Elastomers are used in a wide range of automotive and railway applications. However, a severe drawback of most rubbers are their high flammability. Therefore, flame retardants (FRs) are added to improve the performance in fire. Generally, rubber composites are filled with high amounts of mineral fillers such as aluminium trihydroxide (ATH) to fulfil fire safety regulations. These high loadings may cause deterioration of the physical properties of the material. This work shows the implementation of two new strategies to achieve the modern demands on non-toxic FRs and the reduction of fillers.
The first approach was the implementation of multilayer graphene (MLG), acting as a multifunctional filler, reinforcing agent and FR. The study presents filler combinations with a systematic variation of the fillers carbon black (CB), MLG and ATH. The nanocomposites were prepared via master batch by an ultrasonically assisted solution mixing. Afterwards the master batch was compounded into the rubber in a two-roll milling. MLG substituted high amounts of the conventional filler CB, leading to reduced filler loadings and a consistent improvement in curing, mechanical and FR properties.
The second strategy was the combination of phosphorous-containing FRs with a potential new polymeric char promoting agent polyaniline (PANI). Char promoting additives such as pentaerythritol (PER) improve the effectiveness of the FR system. The combination of ammonium polyphosphate (APP) with PER was successfully investigated for natural and styrene-butadiene rubber composites. This work investigates the flame retardancy of the combination of FRs with PANI and its capability to act as a char/barrier promoter in EPDM.
The morphology of the rubbers and homogenously dispersion of MLG was investigated via scanning/transmission electron microscope (SEM/TEM) micrographs. Rheological and mechanical measurements assessed the influence of the fillers on the physical properties of the rubber composites. Characterization via thermogravimetric analysis (TGA) led to a broader understanding of the decomposition. In order to determine the flame retardancy effect of these materials, a multi-methodical approach was selected. Limiting oxygen index (LOI) and UL-94 were used to quantify the flammability of the rubber composites. The cone calorimeter provided information about the fire behaviour in forced flaming conditions. Residues were investigated via elementary analysis and XPS to clarify the composition of the remaining material. Glow-Wire and FMVSS 302 tests revealed significant results in terms of flame retardancy. The flame retardancy investigation of rubber composites, combinations of ATH with MLG and ATH with phosphorous-containing FRs, broaden the horizons of rubber flame retardancy solutions. By examining alternate FR formulations and their effect on mechanical and physical properties of the rubber, new insight into the range of applicable additives for rubber composites may be won.
In this study, multicomponent flame retardant systems, consisting of Ammonium polyphosphate (APP), aluminum trihydroxide (ATH), and polyaniline (PANI), were used in ethylene propylene diene monomer (EPDM) rubber. The multicomponent system was designed to improve flame retardancy and the mechanical properties of the rubber compounds, while simultaneously reducing the amount of filler. PANI was applied at low loadings (7 phr) and combined with the phosphorous APP (21 phr) and the mineral flame retardant ATH (50 phr). A comprehensive study of six EPDM rubbers was carried out by systematically varying the fillers to explain the impact of multicomponent flame retardant systems on mechanical properties. The six EPDM materials were investigated via the UL 94, limiting oxygen index (LOI), FMVSS 302, glow wire tests, and the cone calorimeter, showing that multicomponent flame retardant systems led to improved fire performance.
In cone calorimeter tests the EPDM/APP/ATH/PANI composite reduced the maximum average rate of heat emission (MARHE) to 142 kW·m-2, a value 50% lower than that for the unfilled EPDM rubber. Furthermore, the amount of phosphorus in the residues was quantified and the mode of action of the phosphorous flame retardant APP was explained. The data from the cone calorimeter were used to determine the protective layer effect of the multicomponent flame retardant systems in the EPDM compounds.
The impact of polyaniline in phosphorus flame retardant ethylene-propylene-diene-rubber (EPDM)
(2019)
Usually elastomers are loaded with high amounts of flame retardants to fulfill fire safety requirements. In this study the potential char precursor polyaniline (PANI) and the established fire retardant pentaerythritol (PER) were implemented in ethylene-propylene-diene monomer rubber (EPDM). PANI and PER were used in low loadings (7 phr) and combined with two phosphorous flame retardants, Ammonium polyphosphate (APP) and a piperazine-pyrophosphate/phosphoric acid compound (FP), to boost their performance. A comprehensive study is presented, explaining the impact of PANI on curing and mechanical properties, including compensation for the plasticizer-like effect of APP in EPDM, and improved flame retardancy. In the cone calorimeter test, the combination of EPDM/FP/PANI reduced the effective heat of combustion by 20%. All nine EPDM rubber compounds were investigated with the LOI and UL 94 tests, cone calorimeter, FMVSS 302 and glow wire testing to quantify fire performance. The PANI containing EPDM rubbers, EPDM/APP/PANI and EPDM/FP/PANI outperformed the corresponding PER containing, EPDM/APP/PER and EPDM/FP/PER rubbers in various tests. Moreover, the study investigated the impact of PANI and PER on the mode of action of the phosphorus species and showed that the addition of PANI increased the amount of phosphorus in the condensed phase. To receive a broader understanding of the flame retardant mode of action of PANI in combination with APP and FP, calculations were carried out to estimate the impact of PANI on the protective layer effect.