Filtern
Dokumenttyp
- Vortrag (16)
- Posterpräsentation (6)
- Zeitschriftenartikel (4)
- Beitrag zu einem Tagungsband (4)
Schlagworte
- Laser Powder Bed Fusion (30) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (23)
- 9 Komponentensicherheit (18)
- 8.0 Abteilungsleitung und andere (16)
- 8.5 Röntgenbildgebung (13)
- 9.6 Additive Fertigung metallischer Komponenten (8)
- 9.3 Schweißtechnische Fertigungsverfahren (6)
- 9.4 Integrität von Schweißverbindungen (6)
- 5 Werkstofftechnik (4)
- 5.1 Mikrostruktur Design und Degradation (4)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
Eingeladener Vortrag
- nein (16)
Residual stresses Analysis in Additively Manufactured alloys using neutron diffraction (L-PBF)
(2023)
An overview of recent progress at BAM of residual stress analysis in additively manufactured, in particular Laser Powder Bed Fusion of metallics materials, using neutron diffraction will be presented. This will cover important topics of the stress-free reference, the diffraction elastic moduli and principal stress determination.
The industrialization of AM is only possible by creating synergy with the tools of Industry 4.0. The system technology of Powder Bed Fusion with Laser beam of Metals (PBF-LB/M) reached a level of high performance in terms of process stability and material spectrum in the past years. However, the digital process chain, starting from CAD via CAM and plant-specific compila-tion of the manufacturing file exhibits media disruptions. The consequence is a loss of metadata. A uniform data scheme of simulation for Design for Additive Manufacturing (DfAM), the PBF-LB/M process itself and quality assurance is currently not realized within industry. There is no entity in the common data flows of the process chains, that enables the integration of these functionalities. As part of the creation of a digital quality infrastructure in the QI-Digital pro-ject, an integration of the CAD/CAM chain is being established. The outcome is a file in an advanced commercially available format which includes all simula-tions and manufacturing instructions. The information depth of this file extends to the level of the scan vectors and allows the automatic optimization and holis-tic documentation. In addition, the KPI for the economic analysis are generated by compressing information into a unique file combined with the application of a digital twin. The implementation and advantages of this solution are demon-strated in a case study on a multi-laser PBF-LB/M system. A build job contain-ing a challenging geometry is thermally simulated, optimized, and manufac-tured. To verify its suitability for an Additive Manufacturing Service Platform (AMSP), the identical production file is transferred to a PBF-LB/M system of another manufacturer. Finally, the achieved quality level of the build job is evaluated via 3D scanning. This evaluation is carried out in the identical entity of the production file to highlight the versatility of this format and to integrate quality assurance data.
Laser powder bed fusion (PBF-LB/M) is a metal-based additive manufacturing (AM) process that utilizes a laser to melt powder particles selectively and form the desired product through a layer-by-layer fabrication process. It allows access to a vast new design space and can produce parts with far greater geometrical complexity than traditional methods. However, PBF-LB/M induces inevitable microstructural defects, such as voids and pores, that can adversely affect the quality and performance of the manufactured components. Hence, knowledge of pore formation, types, and suppression is essential for successful future AM applications. This research investigates the formation of different types of pores and their quantification from X-ray micro-computed tomography images of a formerly reported sample. It also examines the influence of the volumetric energy density (VED) on the size, shape, and location of pores for 316L stainless steel parts produced by the PBF-LB/M process.
The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.
Defects are still common in metal components built with Additive Manufacturing (AM). Process monitoring methods for laser powder bed fusion (PBF-LB/M) are used in industry, but relationships between monitoring data and defect formation are not fully understood yet. Additionally, defects and deformations may develop with a time delay to the laser energy input. Thus, currently, the component quality is only determinable after the finished process.
Here, active laser thermography, a non-destructive testing method, is adapted to PBF-LB/M, using the defocused process laser as heat source. The testing can be performed layer by layer throughout the manufacturing process. The results of the defect detection using infrared cameras are presented for a custom research PBF-LB/M machine. Our work enables a shift from post-process testing of components towards in-situ testing during the AM process. The actual component quality is evaluated in the process chamber and defects can be detected between layers.
Great complexity characterizes Additive Manufacturing (AM) of metallic components via laser powder bed fusion (PBF-LB/M). Due to this, defects in the printed components (like cracks and pores) are still common. Monitoring methods are commercially used, but the relationship between process data and defect formation is not well understood yet. Furthermore, defects and deformations might develop with a temporal delay to the laser energy input. The component’s actual quality is consequently only determinable after the finished process.
To overcome this drawback, thermographic in-situ testing is introduced. The defocused process laser is utilized for nondestructive testing performed layer by layer throughout the build process. The results of the defect detection via infrared cameras are shown for a research PBF-LB/M machine.
This creates the basis for a shift from in-situ monitoring towards in-situ testing during the AM process. Defects are detected immediately inside the process chamber, and the actual component quality is determined.
The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.
Die additive Fertigung von metallischen Bauteilen (Additive Manufacturing - AM; auch 3D-Druck genannt) bietet eine Vielzahl an Vorteilen gegenüber konventionellen Fertigungsmethoden. Durch den schichtweisen Auftrag und das selektive Aufschmelzen von Metallpulver im Laser Powder Bed Fusion Prozess (L-PBF) sind u.a. optimierte und flexibel anpassbare Designs und die Nutzung von neuartigen Materialien möglich. Aufgrund der Komplexität des AM-Prozesses und der Menge an Einflussfaktoren ist eine Qualitätssicherung der gefertigten Bauteile unabdingbar. Verschiedene in-situ Monitoringansätze werden bereits angewendet, jedoch findet eine dedizierte Prüfung erst im Nachgang der Fertigung ex-situ statt. Der Grund dafür ist, dass die Entstehung von geometrischen Abweichungen und Defekten auch zeitversetzt zum eigentlichen Materialauftrag und damit auch zum Monitoring stattfinden kann. Die Notwendigkeit geeigneter in-situ Prüfmethoden für L-PBF, um die Erforderlichkeit einer Nacharbeitung frühzeitig festzustellen und Ausschuss zu vermeiden ist angesichts kostenintensiver Ausgangsstoffe und einer oftmals mehrstündigen bis mehrtägigen Prozessdauer besonders hoch.
Daraus motiviert wird im Rahmen des Projektes ATLAMP die Möglichkeit der aktiven Laserthermografie mit Hilfe des defokussierten Fertigungslasers untersucht. Damit ist, bei vergleichsweise geringer Laserleistung, eine zerstörungsfreie Prüfung mittels Flying Spot Thermografie möglich. Diese findet jeweils anschließend an die Fertigung einer Schicht statt, womit der reale Status des Bauteils im Verlauf des AM-Prozesses geprüft wird.
Als Grundlage dafür werden im Rahmen dieser Arbeit mit AM gefertigte, defektbehaftete Probekörper zunächst losgelöst vom Fertigungsprozess untersucht. Damit werden die Grundlagen für den neuartigen Ansatz der aktiven in-situ Laserthermografie im L-PBF-Prozess mittels des Fertigungslasers geschaffen. Auf diese Weise lassen sich auch zeitversetzt auftretende Defekte zerstörungsfrei im Prozessverlauf feststellen und eine aussagekräftige Qualitätssicherung des Ist-Zustands des Bauteils erreichen.
Der Vortrag stellt nach einer kurzen allgemeinen Einleitung zur additiven Fertigung und des Laser Powder Bed Fusion Verfahrens einige Herausforderungen vor, die derzeitig den Einsatz von AM-Komponenten in sicherheitsrelevanten Anwendungen erschweren. Abschließend werden zwei Beispiele von Arbeiten der BAM gezeigt, die zur Überwindung dieser Herausforderungen beitragen können.
The formation of irregularities such as keyhole porosity pose a major challenge to the manufacturing of metal parts by laser powder bed fusion (PBF-LB/M). In-situ thermography as a process monitoring technique shows promising potential in this manner since it is able to extract the thermal history of the part which is closely related to the formation of irregularities. In this study, we investigate the utilization of machine learning algorithms to detect keyhole porosity on the base of thermographic features. Here, as a referential technique, x-ray micro computed tomography is utilized to determine the part's porosity. An enhanced preprocessing workflow inspired by the physics of the keyhole irregularity formation is presented in combination with a customized model architecture. Furthermore, experiments were performed to clarify the role of important parameters of the preprocessing workflow for the task of defect detection . Based on the results, future demands on irregularity prediction in PBF-LB/M are derived.