Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
(2024)
Zinc-based surface coatings are widely applied with high-strength steels in automotive industry. Some of these base materials show an increased brittle cracking risk during loading. It is necessary to examine electrogalvanized and uncoated samples of a high strength steel susceptible to liquid metal embrittlement during spot welding with applied external load. Therefore, a newly developed tensile test method with a simultaneously applied spot weld is conducted. A fully coupled 3D electrical, thermal, metallurgical and mechanical finite element model depicting the resistant spot welding process combined with the tensile test conducted is mandatory to correct geometric influences of the sample geometry and provides insights into the sample’s time dependent local loading. With increasing external loads, the morphology of the brittle cracks formed is affected more than the crack depth. The validated finite element model applies newly developed damage indicators to predict and explain the liquid metal embrittlement cracking onset and development as well as even ductile failure.
The present work seeks to extend the level of understanding of the stress field evolution during direct laser deposition (DLD) of a 3.2 mm thick multilayer wall of Ti-6Al-4V alloy by theoretical and experimental studies. The process conditions were close to the conditions used to produce large-sized structures by the DLD method, resulting in specimens having the same thermal history. A simulation procedure based on the implicit finite element method was developed for the theoretical study of the stress field evolution. The accuracy of the simulation was significantly improved by using experimentally obtained temperature-dependent mechanical properties of the DLD-processed Ti-6Al4V alloy. The residual stress field in the buildup was experimentally measured by neutron diffraction. The stress-free lattice parameter, which is decisive for the measured stresses, was determined using both a plane stress approach and a force-momentum balance. The influence of the inhomogeneity of the residual stress field on the accuracy of the experimental measurement and the validation of the simulation procedure are analyzed and discussed. Based on the numerical results it was found that the non-uniformity of the through-thickness stress distribution reaches a maximum in the central cross-section, while at the buildup ends the stresses are distributed almost uniformly. The components of the principal stresses are tensile at the buildup ends near the substrate. Furthermore, the calculated equivalent plastic strain reaches 5.9% near the buildup end, where the deposited layers are completed, while the plastic strain is practically equal to the experimentally measured ductility of the DLD-processed alloy, which is 6.2%. The experimentally measured residual stresses obtained by the force-momentum balance and the plane stress approach differ slightly from each other.
The paper deals with a numerical finite element simulation of the residual stress evolution in friction stir welding of 6 mm thick aluminum alloy AA2024-T3. The transient thermal field during the welding process was calculated with the commercial code COMSOL Multiphysics 5.0. Therefore, a thermal-pseudo-mechanical (TPM) heat source was implemented. A subsequent mechanical simulation was performed with varying hardening models for different welding speeds of 60 and 300 mm/min. The influence of softening of the material, which was due to hardening precipitation dissolution associated to the heating, was also investigated. Experiments in terms of thermocouple measurements as well as Vickers hardness and X-ray measurements of the residual stresses were conducted and compared to numerically obtained results. A qualitatively as well as quantitatively good agreement was found for different applied welding speeds.
Welding is one of the most critical operations for the construction of reliable metal structures in everything from ships to reactor vessels. When welds fail, the entire structure often fails—so expectations on weld quality have never been higher. Any process that uses a localized heat source, such as welding, is likely to result in some distortion. The welding process of very thick metal components is not inherently stable and is barely controllable without external forces.
Pulse thermography is a non-destructive testing method based on infrared imaging of transient thermal patterns. Heating the surface of the structure under test for a short period of time generates a non-stationary temperature distribution and thus a thermal contrast between the defect and the sound material. In modern NDT, a quantitative characterization of hidden imperfections in materials is desired. In particular, defect depth and shape are of interest. The reconstruction of the defect from thermography data is a nonlinear inverse problem, and ill-posed. We propose an algorithm for the identification of subsurface defects based on the travel time of the reflected thermal pulse. Our work extends results by Lugin and Netzelmann, taking lateral thermal flows directly into account while retrieving the defect depth. This requires significantly less computational work. Quantitative information about the defect shape and depth is obtained. Application of our method to both thermography data generated by a finite element simulation and experimental heating of PVC test specimens with different defects yields good reconstruction of the actual defects.
Modern structural integrity assessment procedures in the field of nuclear related technology incorporate fracture
mechanical concepts. Therefore, they inevitably require the availability of both, loading parameters as well as material
characteristics in terms of fracture mechanical quantities. Especially in case of dynamic loading conditions, the methods
for the determination of the loading parameters need further improvement and there is a lack of material characteristics
as well. In Germany, ductile cast iron (DCI) is used for heavy-sectioned casks for radioactive materials. New developments
in cask design and efforts to extend the application limits require further investigations. The present study is part
of an ongoing fracture mechanics research programme of BAM which is focused on the systematic mechanical and
fracture mechanical material characterisation of DCI materials under dynamic loading conditions. In this study, results
of fracture mechanics investigations on ductile cast iron from an original DCI container with a wide variety of microstructure
under dynamic loading conditions in the temperature range from -50 °C to +22 °C are presented. Large scale
as well as small scale single edge crack bend specimens SE(B) with thicknesses of 140 mm and 15 mm, respectively
were tested. Furthermore, it is reported on the results of a finite element simulation of the dynamic large scale fracture
mechanics tests. Strength and deformation characteristics were determined in dynamic tensile tests. They are discussed
with respect to the influence of pearlite content and test temperature. The material specific experimental difficulties in
the determination of reliable dynamic crack initiation toughness values of DCI are outlined.