Filtern
Erscheinungsjahr
- 2011 (13) (entfernen)
Dokumenttyp
- Vortrag (5)
- Zeitschriftenartikel (3)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
- Forschungsbericht (1)
Schlagworte
- Ellipsometry (2)
- Adhesion strength (1)
- Air-coupled ultrasonic transducers (1)
- Bonding strength (1)
- Centrifuge test (1)
- Ellipsometric encoding (1)
- Fabry-Perot layer stacks (1)
- Gas sensing (1)
- Gas sensor (1)
- Iron doped tin oxide (1)
Eingeladener Vortrag
- nein (5)
The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest.
The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers.
The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude.
These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties.
Abschlussbericht zum BMWi/MNPQ-Verbundprojekt VERMERK (versteckte Merkmale) - BMWi-Vorhaben 22/07
(2011)
In this work, thin iron doped tin oxide layers (3–6 nm) were investigated with regard to gas sensitivity by means of surface plasmon resonance (SPR) effect with ellipsometric readout. The experimental set-up was a Kretschmann configuration with gold as metal layer. The sensor system was exposed to different concentrations of methane in the low ppm range and the sensor response of an uncoated gold layer compared to a gold layer coated with iron doped tin oxide. The additional layer effects stability with regard to drift behavior of the sensor and an increase in sensitivity. Furthermore, the sensor is able to detect the toxic gas carbon monoxide in low concentration range (down to 0.5 ppm). The thin layers were investigated by X-ray photoelectron spectroscopy, secondary electron microscopy and spectroscopic ellipsometry. The possible mechanisms taking place on the surface are discussed.
An ellipsometric gas sensor based on the surface Plasmon resonance (SPR) effect of ~ 43 nm thick gold layers was investigated. To protect the gold layer from contamination and to improve the detection limits, the gold layers were top-coated with 5–6 nm thick layers of organic a-C:H or with inorganic metal oxides TiO2 or ZrO2. The additional layers increased the long-term stability, whereas the metal oxide layers protect better than a-C:H. Furthermore, the additional layers decreased the detection limits by one order of magnitude in case of a-C:H and two orders of magnitude in case of the oxides. It could be shown that the detection limits also depend on the kind of preparation (sol–gel process or physical vapour deposition) of the additional layers.