Potential Mapping - What could we measure and what should we able to detect – guideline B03 of DGZfP
(2022)
“Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels.
Areas of corroding reinforcement steel can be located in a non-destructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose, determining the carbonation depth and the concrete cover appears more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.”
Large scale reinforced concrete test specimen for potential mapping under practical conditions
(2017)
Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from e.g. stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. To investigate these influencing factors under practical conditions it requires a specimen with similar damage patterns, dimensions and more factors e.g. metallic mounting parts. Recently the BAM realized such a large scale test specimen for this purpose.