A new concept for the self-diagnosis of embedded fiber Bragg grating (FBG) strain sensors was developed, simulated and experimentally tested. This concept is based on a magnetostrictive metallic layer directly coated on the fibre cladding over the grating segment of the FBG sensor, so that an on-demand external magnetic field in a millitesla scale can produce a controllable artificial strain as an indication signal for the remote optical interrogator. The relationship between the pre-defined magnetic field and its induced Bragg wavelength shift characterizes this validation concept. Any deviation of the local bonding state of the interfaces from the initial or/and any change of shear strain transferring mechanism from composite matrix to the optical fibre core will result in alterations in this sensitive relationship, and thus triggers an immediate alert for a further inspection. The finite element method is used to simulate the strain of this configuration as result of different values of the magnetic field in order to optimize the geometrical sensor parameters. The simulations are verified by experiments results. © (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer.
Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer. Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.
Here we present the fabrication of a solid-core microstructured polymer optical fiber (mPOF) made of polycarbonate (PC), and report the first experimental demonstration of a fiber Bragg grating (FBG) written in a PC optical fiber. The PC used in this work has a glass transition temperature of 145°C. We also characterize the mPOF optically and mechanically, and further test the sensitivity of the PC FBG to strain and temperature. We demonstrate that the PC FBG can bear temperatures as high as 125°C without malfunctioning. In contrast, polymethyl methacrylate-based FBG technology is generally limited to temperatures below 90°C.
Strain sensors used in practical applications must provide reliable measurement data. To achieve this, sensor systems must be validated by using experimental facilities that enable physically independent statements about the performance of the sensor components. The paper describes qualification and validation procedures using a special facility to qualify surface-applied strain sensors and to achieve reliable sensor results. Based on examples concerning fibre optic strain sensor patches with and without FBG sensors, the determination of the strain gauge factor also under combined thermal and mechanical loading will be presented. These results are the basis for development of guidelines and standards.
Shaking table test of a two-storey stone masonry building reinforced with multifunctional textiles
(2010)
The radiation-induced Bragg wavelength shift (BWS) was measured with type I gratings made of 12 fibers with very different composition, i.e., of fibers with an extremely different radiation-induced attenuation. With two of the fibers fabrication parameters like laser intensity, hydrogen loading, and annealing conditions after grating inscription were varied. With another fiber type I and type II gratings were made by a completely different process. With gratings made under identical conditions of the 12 fibers the radiation-induced BWS only varied by about a factor of three. Varying the fabrication parameters led to BWS differences up to nearly a factor of ten.
Die Eignung von Faser-Bragg-Gitter-(FBG)-Sensoren zur Messung ionisierender Strahlung wurde an einem Undulator des Elektronenspeicherrings BESSY II untersucht. Über einen Zeitraum von 20 Wochen wurde eine durch Strahlung verursachte Bragg-Wellenlängenänderung der FBG-Sensoren von 25pm gemessen, was einer Strahlendosis von 720 Gy entspricht.
The suitability of using fiber Bragg grating (FBG) sensors for the measurement of ionizing radiation on the electron storage ring BESSY II by measuring the Bragg wavelength shift caused by radiation was investigated. During a time period of 20 weeks a Bragg wavelength shift of 25pm caused by the ionizing radiation was measured by FBG sensors at the storage ring. This Bragg wavelength shift corresponds to a radiation dose value of 720 Gy.