Aim of this study is to provide information about moisture dependent material behaviour of unstabilised loadbearing earth blocks and mortars. Compressive strength and Young’s modulus were investigated after conditioning in varying relative humidity reaching from 40 % up to 95 %. The material composition and physical properties were investigated to understand the influence of relative humidity onto the mechanical properties. A normalisation of strength and stiffness by the values obtained at 23 ◦C and 50 % relative humidity reveals a linear dependence of compressive strength and Young’s modulus that is regardless of the material composition.
Thus, it is possible to describe the influence of relative humidity onto the load-bearing behaviour of unstabilised earth masonry materials in a generally valid formulation.
block and mortar types is analysed with particular regard to the influence of varying relative humidity. The uniaxial compressive strength and deformation characteristics of unstabilised earth blocks and mortars as well as of unstabilised earth block masonry are studied in detail and compared to conventional masonry to evaluate whether the structural design can be made accordingly. An increase of 30 % points in relative humidity leads to a reduction of the masonry´s compressive strength between 33 % and 35 % whereas the Young´s modulus is reduced by 24–29 %. However, the ratio between the Young´s modulus and the characteristic compressive strength of earth block masonry ranges between E33/fk = 283–583 but is largely independent of the relative humidity. The results show that the mechanical properties of the investigated unstabilised earth block masonry are sufficient for load-bearing structures, yielding a masonry compressive strength between 2.3 MPa and 3.7 MPa throughout the range of moisture contents
investigated. In general, the design concept of conventional masonry can be adapted for unstabilised earth masonry provided that the rather low Young´s modulus as well as the moisture dependence of both, compressive strength and Young´s modulus, are sufficiently taken into
account.
Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.
The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages.
The main aim of the research was the development of a first valid database for material parameters of earth block masonry (EBM) with particular regard to statistical characteristics. A solid database is needed for the determination of the materials partial safety factor. Therefore, compressive strength tests were carried out with two types of earth blocks and two types of prefabricated earth mortar.
The evaluation has shown that the mean variation of the compressive strength was remarkably less than expected, which indicates high quality standards of the components earth block and mortar with regard to industrial production. Using the reliability method, a partial safety factor for EBM subjected to compression was determined on the basis of these test results. The findings have shown that a common calculation method for EBM based on partial safety factors following the valid masonry construction standard is feasible.
In the beginning of the 1980s earth building has undergone a renaissance, which nowadays leads to an increasing use of load-bearing earth constructions and in particular, earth block masonry. At present, there are no common structural standards according to the semi-probabilistic design concept, which is the state-of-the-art in European standards.
A solid database is needed for the determination of the partial safety factor on the resistance side. Therefore, compressive strength tests were carried out with two types of earth blocks and two types of prefabricated earth mortar. The evaluation showed that the variation of the compressive strength was remarkably less than expected, which seems to indicate high quality standards of the components earth block and mortar with regard to industrial production.
On the basis of these results and together with the reliability method, a partial safety factor for earth block masonry subjected to compression was determined. The main aim of the research was the development of a first valid database for material parameters of earth block masonry with particular regard to statistical characteristics. The results showed that a common calculation method for earth block masonry based on partial safety factors following the valid masonry construction standard is feasible.
On the background of the need for reuse of building rubble and the saving of natural resources, a European Union research project was performed covering concrete technology and durability aspects. A very special precondition was the use of large-scale processed building rubble with unknown origin and the total replacement of aggregates above 2 mm. Comprehensive tests were carried out on the properties of the starting material from different processing plants and fresh concrete, particularly the interdependence of water addition and wor ability. Investigations on hardened concrete properties included strength devel-opment, creep and shrinkage, modulus of elasticity, capillary absorption, freezing and thawing resistance, and carbonation behavior over a long period. The results demonstrate that the industrial production of a high-grade, durable concrete is possible. The project is a promising contribution for sustainable development.