The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure. The smaller the Wasserstein distance is, the higher the residual burst pressure would be and vice versa.
The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure.
Intermediate-scale testing is indispensable when investigating the fire resistance under simultaneous compressive load of components made of glass- and carbon-fibre-reinforced composites (GFRP and CFRP). BAM is successfully operating an intermediate-scale test stand, developed for a specimen size of 500 mm x 500 mm (1000 mm). The fire resistance in terms of fire stability of CFRP and GFRP sandwiches are investigated, e.g. at 20 % of their compressive failure load at room temperature. Times to failure increase by up to a factor of 4 due to intumescent coatings. For GFRP sandwiches, different core structures with and without additional flame retardants show an astonishing impact on time to failure. CFRP shell structures are investigated on the intermediate scale with and without stringer reinforcements, resulting in completely different mechanical failure behaviour in the ultimate load test as opposed to the fire resistance test. The stringers become the only load-carrying part, while the shell acts as a protective layer. Thus the design exploiting this self-protection potential, i.e. the residue of the front skin protecting the load-bearing structure, is highlighted as a most promising route to enhance the fire resistance of lightweight materials.
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon fibre fabric impregnated with reactive epoxy resin. Measurements were carried out using commercially available prepreg material. For Dynamic Mechanical Analysis (DMA), a single cantilever measuring device was applied. The DMA results were refined by additional DSC measurements. The measurements were carried out with dynamic heating in the temperature range -90 to 280 °C. The heating rates were 1 and 2 K/min, respectively. A glass transition of the uncured material (Tg0) near 1 °C, and crosslinking-induced vitrification and devitrification at the maximal glass transition temperature of the cured material (Tgmax) in the temperature range 220 to 230 °C were found. The activation energies for the glass transitions were determined using an Arrhenius plot. By detailed consideration of the influence of the frequency on the DMA data, indications for gelation were deduced.
In Kooperation zwischen dem Institut für Kunststoffverarbeitung (IKV) und der Bundesanstalt für Materialforschung und -prüfung (BAM) wurde das mechanische Verhalten unter Druck- und Zugbelastung unterschiedlicher morphologischer Strukturen teilkristalliner Thermoplaste (PP und POM) untersucht. Im Ergebnis steigt der E-Modul sowohl der druck- wie auch zugbelasteten Prüfkörper aus spritzgegossenem PP und POM mit gröberem Gefüge an. Probekörper mit scherinduziertem Gefüge zeigen einen hohen Einfluss des Kristallisationsgrads auf den E-Modul.