Nowadays, sensors based on polymers/nanostructured metal oxide composites have been investigated exten-sively because of their sensitivity to NO2 gas at ambient temperature. In this work, nanocomposite membranes of xanthan gum (XG) with different contents of MnO2 nanoparticles were prepared as a potential NO2 gas sensor operating at room temperature by a simple one-step oxidation-reduction reaction. The structural, morphological, thermal, and electrical properties of the composite membrane were investigated. The FT-IR results confirm the successful preparation of MnO2 through the oxidation of XG by KMnO4 and reveal further the structural changes of the XG/MnO2 nanocomposite upon its exposure to NO2 gas. The capping of the synthesized MnO2 nano-particles by XG, the surface composition of the XG/MnO2 nanocomposite membranes, and the effect of NO2 gas on the surface composition was investigated using the XPS technique. The DC conductivity and dielectric loss of nanocomposites were higher than for neat XG. The conductivities of the nanocomposites XG/MO-4, XG/MO-4/ low NO2, and XG/MO-4/high NO2 composites are half, one, and three orders of magnitude higher than that for pure XG revealing a transition from insulating to conductive properties. The results demonstrated that XG/MnO2 nanocomposite membranes are promising for potential applications in NO2 gas sensing.
An immobilization of graphene oxide (GO) into a matrix of polyvinyl formaldehyde (PVF) foam as an eco-friendly, low cost, superior, and easily recovered sorbent of Pb ions from an aqueous solution is described. The relationships between the structure and electrochemical properties of PVF/GO composite with implanted Pb ions are discussed for the first time. The number of alcohol groups decreased by 41% and 63% for PVF/GO and the PVF/GO/Pb composite, respectively, compared to pure PVF. This means that chemical bonds are formed between the Pb ions and the PVF/GO composite based on the OH groups. This bond formation causes an increase in the Tg values attributed to the formation of a strong surface complexation between adjacent layers of PVF/GO composite. The conductivity increases by about 2.8 orders of magnitude compared to the values of the PVF/GO/Pb composite compared to the PVF. This means the presence of Pb ions is the main factor for enhancing the conductivity where the conduction mechanism is changed from ionic for PVF to electronic conduction for PVF/GO and PVF/GO/Pb.
The electrospray ionization (ESI) method was used for deposition of thin films of poly(acrylic acid) (PAA) onto ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 zeolites. This method allowed the formation of uniform polymer films of controlled thickness on conductive substrates.
The zeolites were prepared home-made. The effect of incorporation of Cu (5 wt.%) and Ag-Cu (1+4 wt.%) onto ZSM-5 on its particle size, unit cell parameters and crystallinity was investigated.
The deposited PAA layer acts as a common dispersing agent with its ionic COOH (COO-) groups. The antibacterial activity towards the bacterial strains such as Staphylococcus pneumonia (S. Pneumonia), Bacillus subtilis (B. subtilis), Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) as Gram positive and Gram negative bacteria, respectively, and Aspergillus fumigatus (A. fumigatus), Candida albicans (C. albicans) as Fungi was evaluated. The chemical and physical modifications of ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 surfaces were characterized by X-ray photoelectron spectroscopy, Fourier-transform infrared spectroscopy, atomic force microscopy and X-ray diffraction.
The Cu/ZSM-5 and Ag-Cu/ZSM-5 nanocomposites coated with a 10 nm thick PAA layer exhibit significant antibacterial activity. The carboxyl (¬-COOH) or the corresponding carboxylate groups (¬-COO-) interact with Cu2+ and Ag+ ions by formation of ionic bonds (¬-COO-Ag+ or 2 ¬-COO->Cu2+). Moreover, short exposure to light and temperature has reduced Cu2+ and Ag+ to Cu0 and Ag0.
Thin poly(acrylic acid) PAA films were deposited by pulsed plasma polymerization on different organic and inorganic substrates. The structureproperty relationships of the deposited acrylic acid polymers were studied in dependence on the monomer pressure by various techniques and probes. The surface and bulk properties of the plasma deposited films were investigated by X-ray photoelectron spectroscopy, attenuated total reflection infrared, and broad band dielectric spectroscopy. The experimental infrared frequencies of PAA films are compared with those predicted from quantum mechanical calculation. The concentration of the COOH groups in the film (stored in ambient air) decreased by about 15 % compared to the as-prepared sample. The plasma deposited PAA probably form a highly branched product. However, the dielectric measurements show that in addition to the hydrogen bonds, self condensation process was able to hinder the localized fluctuation as well. These processes lead to form a cross-linked network polymer film. Nevertheless, a low energy is sufficient to break these processes during heating at atmospheric pressure. Therefore, homogenized samples with free branches (functional group) were obtained after a first heating with structures close to conventional polymerized acrylic acid. Thus, a thermally stable product was obtained.
The pulsed plasma polymerization of allyl alcohol was employed under the aspect of maximal retention of OH groups and the formation of a regular polymer structure. It should be noted that earlier investigations on plasma polymers deposited from allyl alcohol did not show extensive postplasma addition of oxygen and water vapor from ambient air during storage, measuring the elemental O/C ratio by means of X-ray photoelectron spectroscopy (XPS).The identification of OH groups in the plasma polymerized polymer using FTIR spectroscopy was such an indicator for fragmentation. The peak area of OH groups in the film which was stored was increased by about 20% compared to that measured ('in situ'). These phenomenons reflected that moisture and O2 in air played an important role in scavenging the free radicals. The addition of water and more specifically chemical bonding of OH of water in the deposited plasma polymer may serve as an indicator for monomer fragmentation, poly recombination, and the remaining radicals responsible for film formation. Moreover, the dielectric measurements show that the plasma deposited films are not thermally stable but undergo a postplasma chemical reaction during heating, where the reaction kinetics depends on pressure.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
Degradation behavior of thin polystyrene films on exposure to Ar plasma and its emitted radiation
(2013)
Spin-coated films of amorphous polystyrene (PS) were exposed to argon plasma for a few seconds to several minutes. The PS film was either in direct contact with the plasma or was shielded from the direct plasma contact by filters with different cutoff wavelengths in the vacuum UV region or by a Faraday cage (FC) made from metal mesh to prevent the impinging of charged species. Only energy-rich neutrals and plasma radiation may be operative in presence of the FC. lithium fluoride (LiF) filter protects the sample from direct contact with the plasma. Wavelengths of plasma radiation shorter than c. 105 nm (≈ 11.8 eV) were cut off. Glass filters made of fused SiO2 have a cutoff at λ ≈175?nm completely the vacuum UV radiation of plasma (ca. 175 nm ≈ 7.0 eV). These energies are sufficient to produce C–C, C–H bond scissions in case of direct Ar plasma exposure and Ar plasma exposure with use of the LiF filter. Only quartz glass shielding did not produce significant effects on the polymer surface in comparison to the reference PS, either in surface energy or O/C ratio or in IR spectra. Oxygen plasma has worked most aggressive and had etched the PS film, thus establishing a steady state between introduction of new oxygen functionalities and polymer etching. Ar plasma exposure produces also oxidation and etching of the polymer films as the oxygen plasma. Using of a FC during Ar plasma exposure or the LiF filter a slightly weaker oxidation was observed.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.