Visualization of surface modifications may be very challenging for coating/substrate systems of either almost identical optical constants, e.g. transparent films on substrates of the same material, or minor film thickness, substance quantity and affected area, e.g. ultra-thin or island films. Methods for visualization are optical microscopy (OM), imaging ellipsometry (IE), and referenced spectroscopic ellipsometry (RSE). Imaging ellipsometry operates at oblique incidence near Brewster angle of the bare, clean or unmodified substrate. In this configuration, reflected intensities are rather weak. However, the contrast to add-on and sub-off features may be superior. Referenced spectroscopic ellipsometry operates in a two-sample configuration but with much higher intensities. In many cases, both ellipsometric techniques reveal and visualize thin films, printed-pattern, laser-induced changes, and impurities better than optical microscopy. In particular for stratified homogeneous modifications, ellipsometric techniques give access to modelling and hence thickness determination. Modifications under investigation are polymer foil residue on silicon, laser-induced changes of ta-C:H coatings on 100Cr6 steel, imperfections of ta-C:H on thermal silicon oxide, degradation of glass, thin film tin oxide pattern on silicon, printed and dried pattern of liquids such as deionized water, cleaning agents, and dissolved silicone. © 2016 Elsevier B.V. All rights reserved.
Gas cylinders made of composite materials receive growing popularity in light-weight applications. Current standards are mostly based on safety determination relying on minimum amounts of endured load cycles and a minimum burst pressure of a small number of specimens. This paper investigates the possibilities of a probabilistic strength assessment for safety improvements as well as cost and weight savings. The probabilistic assessment is based on destructive testing of small sized samples. The influence of sample size on uncertainty of the assessment is analysed. Furthermore, methods for the assessment of in-service ageing (degradation) are discussed and displayed in performance charts.
HNBR, EPDM and FKM O-rings were aged uncompressed and compressed at 75 °C, 100 °C, 125 °C and 150 °C for up to 1 year. HNBR exhibited the strongest ageing effects with high increases of hardness and glass transition temperature. Furthermore, heterogeneous ageing caused by diffusion-limited oxidation effects had a significant influence for HNBR at ageing temperatures of 125 °C and 150 °C. EPDM showed similar property changes as HNBR, but less pronounced. FKM displayed only minor ageing effects. O-rings aged in compression exhibited considerable compression set (CS). CS data was used for a time-temperature shift and resulting master curve construction. Leakage rate measurements showed that O-rings can remain leak tight under static conditions even if material properties have already deteriorated strongly.