In this presentation tribological investigations on steels, polymers and coatings in gaseous and liquid hydrogen are shown. For steels the results of show that although martensitic steel may suffer from hydrogen embrittlement, application e.g. in roller bearings is possible. On the other hand, martensitic transformation of austenitic steels may cause problems in the application of these materials. Furthermore, the tribological performance of polymer composites with and without solid lubricant fillers in gaseous and liquid hydrogen was investigated. In particular, PEEK- and PTFE-matrix compounds showed low friction and sufficient low wear under these conditions. Among the solid lubricants, carbon-based materials are appropriate for hydrogen applications. Several variants of DLC and ta-C materials were tested. Beside the results for hydrogen, also a comparison with CH4-environment is shown.
The martensitic steels X30CrMoN15-1 and 100Cr6 did not show any hydrogen enhanced wear in sliding friction tests against alumina balls in hydrogen gas environment. However, depending on the purity of the environment, unexpected high wear occurred at the alumina ball. The results of a tests series with a broad variation of test parameters are presented.
Sliding wear of martensitic steels in hydrogen – X30CrMoN15-1 and 100Cr6 – the role of water traces
(2016)
Initially the primary objective of the project has been the investigation of the influence of gaseous hydrogen on the wear of martensitic steels under heavy tribological stress. As a counter body an Al2O3 ball has been used because the material is inert and hard so that a low amount of wear was expected. If only the gas pressure is responsible for the absorption of hydrogen from the gas to pure α-iron it would require 15·105 MPa (~15 Mbar) to press 1 ppm into the material.
In the test series the Al2O3 balls showed in N2 and H2 atmosphere a higher wear compared to aerial experiments which showed a smaller wear track and a severer wear for the disc. Because of scattering and thereof following investigations it was shown that hydrogen has no noticeable influence but water traces in the gas are manipulating the outcome of the tests distinctly.
High performance polymer composites have been intensively investigated for tribological applications in air, but rarely in hydrogen environment. Author's previous benchmark of composites in liquid hydrogen (LH2) showed that graphite filled polymers have beneficial friction behaviour in this extreme condition. Therefore, further investigations have been undertaken in hydrogen environment. This paper presents first results obtained with polyimide composites filled with different types (natural, synthetic) and amounts of graphite in air, vacuum and hydrogen environments. A particular attention is taken to the influence of hydrogen on graphite as well as on the polymer matrix.
For further development of hydrogen technology, it is necessary to have a sufficient number of materials for safe and reliable operation available. Frictional contacts exposed to hydrogen, are critical because of vanishing protective oxide layers in the presence of a chemical reducing environment. Furthermore, liquid lubricants are often not applicable, because of purity requirements, or very low temperatures in the case of liquid hydrogen. Thus, for numerous tribosystems in hydrogen technology, solid lubrication is the only possible method for reducing friction and wear. Therefore, investigations on the tribological behaviour of friction reducing materials, such as PTFE, graphite, DLC and MoS2, in inert and hydrogen environment were carried out. The results show that solid lubricants, applied as coatings or as components in polymer composites, are able to reduce friction and wear in gaseous as well as in liquid hydrogen. However, some materials are very sensitive to the environmental medium.