The paper presents the first complex study of Gamma radiation effects on a low-loss perfluorinated polymer optical fiber (PF-POF) based on Cytop® polymer. Influence of gamma radiation on fiber’s optical, mechanical and climatic performance is investigated. The radiation-induced attenuation (RIA) in the visible and near-infrared region (0.4 μm-1.7 mm) is measured and its origins are discussed. Besides attenuation increase, radiation is also shown to decrease the thermal degradation stability of the fiber and to increase its susceptibility to water. With regard to complex fiber transmission performance upon irradiation, the optimal operation wavelength region of PF-POF-based systems intended for use in Radiation environments is determined to be around 1.1 μm. On the other hand, the investigated fiber holds potential for low-cost RIA-based optical fiber dosimetry applications with sensitivity as high as 260 dBm⁻¹/kGy in the visible region.
The sensitivity of low-loss perfluorinated polymer optical fiber (PF-POF) to gamma radiation is investigated for on-line radiation monitoring purposes. The radiation-induced attenuation (RIA) of a commercial PF-POF based on Cytop material is measured in the visible spectral region. The fiber RIA shows strong wavelength dependence with rapid increase towards the blue side of the spectrum. The wide range of radiation sensitivities is available via careful selection of appropriate monitoring wavelength. The accessible sensitivities span from 1.6 ± 0.2 dBm-1/kGy measured at 750 nm to 18.3 ± 0.7 dBm-1/kGy measured at 420 nm. The fairly high radiation sensitivity as well as its wide tunability makes the fiber a promising candidate for a broad range of applications.
In this paper, we present the first results regarding the on-line monitoring of gamma-ray exposure effects on a commercial multi-mode perfluorinated polymer optical fiber (PF-POF), type GigaPOF-50SR from Chromis Fiberoptics. Our focus was to evaluate on-line the radiation induced attenuation (RIA) over a wide spectral range (320 nm – 1700 nm), in order to assess the fiber’s radiation hardness and its possible use in radiation detection. An Ocean Optics QE65000 high sensitivity spectrometer and a StellarNet near-IR spectrometer were used to cover the spectral ranges 200 nm – 1μm and 900 nm – 1.6 μm, respectively. Electron paramagnetic resonance was used to monitor the recovery of the irradiation induced centers at room temperature. The study indicated that the optical fiber can be used as radiation monitor at low dose rates by measuring the attenuation in the UV, while higher dose rates irradiation can be observed by RIA monitoring at specific wavelengths in the visible spectral range.