Eingeladener Vortrag
- nein (1)
The presentation shows how the three-dimensional quantification of dislocations and their characteristic features, e.g. Burgers vector, line direction, dislocation density, is carried out at the transmission electron microscope in scanning mode (STEM) at Division 5.1 at BAM. Exemplarily, the methods are shown for Ni-base superalloy single crystals, for which a short introduction is given using further TEM techniques. Additional examples on low angle grain boundaries, nucleation of oxides at dislocations and interaction of dislocations and carbides are shown.
The content of the presentation was addapted, aiming at scientists who work within the DFG Priority Programme 1713 "Strong coupling of thermo-chemical and thermo-mechanical states in applied materials".
Experimental study on M23C6 nucleation and growth mechanisms in Ni-base superalloy single crystals
(2017)
The addition of carbon to Ni-base superalloy single crystals has been increasingly carried out to improve low angle grain boundary (LAGB) resistance and castability. Consequently, the precipitation of carbides is highly probable during long-term application of components subjected to higher temperatures (> 1000 °C). While the view on the role of carbides as strengthening or detrimental is polemical, their inevitable increased presence in carbon-doped alloys must be addressed. In the present work, the evolution of M23C6 carbides forming in the commercial grade Ni-base superalloy LEK 94 during high-temperature and low-stress creep exposure is assessed. Although carbon is not intentionally added to the LEK 94 alloy, it admits up to 0.1 at. %, which together with the high content of M23C6-forming transition metals, leads to their precipitation. The precipitation is induced here during creep experiments at 1020 °C and a nominal applied stress of 160 MPa along [001]. The correlation of precipitation and external load is carried out by evaluating the carbides in the gage section of parallel and circularly notched cylindrical samples, as well as in their heads. Characterization is made by transmission electron microscopy (TEM). Although primary MC carbides form mostly in interdendritic regions during casting, high temperature exposure induces M23C6 carbide nucleation especially in the γ phase of dendritic regions, where a stronger partitioning of refractory elements is present. The carbides have a needle shape with their main axis on 〈100〉 and a cube-on-cube orientation relationship. They present incoherent {100} facets along their elongated region and semi-coherent {111} facets at their ends. Their nucleation and growth mechanisms are discussed based on microstructural observation under different experimental conditions.
Mechanism of porosity growth during homogenisation in single crystal nickel-based superalloys
(2013)
Several mechanisms for porosity growth in single crystal nickel-based superalloys during homogenisation heat treatment have been proposed in the literature. They were carefully checked using different experimental methods, namely quantitative light microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and density measurements. It is shown that the main mechanism is the Kirkendall–Frenkel effect, i.e. generation of voids due to uncompensated efflux of Al atoms from dissolving γ/γ′-eutectic areas. The Al diffusion is supported by the afflux of vacancies from surrounding γ-matrix which results in porosity growth. This conclusion is confirmed by the estimation of the vacancy afflux towards the dissolving eutectic.
Optical and scanning electron microscopy, as well as electron microprobe analysis and electron backscatter diffraction, have been used to study diffusion processes that occur in a diffusion pair that consistsof a single-crystal CMSX-10 nickel-base superalloy and polycrystalline nickel, at temperatures of 1050–1250°C. It has been found that, in this system, the distributions of γ-stabilizing elements (Cr, Co, W, and Re) are described by the Boltzmann solution for diffusion between two semiinfinite plates of a binary alloy. The processing of these distributions has shown that the diffusion coefficients of Cr, Co, W, and Re in the multicomponent system are close to those in binary alloys of these elements with Ni. The diffusion redistribution of the elements leads to the dissolution of the γ′ phase in the nickel-base superalloy, growth of nickel grains toward the superalloy constituent of the diffusion pair, and the formation of porosity on both sides of the migrating interface, which is determined from a crystal misorientation of the alloy single crystal and nickel grains.
Material modelling and lifetime prediction of Ni-base gas turbine blades under TMF conditions
(2014)
Under cyclic thermomechanical loading conditions, various damage mechanisms such as strain accumulation, creep cavitation, ageing, fatigue surface cracking etc. may take place in the material of a gas turbine blade. Depending on the loading conditions, all these effects can contribute to reduce the lifetime of the component. Subject of the present work is the development of a material model to describe the mechanical effects mentioned above, as well as the development of a lifetime model able to discriminate the different damage mechanisms.
SC16 at 950°C under LCF loading on smooth cylindrical specimen: influence of secondary orientation
(2008)
Thermo-mechanical fatigue (TMF) testing plays an increasingly important role in the design, the reliability assessment and the lifecycle management of safety critical components used, for instance, for power generation, in the process industry and in aeronautical and automotive applications, with a view to increasing the fuel efficiency, safety and service intervals, while reducing production (and material) costs. In a European Commission funded research project (acronym: TMF-Standard) of the 5th Framework Programme, 20 European laboratories have undertaken a joint research effort to establish a validated code-of-practice (CoP) for strain-controlled TMF testing. Starting from a survey of the testing protocols and procedures previously used by the partners, a comprehensive pre-normative research activity into various issues has been completed, addressing the dynamic temperature control, the effects of deviations in nominal temperatures and phase angles, the influences of temperature gradients, as well as the practicalities of test interruption and restart procedures. Meaningful allowable tolerances for the various test parameters were identified and practical recommendations as to the test techniques were formulated. From this a preliminary CoP was compiled and used to guide an extensive round robin exercise among the project partners. From the statistical analysis of that exercise, a validated CoP was derived dealing with strain-controlled constant amplitude TMF of nominally homogeneous metallic materials subjected to spatially uniform temperature fields and uniaxial mechanical loading. It is intended to give advice and guidance on the appropriate test setup, testing procedures and the analysis of results, in particular for newcomers in the field of strain-controlled TMF. This paper highlights some of the results of the TMF-Standard project. Moreover, commonalities and differences of the present CoP with respect to the standard documents for strain-controlled TMF, which have been developed at ISO and ASTM levels, are presented in this paper.