Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (21)
- Vortrag (10)
- Beitrag zu einem Tagungsband (3)
- Buchkapitel (1)
- Posterpräsentation (1)
Sprache
- Englisch (36)
Schlagworte
- Glass transition (36) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (10)
- 6.6 Physik und chemische Analytik der Polymere (10)
- 5 Werkstofftechnik (3)
- 5.6 Glas (2)
- 7 Bauwerkssicherheit (2)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (2)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.4 Sicherheit von Lagerbehältern (1)
- 5.0 Abteilungsleitung und andere (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
Eingeladener Vortrag
- nein (10)
This work studies the influence of the adsorbed layer on the glass transition of thin films of polysulfone. Therefore, the growth kinetics of the irreversibly adsorbed layer of polysulfone on silicon substrates was first investigated using the solvent leaching approach, and the thickness of the remaining layer was measured with atomic force microscopy. Annealing conditions before leaching were varied in temperature and time (0–336 h). The growth kinetics showed three distinct regions: a pre-growth step where it was assumed that phenyl rings align parallel to the substrate at the shortest annealing times, a linear growth region, and a crossover from linear to logarithmic growth observed at higher temperatures for the longest annealing times. No signs of desorption were observed, pointing to the formation of a strongly adsorbed layer.
Second, the glass transition of thin polysulfone films was studied in dependence on the film thickness using spectroscopic ellipsometry. Three annealing conditions were compared: two with only a tightly bound layer formed in the linear growth regime and one with both tightly bound and loosely adsorbed layers formed in the logarithmic growth regime. The onset thickness and increase in the glass transition temperature increases with annealing time and temperature. These differences were attributed to the distinct conformations of the formed adsorbed layers.
We report the dielectric and calorimetric investigations of an homologous series of Janus polynorbornenes with rigid main backbone and flexible -Si(OR)3 side groups, of differing length alkyl chains (R = Propyl, Butyl, Hexyl, Octyl, Decyl). Dielectric dispersion reveals two active processes at low temperatures, denoted as β- and α- relaxation. The former can be assigned to localized fluctuations, whilst the latter relates to the glassy dynamics of the flexible -Si(OR)3 side groups, that creates a nanophase separation in both the alkyl chain rich and backbone rich domains. Temperature modulated DSC measurements and X-ray scattering experiment confirm the nanophase separation. Fast Scanning Calorimetry employing both fast heating and cooling rates detects the glass transition temperatures of the backbone rich domains, which are beyond or near to their degradation temperatures in terms of conventional DSC. The cooperative length scale of glass transition and the size of the alkyl chain rich domains increases with chain length. Alongside these results, a significant conductivity contribution was observed for all Poly(tricyclononenes) with Si(OR)3 side groups, which is interpreted in terms of a percolation model.
Melting is well understood in terms of the Lindemann criterion, which
essentially states that crystalline materials melt when the thermal vibrationsof their atoms become so vigorous that they shake themselves free of the binding forces. This picture does not necessarily have to hold for glasses, where the nature of the solid–liquid cross-over is highly debated. The Lindemann criterion implies that the thermal expansion coefficients of crystals are inversely proportional to their melting temperatures. Here we find that, in contrast, the thermal expansion coefficient of glasses decreases more strongly with increasing glass temperature, which marks the liquid–solid cross-over in this material class. However, this proportionality returns when the thermal expansion coefficient is scaled by the fragility, a measure of particle cooperativity. Therefore, for a glass to become liquid, it is not sufficient to simply overcome the interparticle binding energies.
Instead, more energy must be invested to break up the typical cooperative particle network that is common to glassy materials. The thermal expansion coefficient of the liquid phase reveals similar anomalous behaviour and is universally enhanced by a constant factor of approximately 3. These universalities allow the estimation of glass temperatures from thermal expansion and vice versa.
We study the molecular mobility and electrical conductivity of a homologous series of linear shaped columnar ionic liquid crystals ILCn, (n = 8, 10, 12, 14, 16) using Broadband Dielectric Spectroscopy (BDS), Specific Heat Spectroscopy (SHS), and X-ray scattering. We aim to understand how the alkyl chain length influences the dynamics and electric conductivity in this system. Two dielectrically active relaxation modes are observed, the and the αcore process, that correspond to the localized relaxation of the alkyl chains, and cooperative motions of the aromatic core in the columns respectively. Both the relaxation and the αcore process slow down with increasing alkyl chain length. SHS reveals one relaxation process, the αalkyl process that has similar temperature dependence as that of the αcore process for ILC12, 14, 16 but shifts to higher temperature for ILC8 and 10. For ILC12, 14, 16 the absolute values of DC conductivity increase by 4 orders of magnitude at the transition from the plastic crystalline to hexagonal columnar phase. For ILC8, 10 the DC conductivity behavior is similar to ionic liquids, where the conductivity is coupled with structural relaxation. Small-Angle X-ray (SAXS) investigations reveal that both the intercolumnar distance and disorder coherence length increase with alkyl chain length, conversely the DC conductivity decreases monotonically.
We investigate the molecular dynamics and electrical conductivity for a homologous series of linear shaped guanidinium based cyclic ILCs that vary in alkyl chain length, CLCRs (R = 8, 10, 12, 14, 16) by employing broadband dielectric spectroscopy (BDS), and calorimetry comprised of Fast Scanning Calorimetry (FSC) and temperature modulated FSC (TMFSC). Besides conductivity at high temperatures, the dielectric dispersion reveals two relaxation modes: the fast γ and the slow α1 relaxation. The former is assigned to the localized fluctuations while the latter is due to segmental dynamics of the alkyl chains. The γ mode slows down for long chain length CLCs (12,14,16) compared to their shorter analogues. Calorimetric investigation reveals one process, the α2 process, for all ILCs. The α2 process for CLC10, 12, and 14 has a similar temperature dependence as the dielectric α1 relaxation, while for the CLC8 and 10, it's shifted to a higher temperature. For all CLCRs, the absolute values of DC conductivity increase by 4 orders of magnitude at the transition from the plastic crystalline to hexagonal columnar phase. This increase is due to the change in the underlying conduction mechanism from delocalized electron hopping in the crystalline phase to one-dimensional ion mobility in the columnar phase. The glassy dynamics shifts to higher temperatures with increasing alkyl chain length. Conversely, the DC conductivity drops by 3 orders of magnitude from CLC8 to CLC16.
We report the dielectric and calorimetric investigations of an homologous series of Janus polynorbornenes with rigid main backbone and flexible -Si(OR)3 side groups, of differing length alkyl chains (R = Propyl, Butyl, Hexyl, Octyl, Decyl). Dielectric dispersion reveals two active processes at low temperatures, denoted as β- and α- relaxation. The former can be assigned to localized fluctuations, whilst the latter relates to the glassy dynamics of the flexible -Si(OR)3 side groups, that creates a nanophase separation in both the alkyl chain rich and backbone rich domains. Temperature modulated DSC measurements and X-ray scattering experiment confirm the nanophase separation. Fast Scanning Calorimetry employing both fast heating and cooling rates detects the glass transition temperatures of the backbone rich domains, which are beyond or near to their degradation temperatures in terms of conventional DSC. The cooperative length scale of glass transition and the size of the alkyl chain rich domains increases with chain length. Alongside these results, a significant conductivity contribution was observed for all Poly(tricyclononenes) with Si(OR)3 side groups, which is interpreted in terms of a percolation model.
Molecular mobility and conductivity of four bent shaped tetramethylated guanidiniumbased ionic liquid crystals(ILCs) with varying head group configuration (cyclic or acyclic) and alkyl chain length is investigated by a combination of broadband dielectric spectroscopy (BDS) and specific heat spectroscopy (SHS). Two dielectrically active processes observed in the plastic crystalline phase at low and high temperatures are denoted as γ and α1 relaxation. The former is assigned to localized fluctuations of methyl groups including nitrogen atoms in the guanidinium head groups. SHS investigations reveal one calorimetrically active process termed as α2 Relaxation process. The temperature dependencies of the relaxation rates of α1 and α2 are similar for the cyclic ILCwhile for the acyclic counterpart they are different. Possible molecular assignments for the α1 and α2 relaxation are discussed in detail. Alongside relaxation processes, a significant conductivity contribution was observed for all ILCs, where the absolute value of DC conductivity increases by 4 orders of magnitude at the transition from the crystalline to the hexagonal columnar phase. The increase is traced to the change in the underlying conduction mechanism from the delocalized electrical conduction in the Cry phase to ionic conduction in the quasi 1D ion columns formed in the hexagonal columnar mesophase.
For the first time, dielectric and calorimetric investigations of a homologous series of Janus polynorbornenes with rigid main backbones and flexible −Si(OR)3 side groups of differing length alkyl chains (R = propyl, butyl, hexyl, octyl, and decyl) is reported. Generally, this class of polymers has some potential for applications in the field of gas separation membranes. Two dielectrically active processes are observed at low temperatures, denoted as β- and α-relaxation. The former can be assigned to localized fluctuations, while the latter is related to the glassy dynamics of the flexible −Si(OR)3 side groups, creating a nanophase separation in both the alkyl chain-rich and backbone-rich domains. This is confirmed through temperature-modulated differential scanning calorimetry (TMDSC) measurements and X-ray scattering experiments. The glass transition temperatures of the backbone rich domains, which are beyond or near to their degradation temperatures in terms of conventional DSC, are determined for the first time using fast scanning calorimetry employing both fast heating and cooling rates. This is complemented with scattering experiments that show how the size of the alkyl chain-rich domains increases with the side chain length. Alongside these results, a significant conductivity contribution was observed for all poly(tricyclononenes) with −Si(OR)3 side groups, which is interpreted in terms of a percolation model.
Understanding the failure mechanisms that lead to leakage of rubber seals at low temperatures is important. Rubber properties are highly temperature dependent. Changes in behaviour at low temperatures can result from the rubber-glass transition and for some rubbers by partial crystallisation. Experimental results on the low temperature behaviour of different rubber seals were discussed to help understand seal failure processes.
To understand the influence of water and alkalis on aluminosilicate glasses, three polymerized glasses with varying ratios of Na/K were synthesized [(22. 5-x)Na2O-xK2O-22.5 Al2O3-55 SiO2 with x = 0, 7.5, and 11.25]. Subsequently, these glasses were hydrated (up to 8 wt% H2O) in an internally heated gas pressure vessel. The density of hydrous glasses linearly decreased with water content above 1 wt%, consistent with the partial molar volume of H2O of 12 cm3/mol. Near-infrared spectroscopy revealed that hydroxyl groups are the dominant species at water content of <4 wt%, and molecular water becomes dominating at water content of >5 wt%. The fraction of OH is particularly high in the pure Na-bearing glass compared to the mixed alkali glasses. 27Al magic angle spinning-NMR spectroscopy shows that aluminum is exclusively fourfold coordinated with some variations in the local geometry. It appears that the local structure around Al becomes more ordered with increasing K/Na ratio. The incorporation of H2O reinforces this effect. The differential thermal analysis of hydrous glasses shows a significant mass loss in the range of glass transition already during the first upscan, implying the high mobility of water in the glasses. This observation can be explained by the open structure of the aluminosilicate network and by the low dissociation enthalpy of H2O in the glasses (≈ 8 kJ/mol). The effect of the dissolved H2O on the glass transition temperature is less pronounced than for other aluminosilicate glasses, probably because of the large fraction of Al in the glasses.