Grain refinement is an important possibility to enhance the weldability of aluminium weld metal that is usually defined by its susceptibility to solidification cracking. In this study, grain refinement was achieved through the addition of commercial grain refiner containing titanium and boron to the GTA weld metal of aluminium alloy 6082. The weld metal mean grain size could be reduced significantly from about 70 µm to a saturated size of 21 µm with a change in grain shape from columnar to equiaxed. The grain refinement prevented the formation of centreline solidification cracking that was present only in welds with unrefined grain structure. A variation of torch speed led to a strong change of solidification parameters such as cooling rate that was measured in the weld metal and the corresponding solidification rate and thermal gradient. The ratio thermal gradient/growth rate (G/R) decreased from 50 K s/mm² (high torch speed) to 10 K s/mm² (low torch speed). However, the variation of torch speed did not change the tendency for solidification cracking. The microstructure of unrefined and completely refined weld metal was compared. The observed change in size and distribution of the interdendritic phases was related to the change in susceptibility to solidification cracking.
The occurrence of solidification cracking during welding remains a little understood phenomenon, in spite of extensive studies and tests performed to evaluate and compare the relative weldability of many different alloys. From an approach often adopted in the welding community attributed to Prokhorov, solidification cracks are believed to form when a critical tensile strain is exceeded, specific to the alloy, assuming that the mushy-zone has limited ductility. Tensile stresses and strains normally form behind a moving weld pool as a result of solidification shrinkage and thermal contraction, as influenced by welding parameters and the degree of restraint.
In the present work, mechanisms are proposed for solidification crack initiation and growth in aluminum alloy 6060 arc welds. Calculations for an interdendritic liquid pressure drop, made using the Rappaz-Drezet-Gremaud (RDG) model, demonstrate that cavitation as a liquid fracture mechanism is not likely to occur except at elevated levels of hydrogen content. Instead, a porosity-based crack initiation model has been developed based upon pore stability criteria, assuming that gas pores expand from pre-existing nuclei. Crack initiation is taken to occur when stable pores form within the coherent dendrite region, depending upon hydrogen content. Following initiation, crack growth is modeled using a mass balance approach, controlled by local strain rate conditions. The critical grain boundary liquid deformation rate needed for solidification crack growth has been determined for a weld made with a 16 pct 4043 filler addition, based upon the local strain rate measurement and a simplified strain rate partitioning model. Combined models show that hydrogen and strain rate control crack initiation and growth, respectively. A hypothetical hydrogen strain rate map is presented, defining conceptually the combined conditions needed for cracking and porosity.
Weld metal microstructure for alloy 6060 aluminum welds, made using the gas-tungsten arc process and alloy 4043 filler metal, has been characterized using optical metallography, EPMA microprobe analysis, SEM/EBSD and STEM/EDX electron microscopy, and single-sensor differential thermal analysis (SS-DTA). In addition, alloy 6060 castings were solidified at variable cooling rates approaching that of welding, to provide a reference for comparison with weld microstructure. It was found that a major change in cast microstructure occurs at cooling rates higher than 27 K/s resulting in a structure similar to that observed in weld metal. Rapid cooling is believed to favor low temperature solidification reactions that normally would be achieved only at higher silicon content. Accordingly, additions of 4043 filler metal that increase the weld metal silicon content have only limited affect on weld solidification range and microstructure. This has direct implications regarding how 4043 filler additions improve weldability and weld quality.
Influence of variable polarity pulsed current technique on grain refinement of AZ31 weldments
(2009)
AZ31 Mg alloy sheet was welded using a gas-tungsten arc (GTA) process over inserts containing 2.3-9.3 wt.% Al. The welded specimens were susceptible to SCC in distilled water, with susceptibility increasing with decreasing weld metal Al (or β particle) concentration. Primary stress corrosion cracks initiated at the weld metal-HAZ interface by stress-assisted localised dissolution and propagated through the weld and base metals by transgranular and intergranular H-assisted fracture (TG-HAF and IG-HAF) respectively. The IG fracture mode may be intrinsic to the texture imparted upon the base metal by rolling. The increase in SCC susceptibility with decreasing weld metal Al concentration is contrary to the purported roles of β particles in promoting localised corrosion and as crack nucleation sites, but corresponds with increases in weld - base metal galvanic current density and weld metal localised corrosion susceptibility.
Earlier work has established that a critical amount of 4043 filler is required to avoid solidification cracking when arc-welding 6060 aluminium, depending upon local strain conditions. For example, when the mushy zone behind the weld pool experiences a tensile strain from combined thermal and shrinkage stresses, the possibility exists for crack initiation. For a greater rate of strain, it has been determined that a greater 4043 dilution (i.e. higher weld metal silicon content) is required to avoid crack initiation. Making use of the Controlled Tensile Weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and no-crack conditions for different local strain rates and filler dilutions, holding all other welding parameters constant. Using this established boundary as a line of reference, additional parameters have now been examined and their influence on cracking has been characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl3 + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of a critical strain rate required to initiate cracking for a given 4043 filler dilution.