This paper presents investigation results of a process for defect-free hybrid laser arc welding (HLAW) of closed circumferential welds. The process aims to avoid weld imperfections in the overlap area of a HLAW circumferential weld. A process control strategy for closing the circumferential weld was developed to achieve a defect-free overlap region by controlling the solidification conditions at the end of the weld. The controlled heat flow is achieved by adjusting the parameters of both welding processes involved, the laser beam as well as gas metal arc welding (GMAW) process. Experimental investigations were carried out on 12 mm to 15 mm thick tube sections. The influence of process parameters such as the laser ramp time, the change in magnification scale and the defocusing of the laser beam on the solidifi-cation conditions at the end of the circumferential weld was investigated to find an optimum strategy for ramping out the process energy. Within the framework of the experimental studies, it was demonstrated that defocusing the laser beam in the range between 60 mm and 100 mm over a short run-out area of the weld of approximately 15 mm led to a significantly better weld formation in the overlap area. A favourable cup-shaped weld shape could be achieved without a tendency to crack. The laser optics with a motor-driven lens system made it possible to increase the laser beam diameter without changing the position of the GMAW arc relative to the component surface.
In diesem Beitrag werden Ergebnisse der Untersuchungen eines Verfahrens zum fehlerfreien Laserstrahl-MSG-Hybridschweißen von geschlossenen Rundnähten vorgestellt. Das Verfahren zielt auf die Vermeidung von Schweißnahtunregelmäßigkeiten im Überlappbereich einer hybridgeschweißten Rundnaht. Eine Strategie der Prozessführung beim Schließen der Rundnaht wurde entwickelt, mit der ein fehlerfreier Überlappbereich durch die Kontrolle der Erstarrungsbedingungen am Schweißnahtende erreicht wird. Die kontrollierte Wärmeführung wird durch eine Anpassung der Parameter von beiden beteiligten Schweißprozessen, dem Laserstrahl sowie dem Metallschutzgas (MSG)-Schweißprozess, realisiert. Experimentelle Untersuchungen wurden an 12 bis 15 mm dicken Rohrabschnitten durchgeführt. Der Einfluss von Prozessparametern wie der Veränderung des Abbildungsmaßstabs und der Defokussierung des Laserstrahls auf die Erstarrungsbedingungen am Ende der Rundnaht wurde untersucht, um eine optimale Strategie zum Herausführen der Prozessenergie zu finden.
Im Rahmen der experimentellen Untersuchungen konnte gezeigt werden, dass eine Defokussierung des Laserstrahls im Bereich zwischen 60 mm und 100 mm über einen kurzen Auslaufbereich der Naht von etwa 15 mm zu einer deutlich besseren Nahtausbildung im Überlappbereich führt. Es konnte eine günstige kelchförmige Schweißnaht ohne eine Tendenz zur Rissbildung erzielt werden. Die Laseroptik mit motorisch angesteuertem Linsensystem ermöglichte dabei eine Vergrößerung des Laserstrahldurchmessers ohne eine Veränderung der Position des MSG-Lichtbogens relativ zur Bauteiloberfläche.
With an availability of the modern high power fibre lasers the application range of laser and laser hybrid welding can be significantly increased. For the implementation of this new technology in the economically extremely interesting application of pipeline construction it is necessary to fulfil a series of systematic research studies. As it has been shown in the past the fibre laser hybrid wielding of pipeline Steel X65 up to 32 mm thickness is possible with appropriate quality. For the use of laser-hybrid welding in pipe laying insensibility towards tolerances and the possibility of girth welding are very important factors in addition to the weld seam quality. The aim of a Research project carried out in the Federal Institute for Materials Research and Testing (BAM) was the development of a welding procedure using high power fibre laser in combination with GMAWProcess which could be applied for welding of pipelines. For tests segments of linepipes with an outer diameter of 914 mm and a wall thickness of 16 mm have been welded using specially designed equipment for girth welding of pipes. First promising results for the use of laser-hybrid welding of thick materials could be demonstrated. The gap-bridgeability and misalignement was studied.
Laser Plasma Hybrid Welding of Austenitic Stainless Steels - Phenomena of Process Instability
(2007)
Laser plasma hybrid welding has been proved to be a very stable hybrid welding process and
welds of high quality can be produced, especially if high surface quality and low spattering is
demanded such as in welding fabrication of high alloyed austenitic stainless steels.
In particular cases, even though welds display high outer quality, X-ray examinations
revealed weld defects which may range from low porosity to blowhole-like cavities. The
phenomena and the main influencing parameters such as arc current, welding speed and
focal point position are discussed. Parameter fields will be suggested for welding plates of
different austenitic stainless steel grades with thicknesses ranging from 3 to 8 mm. The
results are based on welding experiments carried out using a 4.4 kW diode pumped Nd:YAGlaser.
Thus, also the influence of the feeding fibre diameter has been investigated and it was found
that the resulting beam shape has a major effect on the welding performance.
Within the framework of an AiF (The German Federation of Industrial Research Associations) project, investigations were conducted into the solidification behaviour of various high-alloy austenitic steels in laser and laser-GMA hybrid welding. For comparison purposes, reference was made to pure gas metalarc welding tests. It was possible to raise the welding speeds in hybrid welding compared with the individual gas metal-arc (GMA) and laser welding processes. The central subjects of the investigations were the type of solidification and the connected hot cracking behaviour during welding. In this respect, particular attention was paid not only to the kinetic effects during solidification which may be caused by the high solidification rates in laser and hybrid welding but also to their consequences.