Filtern
Dokumenttyp
- Zeitschriftenartikel (7)
- Beitrag zu einem Tagungsband (3)
- Vortrag (1)
- Posterpräsentation (1)
Schlagworte
- Laser implantation (9)
- Surface texturing (6)
- TiB2 (6)
- Hot stamping (5)
- X38CrMoV5-3 (5)
- Hot-Stamping (3)
- AISI D2 (2)
- Localized laser dispersing (2)
- Presshärten (2)
- Surface modification (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
In the automotive industry, the development of electrically powered vehicles has become a major forward-looking topic. For improving the range and thus the efficiency of electric cars, lightweight construction has gained even more importance. In this regard, hot stamping has been established as a suitable and resource efficient process to manufacture high-strength and lightweight body-in-white components. This method combines hot forming and quenching of boron-manganese steel 22MnB5 in a single process step. As a result, complex structures with thin sheet thicknesses and high ultimate tensile strength up to 1500 MPa are generated. However, the use of lubricants is not possible at elevated temperatures, which subsequently leads to high thermo-mechanical tool stresses. As a side effect, high friction and severe wear occur during the forming process, which affect the resulting part quality and maximum tool life. Therefore, the aim of this study is to improve the tribological performance of hot stamping tools by using a laser implantation process. This technique is based on manufacturing highly wear resistant, separated and elevated structures in micrometer range by embedding hard ceramic particles into the tool material via pulsed laser radiation. As a result, highly stressed areas on the tool surface can be modified locally, which in turn influence the tribological and thermal behavior during the forming process. In this regard, laser implanted and conventionally tool surfaces were investigated under hot stamping conditions. A modified pin-on-disk test was used to analyze the friction coefficient and occuring wear mechanisms. Furthermore, quenching tests as well as hardness measurements were carried out to gain in-depth knowledge about the cooling behavior of the modified tool surfaces and its impact to the resulting mechanical part properties.
In the automotive industry, hot stamping has been established as a key technology for manufacturing safety-relevant car body components with high strength-to-weight ratio. However, hot stamping tools are stressed by cyclic thermo-mechanical loads, which leads to severe wear and high friction during the forming operation. Consequently, the quality of the parts, the durability of the tools and the efficiency of the process are negatively affected. Within the scope of this work, a promising approach named laser implantation process has been investigated for improving the tribological behavior of hot stamping tools. This technique enables the fabrication of highly wear resistant, separated and elevated micro-features by embedding hard ceramic particles into the tool via pulsed laser radiation. Hence, highly stressed tool areas can be modified, which influences the thermal and tribological interactions at the blank-die interface. To clarify these cause-effect relations, numerical simulations, quenching tests as well as tribological investigations have been conducted. In this context, laser-implanted tools reveal a significantly improved tribological performance while offering the possibility to adjust the thermal properties within hot stamping. Based on these results, a tailored tool modification can be pursued in future research work, in order to enhance the effectiveness of hot stamping tooling systems.
The aim of this study is to increase the tribological performance of hot stamping tools by using a laser implantation process. This technique allows the fabrication of separated, elevated and dome-shaped microfeatures on the tool surface in consequence of a localized dispersing of ceramic particles via pulsed laser radiation. Hence, the topography and material properties of the tool are modified, which influences the tribological interactions at the blank-die interface. However, an appropriate selection of ceramic particles is an essential prerequisite, in order to obtain tailored and highly wear resistant surface features. In this regard, different titanium-based hard particles (TiB2 and TiN) were laser-implanted on hot working tool specimens and subsequently tested by means of a modified pin-on-disk test regarding to their wear and friction behavior.
Within the scope of this work, a new surface engineering technology named laser implantation has been investigated, in order to improve the tribological performance of hot stamping tools. This technique is based on manufacturing highly wear-resistant, separated, and elevated microfeatures by embedding hard ceramic particles into the tool surface via pulsed laser radiation.
Hence, the topography and material properties of the tool are modified, which influences the thermal and tribological interactions at the blank-die interface. To verify these assumptions and to clarify the cause–effect relations, different titanium-based particles (TiB2, TiC, TiN) were laser-implanted and subsequently analyzed regarding to their geometrical shape and mechanical properties. Afterwards, quenching tests as well as tribological experiments were carried out by using titanium-diboride as the most promising implantation material for reducing the tribological load due to high hardness value of the generated implants. Compared to conventional tooling systems, the modified tool surfaces revealed a significantly higher wear resistance as well as reduced friction forces while offering the possibility to adjust the thermal interactions at the blank-die interface. Based on these results, a tailored tool surface modification can be pursued in future research work, in order to enhance the effectiveness of the hot stamping technology.
The control of friction and wear is a major concern in many industrial applications. A promising method for tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in a deterministic pattern where needed on highly stressed surfaces, i.e., on forming or cutting tools.
However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free metal matrix composite with a high share of homogeneously distributed particles and, especially, high implant hardness. In this study, TiN, TiC, and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel were investigated.
Although all powder materials had grain sizes smaller than 10 μm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (∼64%) was observed for TiB2. By scanning electron microscopy and energy dispersive x-ray spectroscopy, it was also shown that a significant share of the preplaced particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By x-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in situ formation of TiC particles, which was proven by electron backscatter diffraction.
In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown
the most promising results.
The potential of lowered surface features as well as the application of wear resistant coatings have been known for many years to improve the tribological behavior of forming tools. More recent studies also discuss the capability of protruded microfeatures for adjusting the tribological behavior between contacting surfaces. The demand for a high wear resistance of such structures as well as their economical and reliable production, however, often limits the industrial application. The laser implantation process can overcome these limitations. In contrast to conventional cw-laser dispersing processes, where the formation of uniform metal matrix composite layers is intended, this surface engineering technique aims to improve the tribological behavior of contacting surfaces by a localized dispersing of pre-placed hard ceramic particles. This enables the formation of deterministic textures composed of separated wear resistant dome- or ring-shaped microstructures (implants).
Since TaC shows very promising material properties for improving the wear resistance of tools exposed to severe operating conditions, this paper analyzes its suitability for pulsed laser implantation on X38CrMoV5-3 tool steel for the first time. In the experiments, the influence of the particles and the laser parameters (pulse power, pulse duration and focal diameter) on the material properties of the localized dispersed zones was studied by optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction. The composite´s (micro-) hardness was measured and calculated by using a rule of mixture. Additionally, the influence of the laser parameters and the TaC particles on the geometrical properties of the implants was studied by optical microscopy and white light interferometry.
The results showed that defect-free implants with hardness values of ~900 HV1 can be obtained at the focal spot, since a localized dispersing of the TaC particles is possible using a pulsed millisecond laser. However, in dependence of the laser intensity, also a partial dissolution of the initial particles occurs. This leads to the precipitation of new dendritic TaC nanoparticles and to varying contents of retained austenite in the matrix. Both effects have a strong influence on the implant hardness and must be considert by the rule of mixture. Regarding the geometrical response it was pointed out that protruded microfeatures with heights up to 10 µm can be created. In comparison to laser remelted zones, the implanted zones showed significantly altered weld pool profiles due to the influence of the particles on the melt convection. A transition of the implant shape from predominantly dome-shaped to predominantly ring-shaped was observed for intensities >1.7∙106 W/cm2 due to the onset of the keyhole effect.
The laser implantation–named technique aims to address the tribological problems frequently seen on tool surfaces during hot stamping. It is based on the creation of elevated dome- or ring-shaped hard structures on the surface of tool steels by a localized dispersing of hard particles. Therefore, a combination of the two distinct approaches that are normally used in surface Technology for optimizing friction and wear, i.e., surface texturing and surface material optimization, are realized in one processing step. In experimental studies, a localized dispersing of TiB2 particles in the surface layer of the hot work tool steel X38CrMoV5-3 was considered and compared with punctual laser–remelted textures. The structures (micro-) hardness was measured at top- and cross-sections. With the aid of a scanning electron microscope, energy dispersive X-ray spectroscopy and X-ray diffraction the interaction between the hard particles and the substrate material were studied. From the results, an optimal parameter range was identified for laser implantation. To the investigation’s end, the implant geometry was measured by optical microscopy and White light microscopy. Furthermore, a mathematic model was introduced, which allows a prediction of the implant geometry as a response to the laser parameters. It was shown that the implantation of TiB2 particles leads to a significant hardness increase up to 1600 HV1 due to the dispersion of initial particles and an in situ precipitation of new titanium-rich phases. It was possible to create defect-free dome- and ring-shaped microstructures on the surfaces. It was also shown that the implants geometry highly depends on the applied laser parameters. The applied central composite design shows a good agreement with the experimental results.
Das Presshärteverfahren hat sich zur ressourceneffizienten Verarbeitung von höchstfesten Stahlwerkstoffen im Karosserieleichtbau weltweit etabliert. Die fehlerfreie Bauteilproduktion wird jedoch durch Reibungs- und Verschleißerscheinungen aufgrund hoher thermo-mechanischer Werkzeugbelastungen und fehlender Schmierstoffsysteme limitiert. Als Lösungsansatz wird eine Modifikation der Werkzeugoberfläche mittels Laserimplantation angestrebt, um folglich deren Verschleißbeständigkeit nachhaltig zu erhöhen. Das Verfahren basiert auf einem lokalen Dispergieren keramischer Hartstoffpartikel in die Werkzeugoberfläche, infolgedessen hochfeste und erhabene Strukturen im Mikrometerbereich entstehen. Aufgrund der signifikanten Reduzierung der Kontaktfläche sowie der hohen Verschleißbeständigkeit der eingesetzten TiB2-Hartstoffe wird ein verbessertes tribologisches Einsatzverhalten unter presshärtetypischen Prozessbedingungen erwartet. Zur Verifizierung dieser Annahmen wurden im Rahmen dieser Arbeit modifizierte Pin-on-Disk Tests durchgeführt, um das Reib- und Verschleißverhalten der laserimplantierten Werkzeugoberflächen unter Presshärtebedingungen zu untersuchen. Zur weiteren Vertiefung des Prozess-verständnisses wurden die verschlissenen Platinen via Tastschnittmessungen und Querschliffaufnahmen analysiert. Durch den Ergebnisvergleich mit konventionellen Werkzeugoberflächen erfolgte eine abschließende Bewertung des tribologischen Einsatzverhaltens der laserimplantierten Strukturen.
Das Presshärteverfahren hat sich zur ressourceneffizienten Verarbeitung von höchstfesten Stahlwerkstoffen im Karosserieleichtbau weltweit etabliert. Die fehlerfreie Bauteilproduktion wird jedoch durch Reibungs- und Verschleißerscheinungen aufgrund hoher thermo-mechanischer Werkzeugbelastungen und fehlender Schmierstoffsysteme limitiert. Als Lösungsansatz wird eine Modifikation der Werkzeugoberfläche mittels Laserimplantation angestrebt, um folglich deren Verschleißbeständigkeit nachhaltig zu erhöhen. Das Verfahren basiert auf einem lokalen Dispergieren keramischer Hartstoffpartikel in die Werkzeugoberfläche, infolgedessen hochfeste und erhabene Strukturen im Mikrometerbereich entstehen. Aufgrund der signifikanten Reduzierung der Kontaktfläche sowie der hohen Verschleißbeständigkeit der eingesetzten TiB2-Hartstoffe wird ein verbessertes tribologisches Einsatzverhalten unter presshärtetypischen Prozessbedingungen erwartet. Zur Verifizierung dieser Annahmen wurden im Rahmen dieser Arbeit modifizierte Pin-on-Disk Tests durchgeführt, um das Reib- und Verschleißverhalten der laserimplantierten Werkzeugoberflächen unter Presshärtebedingungen zu untersuchen. Zur weiteren Vertiefung des Prozess-verständnisses wurden die verschlissenen Platinen via Tastschnittmessungen und Querschliffaufnahmen analysiert. Durch den Ergebnisvergleich mit konventionellen Werkzeugoberflächen erfolgte eine abschließende Bewertung des tribologischen Einsatzverhaltens der laserimplantierten Strukturen.
The control of friction and wear is a major concern in many industrial applications. A promising method for a tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in deterministic pattern where needed on highly stressed surfaces, i.e. on forming or cutting tools. However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free Metal Matrix Composite with a high share of homogeneously distributed particles and especially a high implant hardness.
In this study TiN, TiC and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of the pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel was investigated. Although all powder materials had grain sizes smaller than 10 µm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (~64 %) was observed for TiB2. By scanning electron microscopy and energy dispersive X-ray spectroscopy, it was also shown that a significant share of the pre-placed particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in-situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 HV1 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By X-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in-situ formation of TiC particles, which was proven by electron backscatter diffraction. In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown the most promising results.