It has been shown that selected types of substituents are able to vary the oxidative behavior of multi-walled carbon nanotubes. Such substituents investigated were sterically hindered secondary amino groups bonded in grafted piperidine units and covalently bonded bromine groups. Their interference and activity was preliminary determined in the model cumene and then in oil diesel fraction and low density polyethylene oxidation reactions. Results obtained indicate that chemical linking of amine moieties containing –NH groups directly to the carbon nanotubes core significantly increases their intrinsic anti-oxidative capacity while the grafting of Br-groups provokes the opposite functioning of the pristine samples. This inference was proved by thermogravimetric and differential thermal analysis of the polyethylene composites and experiments on profound aerobic oxidation of petroleum naphthenic fraction derived from the commercial Baku oils blend diesel cut.
Ultrafast laser processing can be used to realize various morphological surface transformations, ranging from direct contour shaping to large-area-surface functionalization via the generation of “self-ordered” micro- and nanostructures as well as their hierarchical hybrids. Irradiation with high-intensity laser pulses excites materials into extreme conditions, which then return to equilibrium through these unique surface transformations. In combination with suitable top-down or bottom-up manufacturing strategies, such laser-tailored surface morphologies open up new avenues toward the control of optical, chemical, and mechanical surface properties, featuring various technical applications especially in the fields of photovoltaics, tribology, and medicine. This article reviews recent efforts in the fundamental understanding of the formation of laser-induced surface micro- and nanostructures and discusses some of their emerging capabilities.
Plastic products used in geotechnical engineering, so-called geosynthetics, are often made of polyolefins (polyethylene or polypropylene) and stabilized against oxidative degradation by antioxidants (AO). Three types of AO “packages” are used: (P1) phenols and phosphites/sulfides, (P2) hindered amines (HAS) with a marginal stabilization P1 of the basic resin, (P3) a combination of packages P1 and P2 with comparable amounts of phenol and HAS. We report about long-lasting oven aging and water immersion tests at 80 °C of 29 different polyolefin based products (geomembranes, geonets and geotextiles). Pronounced differences in the degradation behavior were found depending solely on the type of AO package. In case of P1, the oxidative degradation is prevented by the AO. Autocatalytic oxidation only begins after depletion of AO and may lead to catastrophic failure depending on the environmental conditions. In case of P2, degradation starts right from the beginning. However, it is decelerated and proceeds gradually. In case of P3, the degradation behavior seems to be a superposition of the characteristics obtained for P1 and P2. Plotting the fractional loss of the AO in P1 and P2 as function of the square root of aging time, we identified two regimes of AO depletion. We suggest to attribute this observation to the different mechanisms of AO depletion.