Modifying the level of mostly detrimental welding residual stresses already during the welding process would be highly attractive as time- and cost-consuming post processing may be prevented. The nature of stress buildup during welding-associated cooling is highly affected by phase transformations. Up to now, it is not clear in which way this is applicable to real component welding exhibiting high shrinkage restraint and complex heat input. In this study, two different low transformation temperature (LTT) alloys have been investigated concerning the stress development in restrained multi-run butt welding in order to evaluate the potential of stress reduction. Pulsed gas metal arc welding (P-GMAW) welding was executed on a testing facility designed to simulate real lifelike restraint conditions of component weldments. The effect of reducedMS-temperatures and the heat control on the globally acting stresses was monitored by in-situ measurement of the reaction forces during welding fabrication. Additional local residual stress measurements allowed analyzing global as well as local loading of the welded construction. Although phase transformation has a significant influence on unloading the joint during each weld pass, the reaction stress upon cooling to room temperature seems to be determined mainly by the heat input. On the surface, low longitudinal residual stresses were observed in case of LTT whereas transverse residual stresses are less affected.
For the performance of high-strength steel welds by means of load bearing capacity and safety, the information about stress level and distribution due to welding is needed. The interaction between the filler material grade (strength) and heat input on the reaction stresses in high-strength steels, welded under defined restraint conditions were analysed. Butt welds were joined by a multilayer GMAW process in the Instrumented Restraint Cracking test facility (IRC-test). This test facility allowed a defined restraint and, simultaneously, an in-situ analysis of the reaction stresses while welding and cooling. The reaction force build-up of the weld tests showed a significant influence of the used filler materials according to the heat input. Higher strength filler material grades cause a decrease of the welding stresses compared to lower strength grades, if a low heat input is used. The different stress build-up is described in detail for the root welds, filler layers and subsequent cooling to ambient temperature. Residual stresses in the weld, HAZ and base material were measured in loaded and unloaded condition using the incremental hole drilling method.