The process of viscous flow sintering is a phenomenon that is closely linked to the surface properties of the glass particles. In this work, we studied the extreme case of acid-leaching of soda-lime-silicate glass beads of two different particle size distributions and its effects on non-isothermal viscous sintering of powder compacts. Depth profiling of the chemical composition after leaching revealed a near-surface layer depleted in alkali and alkaline earth ions, associated with concurrent hydration as mass loss was detected by thermogravimetry. Heating microscopy showed that acid treatment of glasses shifted the sinter curves to higher temperatures with increasing leaching time. Modelling of the shrinkage with the cluster model predicted a higher viscosity of the altered surface layer, while analysis of the time scales of mass transport of mobile species (Na+, Ca2+ and H2O) during isochronous sintering revealed that diffusion of Na+ can compensate for concentration gradients before sintering begins. Also, exchanged water species can diffuse out of the altered layer, but the depletion of Ca2+ in the altered surface layer persists during the sinter interval, resulting in a glass with higher viscosity, which causes sintering to slow down.
Literature data on the effect of water on the glass transition in silicate melts are gathered for a broad range of total water content cw from 3 × 10-4 to 27 wt%. In terms of a reduced glass transition temperature Tg*=Tg/TgGN, where TgGN is Tg of the melt containing cw?0.02 wt% total water, a uniform dependence of Tg* on total water content (cw) is evident for silicate melts. Tg* decreases steadily with increasing water content, most strongly at the lowest water content where H2O is dominantly dissolved as OH. For water-rich melts, the variation of Tg* is less pronounced, but it does not vanish even at the largest water contents reported (?27 wt%). Tg* vs. cw is fitted by a three-component model. This approach accounts for different transition temperatures of the dry glass, hydroxyl and molecular water predicting Tg* as a weighted linear combination of these temperatures. The required but mostly unknown water speciation in the glasses was estimated using IR-spectroscopy data for hydrous sodium trisilicate and rhyolite.