Wood products are often treated by different techniques to improve their longevity when used as building materials. Most of the time, the goal is to increase their resistance to weathering effects, deformations in material dimensions or biotic decomposition. These wood treatment techniques have a significant impact on pyrolysis and burning behavior. The general effects of three different common wood treatments on flame retardancy were investigated by comparing treated woods with their untreated counterparts and with other kinds of wood. While the acetylation of beech leads to a slightly increased fire hazard, the thermal treatment of wood and crosslinking of cellulose microfibrils dimethyloldihydroxy-ethyleneurea show a limited flame retarding effect. Switching to woods with a higher lignin content, and thus higher char yield, however, results in a more pronounced improvement in flame retardancy performance. This article delivers a comprehensive and balanced assessment of the general impact of different wood modifications on the fire behavior. Further, it is a valuable benchmark for assessing the flame retardancy effect of other wood modifications.
A quantitative experimental assessment of flame retardancy by the heat shielding in epoxy layered silicate nanocomposite (EP/TPPMMT) is presented. Online heat flux measurements and temperature monitoring within the specimen are performed during the burning in the cone calorimeter. For EP the surface layer equals a pyrolysis front. The reradiation by the hot surface corresponds to the fourth power of the pyrolysis temperature. The surface reradiation (around 10 kW m-2) is thus fairly invariable over burning time and different external heat fluxes. Further, the thermal feedback of the flame is approximated to 20 kW m-2 for both EP and EP/TPPMMT and invariable over different irradiations. Thus the net heat fluxes transformed to the fuel release rate within the pyrolysis front of EP are increased to 45–80 kW m-2 when irradiations of 35–70 kW m-2 are applied. For a residue-forming EP/TPPMMT the surface temperature and thus the reradiation (42–68 kW m-2) crucially increases compared to EP and with increasing irradiation. The net heat fluxes are reduced to 13–22 kW m-2 accordingly. This quantitative assessment of the heat shielding in EP/TPPMMT goes along with proportional and consistent improvement in the fire performance, such as the pyrolysis front velocity, the heat release rate (HRR) characteristics such as averaged and quasi-steady-state HRR and the peak HRR (PHRR). The heat shielding is proven to be the only major flame retardancy effect occurring in nanocomposites based on non-charring polymers.
The fire retardancy mechanism of aluminium diethyl phosphinate (AlPi) and AlPi in combination with melamine polyphosphate (MPP) was investigated in glass-fibre reinforced polyamide 6 (PA6/GF) by analysing the pyrolysis, flammability and fire behaviour. AlPi in PA6/GF-AlPi partly vaporises as AlPi and partly decomposes to volatile diethylphosphinic acid (subsequently called phosphinic acid) and aluminium phosphate residue. In fire a predominant gas-phase action was observed, but the material did not reach a V-0 classification for the moderate additive content used. For the combination of both AlPi and MPP in PA6/GF-AlPi-MPP a synergistic effect occurred, because of the reaction of MPP with AlPi. Aluminium phosphate is formed in the residue and melamine and phosphinic acid are released in the gas phase. The aluminium phosphate acts as a barrier for fuel and heat transport, whereas the melamine release results in fuel dilution and the phosphinic acid formation in flame inhibition. The higher amount of aluminium phosphate in PA6/GF-AlPi-MPP stabilised the residue in flammability tests in comparison to PA6/GF-AlPi, so that this material achieved a V-0 classification in the UL 94 test.
Fire retardancy effects in single and double layered sol-gel derived TiO2 and SiO2-wood composites
(2012)
Sol–gel derived TiO2 and SiO2-wood inorganic composites are prepared by direct vacuum infiltration of silicon and titanium alkoxide based precursors in pine sapwood in one or two cycles followed by a controlled thermal curing process. The resulting flame retardancy effect is investigated under two different fire scenarios using cone calorimetry and oxygen index (LOI). Heat release rates (HRR) especially the values for the second peak, are reduced moderately for all single layered composites. This effect is more pronounced for double layered composites where HRR was reduced up to 40 % showing flame retardancy potential in developing fires. Beside this, smoke release was lowered up to 72 % indicating that these systems had less fire hazards compared to untreated wood, whereas no meaningful improvement is realized in terms of fire load (total heat evolved) and initial HRR increase. However impressively, the LOI of the composites were increased up to 41 vol% in comparison to 23 vol% for untreated wood displaying a remarkable flame retardancy against reaction to a small flame. An approximate linear interdependence among the fire properties and the material loading as well as fire residue was observed. A residual protection layer mechanism is proposed improving the residue properties for the investigated composites.
Sol–gel technology was applied in tailoring
novel wood-made-inorganic composites with improved
thermal and fire properties. In practice, composites materials
were prepared by impregnating pine sapwood wood with
nano-scaled precursor solutions derived from titanium(IV)
isopropoxide followed by a thermal curing process. Thermal
and fire properties were evaluated by thermal analysis and
cone calorimetry, whereas flammability was specified by
oxygen index (LOI) and UL 94 test. Peak heat release rates
were moderately reduced indicating fire retardance potential
in terms of flame spread attributed to the appropriate protection
layer action of the titania-based depositions. LOI
(oxygen index) values of these composites were increased up
to 38 vol.% in comparison to 23 vol.% for untreated wood.
The flame retardancy performance depends on the fire scenario
and is strongly influenced by wood loading and crackfree
deposition of the titania layers inside the composite.
The pyrolysis and fire behavior of glass-fiber reinforced poly(butylene terephthalate) (PBT/GF) with two different metal phosphinates as flame retardants in combination with and without melamine cyanurate (MC) were analyzed by means of thermogravimetry, thermogravimetry coupled with infrared spectroscopy, flammability, and cone calorimeter tests as well as scanning electron microscopy/energy dispersive X-ray spectroscopy and X-ray fluorescence spectroscopy. In PBT/GF, dosages of 13-20% of the halogen-free flame retardant aluminum phosphinate or aluminum phosphinate in combination with MC fulfill the requirements for electrical engineering and electronics applications (UL 94 = V-0; LOI > 42%), whereas the use of the same amount of zinc phosphinate or zinc phosphinate in combination with MC does not improve the fire behavior satisfactorily (UL 94 = HB; LOI = 27-28%). The performance under forced flaming conditions (cone calorimeter) is quite similar for both of the metal phosphinates. The use of aluminum and zinc salts results in similar flame inhibition predominantly due to the release of the phosphinate compounds in the gas phase. Both metal phosphinates and MC interact with the polymer changing the decomposition characteristics. However, part of the zinc phosphinate vaporizes as a complete molecule. Because of the different decomposition behavior of the metal salts, only the aluminum phosphinate results in a small amount of thermally stable carbonaceous char. In particular, the aluminum phosphinate-terephthalate formed is more stable than the zinc phosphinate-terephthalate. The small amount of char has a crucial effect on the thermal properties and mechanical stability of the residue and thus the flammability.