ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
During the service life of structural sealant glazing (SSG) facades, the loadbearing capacity of the silicone bonds needs to be guaranteed. Laboratory Tests can assess the durability of SSG-systems based on mechanical characteristics of the bond after simultaneous exposure to both climatic and mechanical loads.
This article studies how the material characteristics of two common structural sealants are affected by laboratory and field exposure. Dynamic mechanical Analysis (DMA) confirms a reduction in the dynamic modulus of exposed Silicone samples. Results from thermogravimetric analysis, Fourier-transform infrared spectroscopy, differential scanning calorimetry, and small-angle X-ray scattering/wide-angle X-ray scattering show differences between the two sealants and indicate no/minor changes in the composition and morphology of the laboratory and field exposed sealants. Mechanical characterization methods, such as DMA, and tensile and shear testing of the structural bond, are shown to be sensitive toward the combined climatic and mechanical loadings, and are hence suitable for studying degradation mechanisms of structural sealants.