Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (196)
- Zeitschriftenartikel (72)
- Beitrag zu einem Tagungsband (64)
- Beitrag zu einem Sammelband (23)
- Forschungsbericht (14)
- Sonstiges (7)
- Posterpräsentation (2)
- Handbuch (1)
Schlagworte
- Korrosion (81)
- Nichtrostender Stahl (43)
- Corrosion (19)
- Korrosionsschutz (18)
- Dauerhaftigkeit (15)
- Werkstoffauswahl (15)
- Pitting corrosion (12)
- Stainless steel (12)
- Passivität (11)
- Deckschichtbildung (10)
- Korrosionsprüfung (10)
- Atmosphärische Korrosion (9)
- Betonstahl (9)
- KorroPad (9)
- Potentialfeldmessung (9)
- Stahlbeton (9)
- Corrosion testing (8)
- Electrochemical noise (8)
- Korrosionsverhalten (8)
- Gelartige Elektrolyte (7)
- Zink (7)
- Atmospheric corrosion (6)
- Bimetallkorrosion (6)
- Concrete (6)
- Edelstahl Rostfrei (6)
- Elektrochemie (6)
- Self-corrosion (6)
- Spannstahl (6)
- Verarbeitung (6)
- Verzinkter Betonstahl (6)
- X-ray tomography (6)
- Zinc coatings (6)
- nichtrostender Stahl (6)
- Chlorinduzierte Korrosion (5)
- Concrete parameters (5)
- Gel-type electrolytes (5)
- Korrosionsbeständigkeit (5)
- Korrosionsschnelltest (5)
- Nichtrostende Stähle (5)
- Reinforcement (5)
- Zinkdeckschichten (5)
- Chloride Induced Corrosion (4)
- Duplexstahl (4)
- Einflussgrößen (4)
- Fehlerquellen (4)
- Layer formation (4)
- Passive layer (4)
- Schleifen (4)
- Spannbeton (4)
- Surface treatment (4)
- Wasserstoff (4)
- Abhilfemaßnahmen (3)
- Atmosphärische Korrosionsbelastung (3)
- Auslagerungsversuche (3)
- Austenit (3)
- Bauwesen (3)
- Beton (3)
- Bewehrung (3)
- Bewehrungsstahlkorrosion (3)
- Cement (3)
- Dekorative Oberflächen (3)
- Desinfektion (3)
- Duplex stainless steels (3)
- Elektrolytwiderstand (3)
- Ferrit (3)
- Fleckenbildung (3)
- Galvanostatic Pulse (3)
- Geothermie (3)
- Kathodischer Korrosionsschutz (3)
- Korrosionsversuche (3)
- Lean Duplex (3)
- Lochkorrosion (3)
- Monitoring (3)
- Oberfläche (3)
- Oberflächenbehandlung (3)
- Oberflächenschutzsystem (3)
- Pflege (3)
- Qualitätskontrolle (3)
- Reinigung (3)
- Spannungsrisskorrosion (3)
- Steel in Concrete (3)
- Stress corrosion cracking (3)
- Surface condition (3)
- Thermische Spritzverzinkung (3)
- Verzinkt (3)
- Verzinkte Einbauteile (3)
- Wasserstoffinduzierte Spannungsrisskorrosion (3)
- Zinc (3)
- Überzüge (3)
- Abwasser (2)
- Aluminium (2)
- Austenitic stainless steels (2)
- Befeuchtungsdauer (2)
- Beständigkeit (2)
- Cathodic protection (2)
- Chlorides (2)
- Chromate (2)
- Chromatreduzierter Zement (2)
- Corrosion Risk (2)
- Corrosion protection (2)
- Corrosion resistance (2)
- Deckschichten (2)
- Duplex (2)
- Electrochemical measurements (2)
- Electrochemical tests (2)
- Elektrochemische Messungen (2)
- Elektrochemische Untersuchungsmethoden (2)
- Elektrochemisches Rauschen (2)
- Embedded Sensors (2)
- Experimentalvortrag (2)
- Ferritic stainless steels (2)
- Ferritischer Stahl (2)
- Feuerverzinkt (2)
- Galvanische Korrosion (2)
- Grease (2)
- Grinding (2)
- Hydrogen evolution (2)
- Hydrogen-induced stress corrosion cracking (2)
- Kerbschlagzähigkeit (2)
- Konstruktion (2)
- Korrosionsuntersuchung (2)
- Korund (2)
- Manganese alloyed stainless steels (2)
- Maritime Atmosphäre (2)
- Maritime atmosphere (2)
- Messraster (2)
- Metallographic section (2)
- Moisture Content (2)
- Mortar (2)
- Nachweisgrenzen (2)
- Oberflächenausführung (2)
- Portable Equipment (2)
- Potential mapping (2)
- Potentialmessung (2)
- Prestressed systems (2)
- Prestressing steel (2)
- Prüfprotokoll (2)
- Quality control (2)
- Rapid corrosion test (2)
- Reinforced and Prestressed Concrete Structures (2)
- Reinforcing steel (2)
- Salinization (2)
- Schadensfälle und Mechanismen (2)
- Schutzwirkung (2)
- Schweißnaht (2)
- Schwimmhallen (2)
- Stahlbetonbau (2)
- Stanznieten (2)
- Trinkwasserleitung (2)
- Verbundzone (2)
- Verfahrensbeschreibung (2)
- Versalzung (2)
- Wax (2)
- Wirksumme (2)
- Zerstörungsfreie Prüfung (2)
- Zinküberzüge (2)
- Örtliche Korrosion (2)
- 3D x-ray (1)
- 8. Tagung (1)
- A. Stainless steel (1)
- Abrasive belt (1)
- Abwasseranlagen (1)
- Agar (1)
- Aktiv-Passiv-Element (1)
- Analytical Chemistry (1)
- Atmospheric exposure (1)
- Atmosphäre (1)
- Austenitic (1)
- Austenitic Stainless Steel (1)
- Austenitic stainless steel (1)
- B. Potentiostatic (1)
- Bauwerkserhaltung/Sanierung (1)
- Bauwerksüberwachung (1)
- Belüftungselement (1)
- Bemessung (1)
- Beschichtungen (1)
- Beschichtungen und Überzüge (1)
- Black Steel (1)
- Black steel (1)
- Boden (1)
- Bodenkontakt (1)
- Böden (1)
- C. Passivity (1)
- C. Pitting corrosion (1)
- Carbon steel (1)
- Cathodic Protection (1)
- Cathodic process (1)
- Cathodic reaction (1)
- Chlorid-induced corrosion (1)
- Chloridbelastete Stahlbetonbauwerke (1)
- Chloride (1)
- Chloride induced corrosion (1)
- Chloridgehalt (1)
- Chloridinduzierte Korrosion (1)
- Chrom VI (1)
- Chromat (1)
- Chromatreduziert (1)
- Chromatreduzierte Zemente (1)
- Civil engineering (1)
- Computertomographie (1)
- Contaminated mortar (1)
- Corrosion Monitoring (1)
- Corrosion Rate (1)
- Corrosion monitoring (1)
- Corrosion rate (1)
- Corrosion risk (1)
- Corrosivity category (1)
- CrNi-Stahl (1)
- Critical pitting temperature (1)
- DIN 1045 (1)
- DIN 50929-3 (1)
- Deckschichtwiderstand (1)
- Defekt (1)
- Depassivierung (1)
- Design for durability (1)
- Desinfektionsmaßnahmen (1)
- Detektion (1)
- Detektion korrosionsempfindlicher Oberflächen (1)
- Drop Evaporation Test (1)
- Duplex-Stähle (1)
- Duplexstähle (1)
- EPR (1)
- EPR test (1)
- Edelstahl (1)
- Einflussparameter (1)
- Einflußgrößen (1)
- Einflüsse (1)
- Electrochemical Impedance Spectroscopy (1)
- Electrochemical Noise (1)
- Electrochemical potentiodynamic reactivation (1)
- Electrochemistry (1)
- Elektrochemische Untersuchungen (1)
- Elektrochemische Versuche (1)
- Erdboden (1)
- Exposition (1)
- Expositionsklassen (1)
- Exposure tests (1)
- FT-IR (1)
- Failure (1)
- Ferritic (1)
- Feuchtemessung (1)
- Feuerverzinkter Stahl (1)
- Free weathering (1)
- Gabionen (1)
- Galvanic corrosion (1)
- Galvanische Pulsmessung (1)
- Galvanized construction elements (1)
- Galvanized elements (1)
- Galvanized rebar (1)
- Galvanized steel (1)
- Galvanostatische Pulsmessungen (1)
- Gel electrolytes (1)
- Gelartige Elektolyte (1)
- Gelelektrolyte (1)
- Geländer (1)
- General Chemical Engineering (1)
- Geothermal (1)
- HSCC (1)
- Hard coatings (1)
- High alkaline environment (1)
- Hochlegierter Stahl (1)
- Hot Cracking (1)
- Humidity (1)
- ISO 9223 (1)
- Indoor swimming pools (1)
- Intercrystalline corrosion (1)
- Interkristalline Korrosion (1)
- Karbonatisierung (1)
- Kathodische Polarisation (1)
- Klassische Auslagerung (1)
- Konzentrationselement (1)
- KorroPad Prüfverfahren (1)
- Korrosion von Stahl in Beton (1)
- Korrosionsbeständige Stähle (1)
- Korrosionseigenschaften (1)
- Korrosionspotentiale (1)
- Korrosionsschnelltest für nichtrostenden Stahl (1)
- Korrosionsschnelltest, Nichtrostender Stahl, Passivschicht, KorroPad (1)
- Korrosionsschutzmittel (1)
- Korrosionsschäden (1)
- Korrosionssensoren (1)
- Korrosionstest (1)
- Korrosionsuntersuchungen (1)
- Korrosivitätsklassen (1)
- Kritischer (1)
- LIBS (1)
- Lagerung (1)
- Langzeitverhalten (1)
- Laser Welding (1)
- Lean duplex (1)
- Lebensdauer (1)
- Lieferzustand (1)
- Lochkorrosionspotential (1)
- Macrocell corrosion model (1)
- Manganese alloyed (1)
- Marine atmosphere (1)
- Maritime Technik (1)
- Martensit (1)
- Mass loss (1)
- Mechanische Oberflächenbearbeitung (1)
- Mediengerechte Werkstoffauswahl (1)
- Merkblatt B 3 (1)
- Mischverbindungen (1)
- Nachbearbeitung (1)
- Nachbehandlung (1)
- Ni-Base Alloy (1)
- Ni-Basislegierung (1)
- Ni-alloy (1)
- Nicht rostender (1)
- Normen und Regelwerke (1)
- Normung (1)
- Numerische Verfahren (1)
- Passivation (1)
- Passivschicht (1)
- Pitting Corrosion (1)
- Polarisationswiderstand (1)
- Polarization (1)
- Portable equipment (1)
- Potentialfeldmessungen (1)
- Potentialverlauf (1)
- Praktische Bedeutung (1)
- Prestressed concrete (1)
- Prüfung (1)
- Pull-out tests (1)
- Qualitätskontrolle der Passivschichtausbildung (1)
- Re-passivation (1)
- Rebar (1)
- Reinforced Concrete (1)
- Reinforced and prestressed concrete structures (1)
- Reinforcement Corrosion (1)
- Reinforcement corrosion (1)
- Reinigung und Pflege (1)
- Repassivation (1)
- Runoff (1)
- Salt-spray testing (1)
- Salzsprühnebelprüfung (1)
- Salzsprühnebeltest (1)
- Schadensfälle (1)
- Schadensursachen (1)
- Schnelltest (1)
- Schweißnahtnachbearbeitung (1)
- Schäden (1)
- Sensoren (1)
- Soil (1)
- Spaltkorrosion (1)
- Spaltkorrosionspotential (1)
- Sprayed zinc layer (1)
- Stainless steels (1)
- Stanless steel (1)
- Steel (1)
- Steel reinforcement (1)
- Steel surface (1)
- Straßentunnel (1)
- Stress corrosion Cracking (1)
- Streustromkorrosion (1)
- Stromdichte-Potential-Kurven (1)
- Surface (1)
- Surface finish (1)
- Surface protection system (1)
- Surface treatments (1)
- Thermal-Sprayed Zinc (1)
- Ti-alloy (1)
- TiMgN (1)
- Tunnel (1)
- Umgebungseinflüsse (1)
- Unalloyed steel (1)
- Verbindungstechnische Lösungen (1)
- Verbund (1)
- Verbundverhalten (1)
- Verfleckungen (1)
- Versprödung (1)
- Video monitoring (1)
- Wasseraufnahme (1)
- Zement (1)
- Zement-, Chlorid-, Wasser/Bindemitteleinfluss (1)
- Zerstörungsfrei (1)
- Zerstörungsfreies Messverfahren (1)
- Zink-Aluminium-Überzug (1)
- Zinküberzug (1)
- corrosion invetsigations (1)
- gel-type electrolytes (1)
- zinc coatings (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (196)
ISO 9223 standard for the classification of corrosivity in atmospheres is based on the mass loss of standard samples. We are concerned with the question of which corrosivity categories for Fe-sheets can be found at an offshore wind turbine and where they are comparable with our offshore locations.
The preliminary results indicate that the extreme corrosivity of class CX is only given in splash water-affected exposure, which is not a real atmospheric exposure condition. The results of the exposure at the SP show that the corrosivity category changes into C4, only a few meters above the splash water zone. Compared to the marine environments at Helgoland or OSS-Platform, the corrosivity is higher. The offshore environment is not as corrosive as originally expected, no atmospheric corrosion attack could be determined that would form the corrosivity category C5.
Nichtrostende Stähle sind in Tunnelbauwerken weitverbreitete Werkstoffe, die für Konstruktionsteile verschiedenster Art häufig verwendet werden. Von einfachen Hilfsbauteilen wie Kabelkanälen bis hin zu komplexen Konstruktionen von Schilderbrücken. Tunnel sind aus Sicht des Korrosionsschutzes sehr speziell und zählen in Mitteleuropa zu den korrosivsten atmosphärischen Umgebungsbedingungen. Grund hierfür ist die Kombination aus hoher Feuchtigkeit, Abgasen der Fahrzeuge (SO2, NOx) und dem winterlichen Streusalzeinsatz (Cl-). Die daraus entstehen-den feuchten Oberflächenfilme sind hochchloridhaltig und weisen durch Reaktionen mit Schwefeldioxid sehr niedrige pH-Werte auf. Durch die in Tunnelbauwerken gleichzeitige fehlende Abwaschung der Oberflächenfilme durch Regenereignisse können sich die Verunreinigungen an vielen Ausstattungsteilen über die Einsatzzeit aufkonzentrieren. Für metallene Bauteile und insbesondere auch für nichtrostende Stähle ist dadurch eine hohe Korrosionsbeanspruchung vorhanden, die bei der Werkstoffauswahl bzw. beim Korrosionsschutz zu berücksichtigen ist. Aufgrund der Gefahr für das Auftreten Spannungsrisskorrosion bei einigen nichtrostenden Stahlsorten in Tunnelatmosphären, sind Regeln für die Werkstoffauswahl in Tunneln aufgestellt worden, die seit vielen Jahrzehnten gültig sind. Diese Regeln waren bis 2015 national in der allgemeinen bauaufsichtlichen Zulassung Z-30.3-6 für nichtrostende Stähle festgehalten und werden seit 2015 im europäische Regelwerk DIN EN 1993 1 4 (Eurocode 3) verbindlich genormt. In den ZTV-ING für den Straßenbau wird in Abschnitt 4 auf diese Regelwerke Bezug genommen.
Die Entwicklungen des nichtrostenden Stahlmarktes in den letzten Jahren, insbesondere für den Bausektor, gehen hin zu den Duplexstählen, da diese aufgrund ihres legierungsspezifisch abgesenkten Nickelgehaltes häufig kostengünstiger als die vergleichbaren Austenite sind. Neben vorteilhaften mechanisch-technologischen Eigenschaften, wie zum Beispiel höhere Festigkeiten, weisen sie zudem auch ausgezeichnete Korrosionsbeständigkeiten auf. Hierzu wurden zahlreiche Studien und Forschungsarbeiten durchgeführt, die diese Vorteile bekräftigen konnten. In Tunnelanwendungen sind Duplexstähle bislang wenig untersucht und deren Korrosionsverhalten kann in dieser speziellen Atmosphäre daher nur bedingt eingeschätzt werden.
Das Forschungsprojekt soll diese Erkenntnislücke schließen und durch eine breit angelegte Parameterstudie Duplexstähle für Tunnelanwendungen qualifizieren. Dafür wurden die Korrosionsbedingungen in den Tunneln umfassend untersucht, die Korrosivität der Tunnelatmosphäre anhand normativer Regelwerke beschrieben und dem Korrosionszustand der Prüfkörper aus nichtrostenden Stählen gegenübergestellt.
Technik, Teamwork und Wirksamkeit - Ein Berufsleben als Ingenieur für die technische Sicherheit
(2024)
Der Vortrag beleuchtet verschiedene Aspekte einer ingenieurtechnischen Tätigkeit zur Gewährleistung der technischen Sicherheit. Er gibt Einblicke in die unterschiedlichen Herausforderungen und die Komplexität der Aufgabenstellungen. An Beispielen wird dargestellt, wie die Ergebnisse der Tätigkeit für die Gesellschaft wirksam werden.
Ausgehend von den Grundlagen der Korrosion stellt der Vortrag die Möglichkeiten des Korrosionsschutzes mit Zink vor. Dabei wird sowohl auf den kathodische Korrosionsschutz mit aktiven Zink-Anoden, als auch auf den Korrosionsschutz durch Deckschichtbildung an Zink und Zinküberzügen eingegangen. Veränderte Umweltbedingungen in Europa in den letzten Jahrzehnten, ermöglichen mit Schichtdicken um 80 µm einen Korrosionsschutz von über 100 Jahren, wenn konstruktive Randbedingungen beachtet werden.
Unter Passivität versteht man den Korrosionsschutz durch dünne, festhaftende Schichten aus Korrosionsprodukten. Für den schadensfreien Einsatz nichtrostender Stähle ergeben sich daraus zwei grundsätzliche Anforderungen.
Erstens muss sich die Passivschicht vollständig ausbilden können. Dabei sind die Oberflächenausführung, die mechanische Bearbeitung, die Elementverteilung, Ausscheidungen, die Wärmeeinbringung z.B. bei der schweißtechnischen Verarbeitung, Anlauffarben, sowie die chemische Nachbehandlung bzw. Konditionierung der Oberflächen von großer Bedeutung. Zweitens muss die Repassivierung von Defektstellen unter den Einsatzbedingungen möglich sein. Für das Repassivierungsvermögen sind die Legierungszusammensetzung, mögliche kritische Betriebszustände, prozessbedingte Besonderheiten, wie etwa Stagnationsbedingungen und Reinigungsprozesse von Bedeutung.
Es werden die Ergebnisse eines mehrjährigen Forschungsvorhabens der BAM in Zusammenarbeit mit Straßenbauverwaltungen der Länder und Industriebeteiligten zur betriebstechnischen Ausrüstung von Straßentunneln präsentiert. Schwerpunkte waren die Bestimmung der Korrosivität der Atmosphäre von 3 ausgewählten Straßentunneln, die Analyse korrosionsrelevanter Ablagerungen und von Klimadaten. Die Auswirkungen dieser Einflussgrößen auf die Dauerhaftigkeit von Konstruktionen aus nichtrostenden Stählen wurde ermittelt und in Abhängigkeit verschiedener Einflussparameter dargestellt. Die Ergebnisse der systematischen Untersuchungen an Prüfköpern decken sich mit Beobachtungen an realen Bauteilen. Spaltbehaftete Konstruktionen aus Werkstoffen der CRC III führen demnach in Zeiträumen zwischen 10 und 15 Jahren zu Korrosionserscheinungen, welche die technische Sicherheit beeinträchtigen können und die erwartete Dauerhaftigkeit nicht erfüllen. Die Folge sind zusätzliche Sperrungen und ein vorzeitig notwendiger Unterhaltsaufwand, die erhebliche Kosten verursachen. Im Ergebnis ist eine Überarbeitung des aktuellen Regelwerkes erforderlich, um die angestrebte Dauerhaftigkeit von 30 Jahren zu gewährleisten.
Korrosionsprüfung
(2024)
Der Vortrag gibt einen Überblick über gängige Korrosionsversuche. Die wesentlichen Unterschiede zwischen Prüf- und Untersuchungsverfahren, deren jeweilige Zielstellung, Aussagefähigkeit und Grenzen werden aufgezeigt. Es werden ausgewählte Auslagerungsversuche, Kammerprüfungen sowie elektrochemische Messmethoden zur Bestimmung der Korrosionsbeständigkeit vorgestellt. Anhand praktischer Beispiele werden ausgewählte Ergebnisse der einzelner Methoden vorgestellt und diskutiert.
Übersichtsvortrag zu Korrosionsarten, die bei nichtrostenden Stählen unter verschiedenen Einsatzbedingungen auftreten können. Die Grundlagen zur Pasivität und der örtlichen Störung der Passivität werden im Zusammenspiel komplexer Einflussfaktoren des Korrosionssystems herausgestellt. Die erarbeiteten theoretischen Grundlagen werden anhand praktischer Beispiel für alle relevanten Korrosionsarten vertieft.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergebnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.