Great complexity characterizes Additive Manufacturing (AM) of metallic components via laser powder bed fusion (PBF-LB/M). Due to this, defects in the printed components (like cracks and pores) are still common. Monitoring methods are commercially used, but the relationship between process data and defect formation is not well understood yet. Furthermore, defects and deformations might develop with a temporal delay to the laser energy input. The component’s actual quality is consequently only determinable after the finished process.
To overcome this drawback, thermographic in-situ testing is introduced. The defocused process laser is utilized for nondestructive testing performed layer by layer throughout the build process. The results of the defect detection via infrared cameras are shown for a research PBF-LB/M machine.
This creates the basis for a shift from in-situ monitoring towards in-situ testing during the AM process. Defects are detected immediately inside the process chamber, and the actual component quality is determined.
Learned block iterative shrinkage thresholding algorithm for photothermal super resolution imaging
(2022)
Block-sparse regularization is already well known in active thermal imaging and is used for multiple-measurement-based inverse problems. The main bottleneck of this method is the choice of regularization parameters which differs for each experiment. We show the benefits of using a learned block iterative shrinkage thresholding algorithm (LBISTA) that is able to learn the choice of regularization parameters, without the need to manually select them. In addition, LBISTA enables the determination of a suitable weight matrix to solve the underlying inverse problem. Therefore, in this paper we present LBISTA and compare it with state-of-the-art block iterative shrinkage thresholding using synthetically generated and experimental test data from active thermography for defect reconstruction. Our results show that the use of the learned block-sparse optimization approach provides smaller normalized mean square errors for a small fixed number of iterations. Thus, this allows us to improve the convergence speed and only needs a few iterations to generate accurate defect reconstruction in photothermal super-resolution imaging.
The work to be presented focuses on our most recent studies to laser excited super resolution (SR) thermography. The goal of nondestructive testing with SR is to facilitate the separation of closely spaced defects. Photothermal SR can be realized by performing structured illumination measurements in com-bination with the use of deconvolution algorithms in post-processing. We explain that stepwise as well as continuous scanning techniques are applicable to generate structured illumination measurements. Finally, we discuss the effect of experimental parameters and image processing techniques to find the optimal SR technique which leads to the highest reconstruction quality within laser thermography.
The work to be presented focuses on our most recent studies to laser excited super resolution (SR) thermography. The goal of nondestructive testing with SR is to facilitate the separation of closely spaced defects. Photothermal SR can be realized by performing structured illumination measurements in com-bination with the use of deconvolution algorithms in post-processing. We explain that stepwise as well as continuous scanning techniques are applicable to generate structured illumination measurements. Finally, we discuss the effect of experimental parameters and image processing techniques to find the optimal SR technique which leads to the highest reconstruction quality within laser thermography.
This paper presents deep unfolding neural networks to handle inverse problems in photothermal radiometry enabling super resolution (SR) imaging. Photothermal imaging is a well-known technique in active thermography for nondestructive inspection of defects in materials such as metals or composites. A grand challenge of active thermography is to overcome the spatial resolution limitation imposed by heat diffusion in order to accurately resolve each defect. The photothermal SR approach enables to extract high-frequency spatial components based on the deconvolution with the thermal point spread function. However, stable deconvolution can only be achieved by using the sparse structure of defect patterns, which often requires tedious, hand-crafted tuning of hyperparameters and results in computationally intensive algorithms. On this account, Photothermal-SR-Net is proposed in this paper, which performs deconvolution by deep unfolding considering the underlying physics. This enables to super resolve 2D thermal images for nondestructive testing with a substantially improved convergence rate. Since defects appear sparsely in materials, Photothermal-SR-Net applies trained blocksparsity thresholding to the acquired thermal images in each convolutional layer. The performance of the proposed approach is evaluated and discussed using various deep unfolding and thresholding approaches applied to 2D thermal images. Subsequently, studies are conducted on how to increase the reconstruction quality and the computational performance of Photothermal-SR-Net is evaluated.
Thereby, it was found that the computing time for creating high-resolution images could be significantly reduced without decreasing the reconstruction quality by using pixel binning as a preprocessing step.
Classification of Spot-Welded Joints in Laser Thermography Data Using Convolutional Neural Networks
(2021)
Spot welding is a crucial process step in various industries. However, classification of spot welding quality is still a tedious process due to the complexity and sensitivity of the test material, which drain conventional approaches to its limits. In this article, we propose an approach for quality inspection of spot weldings using images from laser thermography data. We propose data preparation approaches based on the underlying physics of spot-welded joints, heated with pulsed laser thermography by analyzing the intensity over time and derive dedicated data filters to generate training datasets. Subsequently, we utilize convolutional neural networks to classify weld quality and compare the performance of different models against each other. We achieve competitive results in terms of classifying the different welding quality classes compared to traditional approaches, reaching an accuracy of more than 95 percent. Finally, we explore the effect of different augmentation methods.
Crack detection in steel bars at high surface temperatures is a critical problem in any manufacturing industry. Surface breaking cracks are the major problems during the billet casting. Many NDT techniques are proven its capability in crack detection at room temperature. Here, we are demonstrating the possibility of exposure of cracks using laser line thermography at higher surface temperatures (up to 600 °C). A continuous-wave (CW) laser is used to excite the sample kept at higher surface temperatures. The temperature distribution over the sample due to the laser line scanning is captured using a temperature calibrated infrared (IR) thermal camera. The response of the sample temperature in crack detection is investigated using a validated FE model. The impact of the oxide layer in crack detection is investigated by using two types of samples; one without any oxide layer and the second is with the oxide layer. The influence of laser power in the detection of defects at high temperatures is studied. 3D numerical models were developed for the cases; when the sample is with oxide layer and without any oxide layer for a better understanding of physics. The surface temperature rise due to laser heating is higher for the scaled sample compared to the no-scale sample. The presence of the oxide layer above the parent metal will reduce the reflectivity of the surface. Lower reflectivity will lead to increased absorption of incident energy so that the surface temperature rise will be higher than the surface with no scale. Thermal contrast linearly depends on laser power, which means higher laser power will increase the defect detectability even at a higher surface temperature.
In this paper we propose super resolution measurement and post-processing strategies that can be applied in thermography using laser line scanning. The implementation of these techniques facilitates the separation of two closely spaced defects and avoids the expected deterioration of spatial resolution due to heat diffusion. The experimental studies were performed using a high-power laser as heat source in combination with pulsed thermography measurements (step scanning) or with continuous heating measurements (continuous scanning). Our work shows that laser line step scanning as well as continuous scanning both can be used within our developed super resolution (SR) techniques. Our SR techniques make use of a compressed sensing based algorithm in post- processing, the so-called iterative joint sparsity (IJOSP) approach. The IJOSP method benefits from both - the sparse nature of defects in space as well as from the similarity of each measurement. In addition, we show further methods to improve the reconstruction quality e.g. by simple manipulations in thermal image processing such as by considering the effect of the scanning motion or by using different optimization algorithms within the IJOSP approach. These super resolution image processing methods are discussed so that the advantages and disadvantages of each method can be extracted. Our contribution thus provides new approaches for the implementation of super resolution techniques in laser line scanning thermography and informs about which experimental and post-processing parameters should be chosen to better separate two closely spaced defects.
In this work we focus on our most recent studies to super resolution (SR) laser thermography. The goal of SR nondestructive testing methods is to facilitate the separation of closely spaced defects. We explain how to combine laser scanning with SR techniques. It can be shown that stepwise as well as continuous scanning techniques are applicable. Finally, we discuss the effect of experimental parameters and im-age processing techniques to find the optimal SR technique which leads to the highest reconstruction quality within laser thermography.
This paper presents different super resolution reconstruction techniques to overcome the spatial resolution limits in thermography. Pseudo-random blind structured illumination from a onedimensional laser array is used as heat source for super resolution thermography. Pulsed thermography measurements using an infrared camera with a high frame rate sampling lead to a huge amount of data. To handle this large data set, thermographic reconstruction techniques are an essential step of the overall reconstruction process. Four different thermographic reconstruction techniques are analyzed based on the Fourier transform amplitude, principal component analysis, virtual wave reconstruction and the maximum thermogram. The application of those methods results in a sparse basis representation of the measured data and serves as input for a compressed sensing based algorithm called iterative joint sparsity (IJOSP). Since the thermographic reconstruction techniques have a high influence on the result of the IJOSP algorithm, this paper Highlights their Advantages and disadvantages.