In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer.
Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer. Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.
Here we present the fabrication of a solid-core microstructured polymer optical fiber (mPOF) made of polycarbonate (PC), and report the first experimental demonstration of a fiber Bragg grating (FBG) written in a PC optical fiber. The PC used in this work has a glass transition temperature of 145°C. We also characterize the mPOF optically and mechanically, and further test the sensitivity of the PC FBG to strain and temperature. We demonstrate that the PC FBG can bear temperatures as high as 125°C without malfunctioning. In contrast, polymethyl methacrylate-based FBG technology is generally limited to temperatures below 90°C.