The coming years are expected to bring rapid changes in the nanotechnology regulatory landscape, with the establishment of a new framework for nano-risk governance, in silico approaches for characterisation and Risk assessment of nanomaterials, and novel procedures for the early identification and management of nanomaterial risks. In this context, Safe(r)-by-Design (SbD) emerges as a powerful preventive approach to support the development of safe and sustainable (SSbD) nanotechnology-based products and processes throughout the life cycle. This paper summarises the work undertaken to develop a blueprint for the deployment and operation of a permanent European Centre of collaborating laboratories and research organisations supporting safe Innovation in nanotechnologies. The proposed entity, referred to as “the Centre”, will establish a ‘one-stop shop’ for nanosafety-related services and a central contact point for addressing stakeholder questions about nanosafety. Its operation will rely on significant business, legal and market knowledge, as well as other tools developed and acquired through the EU-funded EC4SafeNano project and subsequent ongoing activities. The proposed blueprint adopts a demand-driven service update scheme to allow the necessary vigilance and flexibility to identify opportunities and adjust its activities and services in the rapidly evolving regulatory and nano risk governance landscape.
The proposed Centre will play a major role as a conduit to transfer scientific knowledge between the Research and commercial laboratories or consultants able to provide high quality nanosafety services, and the end-users of such services (e.g., industry, SMEs, consultancy firms, and regulatory authorities). The Centre will harmonise service provision, and bring novel risk assessment and management approaches, e.g. in silico methodologies, closer to practice, notably through SbD/SSbD, and decisively support safe and sustainable innovation of industrial production in the nanotechnology industry according to the European Chemicals Strategy for Sustainability.
This is a corrigendum to the original article "Determining the thickness and completeness of the shell of polymer core-shell nanoparticles by X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and transmission scanning electron microscopy" that was published in "The journal of physical chemistry C", vol. 123 (2019), no. 49 pp. 29765-29775.
Core–shell nanoparticles (CSNPs) have become indispensable in various industrial applications. However, their real internal structure usually deviates from an ideal core–shell structure. To control how the particles perform with regard to their specific applications, characterization techniques are required that can distinguish an ideal from a nonideal morphology. In this work, we investigated poly(tetrafluoroethylene)–poly(methyl methacrylate) (PTFE–PMMA) and poly(tetrafluoroethylene)–polystyrene (PTFE–PS) polymer CSNPs with a constant core diameter (45 nm) but varying shell thicknesses (4–50 nm). As confirmed by transmission scanning electron microscopy (T-SEM), the shell completely covers the core for the PTFE–PMMA nanoparticles, while the encapsulation of the core by the shell material is incomplete for the PTFE–PS nanoparticles. X-ray photoelectron spectroscopy (XPS) was applied to determine the shell thickness of the nanoparticles. The software SESSA v2.0 was used to analyze the intensities of the elastic peaks, and the QUASES software package was employed to evaluate the shape of the inelastic background in the XPS survey spectra. For the first time, nanoparticle shell thicknesses are presented, which are exclusively based on the analysis of the XPS inelastic background. Furthermore, principal component analysis (PCA)-assisted time-of-flight secondary-ion mass spectrometry (ToF-SIMS) of the PTFE–PS nanoparticle sample set revealed a systematic variation among the samples and, thus, confirmed the incomplete encapsulation of the core by the shell material. As opposed to that, no variation is observed in the PCA score plots of the PTFE–PMMA nanoparticle sample set. Consequently, the complete coverage of the core by the shell material is proved by ToF-SIMS with a certainty that cannot be achieved by XPS and T-SEM.
Nanomaterials are a relatively new class of materials for which a regulatory framework still has to be established and regulators require comprehensive datasets of well characterized nanomaterials for the implementation. Especially information about the surface chemistry of nanoparticles is crucial, since it largely determines their biological and environmental fate. How the surface chemistry changes under relevant ageing conditions is of particular interest, because exposure will normally occur not to the pristine material but to a nanoform that underwent some kind of transformation.
In this talk, first a short overview about the contributions of division 6.1 to multiple European-funded projects will be presented, in which surface analytical techniques are used to improve the physical-chemical characterization of nanomaterials. Secondly, a study investigating the surface-chemical transformations of a representative set of titanium dioxide nanoparticles is discussed in more detail. The ageing has partly been performed at the BAM division 7.5, and the surface chemistry was analyzed using time-of-flight secondary ion mass spectrometry (ToF-SIMS) and X-ray photoelectron spectroscopy (XPS). By analyzing the complex mass spectra with principal component analysis (PCA), it was possible to identify even subtle changes that occur upon ageing.
Three current research projects performed at BAM’s Division for Surface Analysis and Interfacial Chemistry are presented that tackle important challenges with regard to the characterization of nanomaterials: 1) The characterization at ambient pressure, 2) the investigation of core-shell nanoparticles, and 3) the characterization of non-spherical particles by electron microscopy.
1) Surface analytical techniques such as Photoelectron Spectroscopy (XPS) or Secondary Ion Mass Spectrometry (SIMS) typically require measurements in ultra-high vacuum. However, for many applications (e.g. catalysis and nanotoxicology) it is important to know the surface chemical properties of nanomaterials at ambient conditions. Therefore, near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) was used to investigate nanoparticles in suspension. The used instrumental set-up allows to directly insert nanoparticle suspensions into the analysis chamber and to measure without prior sample preparation. Compared to dry reference samples measured under high-vacuum, a shift towards higher binding energies was observed for silver nanoparticles in water, indicating a change of surface potential at the water-nanoparticle interface.
2) To determine the dimensions of core-shell nanoparticles (shell thickness, core and total diameter), scanning transmission X-ray microscopy (STXM) was used. The analyzed model system consists of a polytetrafluorethylene (PTFE) core surrounded by a polystyrene (PS) shell, providing a strong X-ray absorption contrast at the C K-edge and a well-defined interface. The introduced STXM‐based methodology yields particle dimensions in agreement with scanning electron microscopy (SEM) results and provides additional information such as the position of the particle core, which cannot be extracted from a SEM micrograph.
3) The accurate measurement of size distributions of non-spherically shaped nanoparticles (representing most of the industrial nanoparticulate materials) is a challenging analytical task. High-resolution electron microscopy (TEM and SEM) is best suited to access the shape of individual nanoparticles. To fill the gap between ideal, monodisperse particles of spherical shape and complex real-world samples, BAM has started the work to develop reference nanoparticles of controlled shape, such as TiO2 platelets, bipyramids, and elongated particles. Results of a recent ISO inter-laboratory comparison will be shown with emphasis on the measurement parameters, descriptors and data analysis.