Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (57)
- Vortrag (40)
- Beitrag zu einem Tagungsband (32)
- Monografie (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (2)
- Forschungsbericht (2)
Schlagworte
- Fracture mechanics (25)
- Fatigue strength (19)
- Bruchmechanik (16)
- Schwingfestigkeit (14)
- Weldments (10)
- Fatigue crack propagation (9)
- Fatigue crack propagation threshold (7)
- Short crack propagation (7)
- Short cracks (7)
- FITNET (6)
Organisationseinheit der BAM
- 9 Komponentensicherheit (52)
- 9.4 Integrität von Schweißverbindungen (49)
- 9.0 Abteilungsleitung und andere (7)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 9.6 Additive Fertigung metallischer Komponenten (5)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 4 Material und Umwelt (2)
- 9.3 Schweißtechnische Fertigungsverfahren (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (40)
Die Anwendung bruchmechanischer Methoden zur schadenstoleranten Bauteilauslegung ist für zyklische Lasten im Bereich der Paris-Geraden Stand der Technik. Technisch relevant sind jedoch häufig geringere Lasten im Schwellenwertbereich der d𝑎/d𝑁-Δ𝐾-Kurve. Aufgrund des großen Einflusses von Rissschließeffekten ist dessen Bestimmung jedoch nicht nur aufwändig, sondern auch potenziell fehlerbehaftet. Die Bauteilauslegung erfolgt zweckmäßigerweise auf der Basis effektiver, d. h. rissschließkorrigierter Rissfortschrittsdaten. Von großer Bedeutung ist auch der intrinsische Schwellenwert, unterhalb dessen keine Risserweiterung mehr eintritt. In diesem Forschungsprojekt erfolgte eine Untersuchung des Einflusses verschiedener Prüfverfahren und Umgebungsbedingungen auf die Ermittlung des Schwellenwerts gegen Ermüdungsrissausbreitung Δ𝐾th. Es wurden statistisch abgesicherte Empfehlungen zur experimentellen Ermittlung des intrinsischen Schwellenwerts Δ𝐾th,eff abgeleitet. Dieser dient auch als Eingangsparameter einer weiterentwickelten Prozedur zur Bauteilauslegung auf der Basis bei einem Lastverhältnis von 𝑅 ≈ 0,8 ermittelter, effektiver, Rissfortschrittsdaten. Es zeigte sich, dass die bei einem Lastverhältnis von 𝑅 ≈ 0,8 in Laborluft bei höherer Prüffrequenzen (≥90 Hz) ermittelten Schwellenwerte eine konservative Abschätzung des intrinsischen Schwellenwerts erlaubten. Bei Lastverhältnissen 𝑅 ≪ 0,8 wurde ein teilweise stark ausgeprägter Einfluss extrinsischer Effekte auf das Rissfortschrittsverhalten festgestellt. Eine Untersuchung der Bruchflächen ergab Oxidschichtdicken in der Größenordnung mehrerer hundert Nanometer. Bei Reduktion der Prüffrequenz auf ≈55 Hz und Prüfung in feuchter Luft (60 % r.F. und 80 % r.F.) konnte auch bei 𝑅 = 0,8 Rissschließen beobachtet werden. Die weiterentwickelte Prozedur zur Bauteilauslegung auf Basis effektiver Rissfortschrittsdaten lieferte aber stets konservative Ergebnisse in einem tolerierbaren Fehlerbereich und ist deshalb zur Anwendung geeignet. Die im Projekt gewonnenen Erkenntnisse tragen zu einer robusten Bauteilauslegung auf bruchmechanischer Basis bei. Der stark reduzierte Versuchsumfang bei Nutzung effektiver Rissfortschrittsdaten gegenüber der Ermittlung von spannungsverhältnisabhängigen Rissfortschrittskurven beschleunigt und vereinfacht die Bauteilauslegung auf Basis bruchmechanischer Methoden.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations.
The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation.
In 2015, the University of Manchester hosted a workshop (‘Mind the Gap’) aimed at identifying gaps in a number of structural integrity fitness-for-service procedures, including R5, R6, BS 7910 and API/ASME. The findings were subsequently summarised in a journal paper and shared with the relevant stakeholders. A second workshop, this time hosted by the University of Bristol in 2017, was intended to build on the findings of the earlier event, identifying which gaps had been filled, which remain and whether new ones have been identified in the meantime. ‘Mind the Gap 2’ was wide-ranging, including consideration of failure by fracture, fatigue crack growth, hightemperature creep and environmentally assisted crack growth, along with the use of innovative techniques to follow the progress of crack growth from the atomic to the macroscopic scale. A summary of the whole event is thus outside the scope of a single paper, so here we concentrate mainly on advances in fracture assessment, on the interface between inspection and ECA, and on how developments are being incorporated into structural integrity procedures. There is a particular emphasis on the energy transition in the UK, where the planned energy mix will include both nuclear power and offshore wind.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present two alternative burst speed assessment methods under development based on the Failure Assessment Diagram (FAD) and a global stability criterion, respectively. In the scope of the fracture mechanics assessment, the failure modes hoop-burst and rim-peeling are investigated with semicircular surface cracks modelled at the critical regions on the turbine disk. The comparison of the predicted critical rotational speed shows good agreement between the assessment methods.
Bei der Auslegung von Achsschenkeln für Nutzfahrzeuge wird für den Überlastfall ein fail-safe-Kriterium (kontrolliertes Versagen) als Basisphilosophie angesetzt. Gefordert wird, dass sich der Achsschenkel auch unter Akzeptanz begrenzten Risswachstums hinreichend elastisch-plastisch verformen kann, ohne dass es zum Bruch kommt. Der Fahrer soll anschließend anhand der bleibenden Verformungen bemerken können, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Eine Voraussetzung für dieses Bauteilverhalten ist eine hinreichende Bruchzähigkeit des Werkstoffs. Diese, wie auch die Rissspitzenbeanspruchung, müssen ermittelt werden, um den bruchmechanischen Sicherheitsnachweis führen zu können. Zur Ermittlung der mechanisch-technologischen und bruchmechanischen Werkstoffeigenschaften wurde ein Prüfkonzept entwickelt, bei dem die Proben an der potenziell kritischen Stelle direkt aus den geschmiedeten Achsschenkeln entnommen werden. Die experimentelle Werkstoffcharakterisierung bildet dann die Beanspruchungsbedingungen beim Überlastereignis ab. Im Rahmen der Produktion stehen jedoch nur Kerbschlagarbeitswerte zur Verfügung und aufwändige bruchmechanische Versuche sollen vermieden werden. Deshalb wurde eine Korrelation zur Abschätzung der vorhandenen Bruchzähigkeit aus der Kerbschlagarbeit herangezogen. Es ergibt sich eine Ergebnismatrix, die die Einflussgrößen Versagenswahrscheinlichkeit, Temperatur und Bruchzähigkeit verknüpft. Abschließend wird ein erster Vergleich der abgeschätzten mit den experimentell ermittelten Bruchzähigkeitswerten gezogen. Dieser weist aus, dass die abgeschätzten Werte geringfügig konservativ sind.
Die sichere Auslegung von Bauteilen kommt an der Anwendung bruchmechanischer Methoden heute nicht mehr vorbei. Das vorliegende Buch bietet eine Einführung in diese Methoden mit besonderen Schwerpunkten auf dem aktuellen Stand der bruchmechanischen Kennwertermittlung und den Methoden der analytischen bruchmechanischen Bauteilbewertung. Es beschreibt die Mechanismen von Risswachstum und Bruch, die grundlegenden Konzepte der Bruchmechanik, die analytische Ermittlung der Rissspitzenbelastung in Bauteilen sowie die Anwendung der Bruchmechanik in unterschiedlichen Kontexten. Der Schwerpunkt liegt dabei auf der praktischen Anwendung u. a. anhand von Demonstrationsbeispielen, die im Detail nachvollzogen werden können.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations.
Using the case study of a fail-safe design criterion for a steering knuckle of a commercial vehicle, the effect of stiffness/constraint on the crack driving force in the component is discussed. The problem arises when assessment procedures such as R6, BS 7910 or SINTAP/FITNET are applied in conjunction with substitute geometries for determining the model parameters K-factor and limit load (or a substitute for the latter), as it is common practice. In the example, the conservatism was so pronounced that this procedure was in fact unusable. A way out could be the finite element-based determination of the model parameters and their use in the analytical framework. This procedure is useful and effective if the finite element-based calculations are used in parameter sensitivity analyses.
The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially at low stress ratios 𝑅. In this work, the influence of the experimental procedure and air humidity on d𝑎∕d𝑁 − 𝛥𝐾 data at different 𝑅 is discussed. Unlike the results at 𝑅 = −1, the threshold values obtained at 𝑅 ≈ 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions.