assisted cracking susceptibility, welded samples are tested using the delayed hydrogen-assisted cracking test. Fractography is performed using scanning electron microscopy along with energy dispersive spectroscopy. The results confirm the suitability and efficiency of low heat input gas metal arc welding for dissimilar weld overlays. Variation of the postweld heat treatment procedure bears potential for improvement in this respect.
Dissimilar metal weld overlays of nickel-base alloys on low-alloy steel components are commonly used in the oil and gas, petrochemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service Environments and temperatures. Traditionally, dissimilar weld overlays are produced using cold or hot wire gas tungsten arc welding.
This study aims to identify and evaluate potential advantages of low heat input gas metal arc welding processes over the conventional gas tungsten arc welding in the production of such overlays. Parts I and II of this publication series described characteristics of the heat-affected zone and the transition zone region of alloy 625 on grade 22 steel overlays. These results indicate a good resistance against hydrogen-assisted cracking, which is being verified within this third part of the publication series. To determine the hydrogen-assisted cracking susceptibility, welded samples are tested using the delayed hydrogen-assisted cracking test. Fractography is performed using scanning electron microscopy along with energy dispersive spectroscopy. The results confirm the suitability and efficiency of low heat input gas metal arc welding for dissimilar weld overlays. Variation of the postweld heat treatment procedure bears potential for improvement in this respect.
A new technique for investigation of interfacial dislocations in nickel-base superalloys by scanning electron microscopy is presented. At high temperatures the pressure of interfacial dislocations against the gamma/gamma'-interface causes grooves. This 'fingerprint of the dislocation network' is visualized by deep selective etching, which removes the gamma'-phase down to the gamma/gamma'-interface. Compared with transmission electron microscopy, the proposed method has important advantages: observation of large sample areas, no superposition of dislocations lying in different specimen depths, possibility of three-dimensional view of dislocation configurations, information about the dislocation mobility, reduced time for preparation and visualization. The method can be applied for multiphase materials where the interface is grooved by interfacial dislocations.
Dissimilar metal weld overlays of nickel base alloys on low alloy steel components are commonly used in the oil and gas, petro-chemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service environments and temperatures. Traditionally, weld overlays are produced using cold or hot wire gas tungsten arc welding (GTAW). Potential advantages of cold metal Transfer (CMT) welding, a low heat input gas metal arc welding process, over the conventional GTAW in production of weld overlays were evaluated. Metallurgical characterization was performed on CMT overlays of Alloy 625 filler metal on Grade 11 and Grade 22 steels. Significant grain refinement was found in the high temperature HAZ compared to the traditional coarse-grained HAZ in arc welding. Evidences of incomplete carbide dissolution, limited carbon diffusion, and incomplete transformation to austenite were also found. These phenomena were related to high heating and cooling rates and short dwell times of the high-temperature HAZ in austenitic state. Tempering effects in the steel HAZ were identified, showing a potential for development of CMT temperbead procedures. Based on the results of this study, the steel HAZ regions in CMT overlays were classified as high-temperature HAZ and intercritical HAZ.
A x-ray radioscopy technique for measuring in situ chemical diffusion coefficients in metallic melts
is presented. The long-capillary diffusion measurement method is combined with imaging
techniques using microfocus tubes and flat panel detectors in order to visualize and quantitatively
analyze diffusive mixing of two melts of different chemical composition. The interdiffusion
coefficient as function of temperature and time is obtained by applying Ficks diffusion laws.
Tracking the time dependence of the mean square penetration depth of the mixing process allows to
detect changes in the mass transport caused by convective flow. The possibility to sort out
convective mass transport contributions from analysis enhances significantly the accuracy compared
to the conventional long-capillary diffusion measurement method with postmortem analysis. The
performance of this novel diffusion measurement method with x-ray radiography technique is
demonstrated by a diffusion experiment in an Al-Ni melt.
When dealing in ultrasonic testing with
inhomogeneous material structure data interpretation can be
rather difficult. This is especially the case when using anisotropic
dissimilar welds made from austenitic steel or nickel based alloys,
which are currently used for modern power plant concepts. In
this work we present an electrodynamic technique to visualize
sound waves with frequencies up to 3 MHz in steel components
providing a simple use and a high signal-to-noise ratio. By
detecting the grazing beam with an electrodynamic probe, we
measured the particle displacement as a function of time with a
spatial resolution in the order of 1 mm. Adapting the
electrodynamic probe and its coil alignment allows for measuring
the displacement components in all three dimensions. This
comprises the detection of the horizontal and vertical particle
displacement with respect to the surface and thus also the
transformation from longitudinal waves into transversal waves
and vice versa. We report on measurements of the sound field in
a complex narrow-gap weld, joining a nickel alloy with a chrome
steel with a substantial anisotropy of the weld structure. The test
system enables us to visualize the wave propagation within the
weld and indicates the reflection scenario and the energy losses
due to both the anisotropic structure and material defects.
A new technique for investigation of interfacial dislocations in nickel-base superalloys by scanning electron microscopy is presented. At high temperatures the pressure of interfacial dislocations against the γ/γ'-interface causes grooves. This 'fingerprint of the dislocation network' is visualized by deep selective etching, which removes the γ'-phase down to the γ/γ'-interface. Compared with transmission electron microscopy, the proposed method has important advantages: observation of large sample areas, no superposition of dislocations lying in different specimen depths, possibility of three-dimensional view of dislocation configurations, information about the dislocation mobility, reduced time for preparation and visualization. The method can be applied for multiphase materials where the interface is grooved by interfacial dislocations.