Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.
Starches and its derivatives are known to exhibit viscosity modifying characteristics. In an ongoing work, the influence of com and cassava starches on some properties of concrete such as compressive strength, heat of hydration and creep are examined. Various percentages (0.0, 0.5, 1.0, 1.5 and 2 %) of starches by weight of cement were added to concrete mixes prepared in the laboratory. Preliminary results of compressive strengths showed that both starches have some positive impact (e.g. there was 5.3 % increase in strength due to a 1 % addition of com starch by weight of cement in comparison to the control while cassava starch of the same percentage gave 4.9 % increase in strength) at certain percentages of starch addition to concrete at 28 days. The creep and hydration results shows the starch additions compares well and in some instance performs better.
The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.
Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages.
On the background of the need for reuse of building rubble and the saving of natural resources, a European Union research project was performed covering concrete technology and durability aspects. A very special precondition was the use of large-scale processed building rubble with unknown origin and the total replacement of aggregates above 2 mm. Comprehensive tests were carried out on the properties of the starting material from different processing plants and fresh concrete, particularly the interdependence of water addition and wor ability. Investigations on hardened concrete properties included strength devel-opment, creep and shrinkage, modulus of elasticity, capillary absorption, freezing and thawing resistance, and carbonation behavior over a long period. The results demonstrate that the industrial production of a high-grade, durable concrete is possible. The project is a promising contribution for sustainable development.
Performance of calcium phosphate cements in the augmentation of sheep vertebrae - An ex vivo study
(2021)
Oil-based calcium phosphate cement (Paste-CPC) shows not only prolonged shelf life and injection times, but also improved cohesion and reproducibility during application, while retaining the advantages of fast setting, mechanical strength, and biocompatibility. In addition, poly(L-lactideco-glycolide) (PLGA) fiber reinforcement may decrease the risk for local extrusion. Bone defects (diameter 5 mm; depth 15 mm) generated ex vivo in lumbar (L) spines of female Merino sheep (2–4 years) were augmented using: (i) water-based CPC with 10% PLGA fiber reinforcement (L3); (ii) Paste-CPC (L4); or (iii) clinically established polymethylmethacrylate (PMMA) bone cement (L5). Untouched (L1) and empty vertebrae (L2) served as controls. Cement performance was analyzed using micro-computed tomography, histology, and biomechanical testing. Extrusion was comparable for Paste-CPC(-PLGA) and PMMA, but significantly lower for CPC + PLGA. Compressive strength and Young’s modulus were similar for Paste-CPC and PMMA, but significantly higher compared to those for empty defects and/or CPC + PLGA. Expectedly, all experimental groups showed significantly or numerically lower compressive strength and Young’s modulus than those of untouched controls. Ready-to-use Paste-CPC demonstrates a performance similar to that of PMMA, but improved biomechanics compared to those of water-based CPC + PLGA, expanding the therapeutic arsenal for bone defects. O, significantly lower extrusion of CPC + PLGA fibers into adjacent lumbar spongiosa may help to reduce the risk of local extrusion in spinal surgery.
In the beginning of the 1980s earth building has undergone a renaissance, which nowadays leads to an increasing use of load-bearing earth constructions and in particular, earth block masonry. At present, there are no common structural standards according to the semi-probabilistic design concept, which is the state-of-the-art in European standards.
A solid database is needed for the determination of the partial safety factor on the resistance side. Therefore, compressive strength tests were carried out with two types of earth blocks and two types of prefabricated earth mortar. The evaluation showed that the variation of the compressive strength was remarkably less than expected, which seems to indicate high quality standards of the components earth block and mortar with regard to industrial production.
On the basis of these results and together with the reliability method, a partial safety factor for earth block masonry subjected to compression was determined. The main aim of the research was the development of a first valid database for material parameters of earth block masonry with particular regard to statistical characteristics. The results showed that a common calculation method for earth block masonry based on partial safety factors following the valid masonry construction standard is feasible.
Für Prüfungen in der Beanspruchung auf Zug zur Bestimmung der Haft- bzw. Klebfestigkeit bzw. in der Beanspruchung auf Druck zur Bestimmung der Härte wurden bisher Zug- bzw. Härteprüfmaschinen als Ein-Proben-Prüfungen verwendet. In der Beanspruchung auf Zug ist die Probe beidseitig, und um das Einleiten von Querkräften zu verhindern, oft doppeltkardanisch einzuspannen. In jedem Falle handelt es sich um Ein-Proben-Prüfungen. Bei der Zentrifugentechnologie kann mit der Zentrifugalkraft als Prüfkraft unter Verwendung eines Trommelrotors erstmals in einer Mehr-Proben- Anordnung gearbeitet werden. Da die Proben nur einseitig unterstützt werden, ist die Beladung über einfaches Einstecken realisierbar.
Mit dem Auf-Tisch-Prüfsystem können bis zu acht Proben gleichzeitig auf Zug oder Druck beansprucht werden. Ein aufgeklebter oder anderweitig mit dem Prüfkörper verbundener und unter Einwirkung der Zentrifugalkraft in einer Führungshülse radial nach außen laufender Prüfstempel beansprucht dann die Klebung, die Beschichtung oder den Verbund auf Zug bis zum Versagen. Im Augenblick des Abrisses wird ein positionscodiertes und drehzahlkorreliertes Signal gesendet und so die Bestimmung von Kleb-, Haft- bzw. Verbundfestigkeiten im Mehr-Proben-Versuch möglich. Analog beansprucht ein in einer Führungshülse radial innen an den Proben anliegender ggf. mit entsprechenden Eindringkörpern ausgerüsteter nach außen gerichteter Prüfstempel die Proben auf Druck.
Aus Drehzahl, Radius und Prüfstempelmasse können dann Kleb-, Haft- bzw, Verbundfestigkeiten oder aber Brinell-, Kugeldruck- oder Vickers-Härtewerte bestimmt werden.