AbstractViscous healing of cracks induced by the Vickers indentation in a soda lime magnesium silicate, a soda borosilicate, and a soda aluminosilicate glass (NAS) was studied by laser scanning microscopy. Plots of the crack length, width, and depth normalized to the initial crack length versus time over viscosity merge into single master curves of each of these quantities for each glass. Despite glass properties do not differ strikingly from each other, however, these master curves strongly differ among the glasses. This finding was attributed to a different interplay of various crack healing phenomena. Lateral cracks were found to be responsible for the bulging of the sample surface around the Vickers imprint, which in turn promotes radial crack widening as the main cause of healing delay. The most rapid healing of lateral cracks was observed in NAS in which bulging and crack widening were least pronounced.
Crack healing in glass ceramic solid oxide fuel cell (SOFC) sealants is of utmost importance as cracks caused by thermal cycling remain a bottleneck in developing durable SOFC. Whereas no or low crystal volume fraction seems most favorable for viscous crack healing, it does not for load bearing and undesired diffusion. On the other hand, crystals or filler particles can make the sealant less prone to these disadvantages but it could increase the effective composite viscosity and retard crack healing.
Against this background, the influence of crystal volume fraction, phi, on viscous crack healing in glass matrix composites prepared from soda lime silicate glass and zirconia filler particles was studied. Vickers indention induced radial cracks were healed isothermally during interrupted annealing steps and monitored with optical microscopy. Due to the slow crystallization of the glass under study, phi could be kept constant during crack healing.
For bulk glass samples (phi = =), the decrease in radial crack length was retarded by an initial increase in crack width due to crack rounding. Up to phi = 0.15 the increase in effective viscosity retarded this crack broadening thereby yielding faster crack healing. For phi > 0.15, crack broadening was progressively suppressed but the same was true for crack healing, which was fully prevented above phi = 0.3. Results indicate that optimum micro structures can prevent crack broadening limited by the global effective composite viscosity and this way promote crack healing limited by local glass viscosity.
A novel method to generalize kinetic data of viscous crack healing in glasses is proposed. The method assumes that crack healing progress is proportional to the healing time, t, and indirect proportional to viscosity, n. This way, crack length and crack width data, normalized to the initial crack length and plotted versus t/n, allow to compare crack healing progress for different cracks and healing temperatures in a master curve. Crack healing experiments conducted in this study demonstrate the applicability of this method for a commercial microscope slide glass.
Fundamental understanding of crack healing in glassy crystalline materials is very important for many applications, especially for solid oxide fuel cells (SOFC) sealants since cracks caused by mechanical stress or thermal cycling still remain a substantial bottleneck in developing durable SOFC.
Previous studies on soda lime silicate glass published by Singh showed that crack healing is driven by viscous flow. He postulated that the healing progress is proportional to time, t, and the inverse viscosity. For a given glass, this finding would allow to present data of crack healing measured at different temperatures in a master curve, if the healing progress is plotted versus t/. Such master curves would be a helpful tool in understanding crack healing kinetics.
To verify the applicability of such master curves, crack healing in non-crystallizing soda-lime-silicate (NCS) and sodium-borosilicate glasses (NBS) was studied. Cracks were generated by Vickers indention and healed isothermally at different temperatures. Crack healing progress was monitored by optical and electron microscopy. The results show that the above mentioned proportionality applies to the two glasses and the afore developed master curve could be obtained in both cases.
Partially crystalline glasses are predominantly used as solid oxide fuel cell (SOFC) sealants due to their superior long term durability. However, cracks caused by thermal cycling still remain a substantial bottleneck in developing durable SOFC sealants inasmuch as, in contrast to crystal free glasses, large crystal volume fractions can retard healing. Hence, the basic understanding of crack healing in glassy crystalline materials and the effects of micro structure are important for finding optimum micro structures for both, durability and crack healing.
For studying these effects, several model glass matrix composites (GMC), for which simultaneous crystal growth and crack healing can be excluded, have been synthesized. Sodium calcium silicate glass – zirconia GMC turned out to provide sufficiently homogeneous, dense and durable model GMC for our studies. The microstructure of this GMC shows large crystal free glassy regions embedded in network of finely dispersed ZrO2 nanoscale crystals. Whereas the glassy regions allow easy local crack healing, the network of dispersed crystals increases the effective viscosity on a global scale. This effect substantially retards crack broadening during later healing stages, which often ends up in large pores. Therefore, this type of microstructure seems to be an interesting candidate for crack healing optimized sealants.
Fundamental understanding of crack healing in glassy crystalline materials is very important for solid oxide fuel cell (SOFC) sealants, since cracks caused by sealing or thermal cycling still remain a substantial bottleneck in developing durable SOFC.
Previous studies on soda lime silicate glass [Sin14] showed that crack healing is driven by viscous flow and that healing progress is proportional to time t and inverse viscosity η. This finding would allow to present healing data of a given glass for different temperatures in a master curve healing progress versus t/η. Such master curves would be a helpful tool in understanding crack healing kinetics.
Against this background, crack healing in non-crystallizing sodium calcium silicate (NCS) and sodium borosilicate glasses (NBS) have been studied. Moreover, to evaluate the influence of micro structure in crystallized glass on crack healing process, glass matrix composites (GMC) were prepared from NCS and zirconia as inert ceramic filler material mimicking a partially crystalline micro structure. By this way, the micro structure can be kept constant during crack healing. Cracks were generated by Vickers indention and healed isothermally at different temperatures. Crack healing progress was monitored by optical and electron microscopy. Results show that the above mentioned proportionality actually applies for the studied glasses for which such a master curve could be obtained. In comparison to a non-crystallized glass, the effective viscosity of GMC is increased by the rigid filler content. This effect substantially retards crack broadening during later healing stages, which often ends up in large pores. On the other hand, local viscous crack healing is still possible in larger glassy regions. This behavior seems to be very interesting for crack healing optimized micro structures.
Fundamental understanding of crack healing in glassy crystalline materials is very important for many applications, especially for sealing solid oxide fuel cells (SOFC) since cracks caused by sealing or thermal cycling still remain a substantial bottleneck in developing durable SOFC.
Previous studies on soda lime silicate glass [Sin14] showed that crack healing is driven by viscous flow and that healing progress is proportional to time t and inverse viscosity η. This finding would allow to present healing data of a given glass for different temperatures in a master curve healing progress versus t/η. Such master curves would be a helpful tool in understanding crack healing kinetics.
Against this background, crack healing in non-crystallizing sodium calcium silicate (NCS) and sodium borosilicate glasses (NBS) have been studied. Moreover, to evaluate the influence of micros structure in crystallized glass on crack healing process, glass matrix composites (GMC) where prepared out of NCS and zirconia as inert ceramic filler material mimicking a partially crystalline micro structure. Cracks were generated by Vickers indention and healed isothermally at different temperatures. Crack healing progress was monitored by optical and electron microscopy. Results show that the above mentioned proportionality actually applies for the studied glasses for which such a master curve could be obtained. In comparison to a non-crystallized glass, the effective viscosity of GMC is increased by rigid filler content. This effect substantially retards crack broadening during later healing stages, which often ends up in large pores. On the other hand, local viscous crack healing is still possible in larger glassy regions. This behavior seems to be very interesting for crack healing optimized sealants.
Partially crystalline glasses are predominantly used as solid oxide fuel cell (SOFC) sealants due to their superior long term durability. However, cracks caused by thermal cycling still remain a substantial bottleneck in developing durable SOFC sealants inasmuch as, in contrast to crystal free glasses, large crystal volume fractions can retard healing. Hence, the basic understanding of crack healing in glassy crystalline materials and the effects of micro structure are important for finding optimum micro structures for both, durability and crack healing.
For studying these effects, several model glass matrix composites (GMC), for which simultaneous crystal growth and crack healing can be excluded, have been synthesized. Sodium calcium silicate glass – zirconia GMC turned out to provide sufficiently homogeneous, dense and durable model GMC for our studies. The microstructure of this GMC shows large crystal free glassy regions embedded in network of finely dispersed ZrO2 nanoscale crystals. Whereas the glassy regions allow easy local crack healing, the network of dispersed crystals increases the effective viscosity on a global scale. This effect substantially retards crack broadening during later healing stages, which often ends up in large pores. Therefore, this type of microstructure seems to be an interesting candidate for crack healing optimized sealants.
Crack healing in glasses
(2017)
Fundamental understanding of crack healing in glassy crystalline materials is very important for many applications, especially for solid oxide fuel cells (SOFC) sealants since cracks caused by mechanical stress or thermal cycling still remain a substantial bottleneck in developing durable SOFC. Previous studies on soda lime silicate glass published by Singh showed that crack healing is driven by viscous flow. There he postulated that the healing progress is proportional to time, t, and the inverse viscosity. This finding would allow to present for a given glass data of crack healing measured at different temperatures in a master curve, if the healing progress is plotted versus t/η. Such master curves would be a helpful tool in understanding crack healing kinetics. To verify the applicability of such master curves, crack healing in non-crystallizing soda-lime-silicate (NCS) and sodium-borosilicate glasses (NBS) was studied. Cracks were generated by Vickers indention and healed isothermally at different temperatures. Crack healing progress was monitored by optical and electron microscopy. The results show that the above mentioned proportionalities applies to the two glasses. In both cases the afore developed master curve could be obtained.