The composites combining aluminum and silica nanoparticles with the addition of tetramethylammonium hydroxide (Al-SiO2(T)) and butanol (Al-SiO2(B)) as mixing media have been successfully fabricated. Corrosion behavior of Al-SiO2 composites before and after exposure in 1M NaCl solution was examined using potentiodynamic polarization (Tafel curve analysis). The study was also equipped with scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and X-ray diffraction (XRD) investigations. Before exposure, Al-SiO2(T) exhibited the best corrosion resistance. Performance improvement was indicated by Al-SiO2(B) up to 10 times better than Al-SiO2(T) after exposure. The increased SiO2 content did not significantly enhance the corrosion resistance of the composites. The Al-SiO2 composites with 5% SiO2 content showed very high corrosion resistance (as the optimum composition). Furthermore, pitting corrosion was observed in the Al-SiO2 composites, indicated by the formation of corrosion products at grain boundaries. The product was affected by the presence of SiO2 in the Al matrix and the NaCl environment at 90 °C (approach to synthetic geothermal media: Na+, Cl, H+, OH-). Our study revealed the presence of γ-Al2O3, γ-Al(OH)3, and Al(OH)2Cl as the dominant corrosion products.
The fabrication and characteristics of amorphous silica reinforced Al matrix composites are studied in this paper. The major starting materials were commercial Al powder and extracted nanoparticle SiO2 (NPS) powder from Indonesian silica sands. Two different active solutions,namely N-butanol and tetramethylammonium hydroxide (TMAH), were introduced during synthesis. Characterisations in terms of physical, mechanical, microstructural and corrosion rate examinations were also employed. Introducing the SiO2 nanoparticles into the Al matrix has decreased the density and increased the porosity of the composites. The addition of N-butanol into Al/SiO2(Al/SiO2(B)) led to broader and lower X-ray diffraction profiles than the addition of TMAH (Al/SiO2(T)). From the microstructural analysis, we found that the SiO2 particles enter and agglomerate into the opening gap of the Al sheets. Furthermore, yield strength, ultimate compression strength and modulus of elasticity tended to reduce the addition of SiO2. The corrosion rate of Al/SiO2(T) was lower than that of Al/SiO2(B) composites.
Investigation of chloride-induced pitting corrosion of steel in concrete with innovative methods
(2016)
The combination of electrochemical and 3D computed tomography (CT) investigations offers the possibility of verifying electrochemical measurements non-destructively. Determining the steel surfaces damaged by pitting corrosion allows developing specimens having damage pattern corresponding to practice. Corrosion phenomena like decoupled pitting corrosion cannot be verified by electrochemical measurements only, but with the combination of those two kinds of investigations it is possible. Another advantage is the minimization of the number of samples. The classical experimental procedure requires the destruction of samples after each damage step.This can be avoided by the use of 3D computed tomography. As long as the corrosion phenomena are completely within the examination zone shown by the 3D computed tomography, the electrochemical measurements can be calculated on an area basis to get the specific corrosion rate or polarization resistance.
During carbon capture and storage (CCS) CO2-corrosion of pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers. The reliability of the steels 42CrMo4, X20Cr13, X46Cr13 and X35CrMo17 is demonstrated in long term laboratory experiments up to 2 years of exposure time. Testings were carried out at ambient pressure under an equivalent corrosive environment as found at the geological onshore CCS-site at Ketzin, Germany (T=60 °C, aquifer water).