The effect of resting time on the rheological properties of cement suspensions is generally explained by early formed structure and overconsumption of polycarboxylate superplasticizers (PCEs). In this paper, we propose that the influence of resting time on the rheological properties is closely related to size variation of non-absorbed PCE. To identify this, glass bead suspensions were prepared with various amounts of PCE and ionic solution, and their rheological properties were evaluated at various times. We found that the yield stress increases with time at higher PCE concentrations and higher ionic strength solutions. Adsorbed PCE during resting tends to bridge the particles rather than disperse them. In addition, it was found that hydrodynamic radius of PCE increased with resting time, and depletion forces resulting from non-absorbed PCE size changes correlate well with the increased yield stress.
Binary systems composed of Portland cement (PC) and calcium sulfoaluminate (CSA) cement have stood out for applications requiring high early strengths. Nevertheless, the application of these systems may be limited due to their properties in the fresh state, which requires a better understanding of the rheological behavior of these materials. Thus, this study evaluated the incorporation of different polycarboxylate-based superplasticizer (SP) contents (0.15, 0.20, and 0.25 wt%) on PC and PC-CSA binary cement pastes. Rotational rheometry, isothermal calorimetry, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and nitrogen adsorption and desorption tests to assess the pore size distribution of cement pastes were conducted. While the SP incorporation reduced the dynamic yield stress of PC pastes, it progressively increased the yield stress of PC-CSA systems. The increase in SP content increased the main heat flow peak of PC-CSA pastes, although it did not significantly affect the cumulative heat after 160 h of hydration. FTIR and XRD confirm higher ettringite contents in the binary systems and indicate the presence of carboaluminates phases after 7 d of hydration in both PC and PC-CSA and hemicarboaluminate in PC-CSA pastes. The CSA incorporation reduced the cumulative pore volume by up to 32% compared to PC pastes, while the SP content evaluated did not significantly affect the porosity of PC-CSA pastes.