Filtern
Dokumenttyp
- Vortrag (10) (entfernen)
Sprache
- Englisch (10)
Referierte Publikation
- nein (10)
Schlagworte
- Tomography (10) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (8)
- 8.5 Röntgenbildgebung (7)
- 3 Gefahrgutumschließungen; Energiespeicher (2)
- 6 Materialchemie (2)
- 8.0 Abteilungsleitung und andere (2)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 3.6 Elektrochemische Energiematerialien (1)
- 4 Material und Umwelt (1)
- 4.5 Kunst- und Kulturgutanalyse (1)
- 5 Werkstofftechnik (1)
Eingeladener Vortrag
- nein (10)
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel.
The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 μm.
In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed
at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in
Garching.
Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the Bundesanstalt für Materialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography with submicron resolution at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well.
In this work, metal organic frameworks (MOFs) embedded in polymer are characterized using differential tomography. MOFs are microporous structures of metal ions, coordinated by organic linker molecules, that can be used in a broad field of applications, especially in gas storage and catalysis. In this work, polymer embedded MOFs were extruded into filaments, which could be used for 3d-printing to profit from the specific properties of the MOFs in polymeric materials combined with the arbitrary shapes provided by 3d-printing. For the extrusion, different polymer classes like ABS, polyester- and polyetherurethanes, as well as different MOFs (ZIF-8, ZIF-67, HKUST-1) were used to create MOF containing filaments with a nominal diameter of 3.0 mm. Differential tomography at the edges of the Zn, Co, and Cu was then used to find the distribution of the corresponding MOF in the filament and to analyze the shape of the inclusions.
The combination of microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on porous material properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of porosity in ceramics.
Moreover, I will show how not-so-novel 2D characterization techniques, based X-ray refraction, can allow a great deal of insights in the damage evolution in microcracked (and porous) ceramics. I will show how X-ray refraction can detect objects (e.g. microcracks) below its own spatial resolution.
Finally, I will discuss the link between the microstructural findings and the mechanical properties of porous microcracked ceramics.
Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the BundesanstaltfürMaterialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well.
In this work, the absorption edge tomography is employed to perform a non-destructive, three-dimensional characterization of the microstructure of metallic alloys. As an example, a high strength Mg-Y-Zn alloy containing long period stacking ordered (LPSO) phases is analysed. The alloy with a nominal composition of Mg97Y2Zn1 was synthesized by melting highly pure magnesium, zinc and a Mg-22%Y master alloy and casting an ingot, which was homogenised at 350 °C and then extruded using an extrusion ratio of 18:1.
The results demonstrate that synchrotron based absorption edge tomography is a promising technique to perform a 3D characterization of the microstructure of metallic alloys.
Hundreds of papyrus rolls, carbonized during the 79CE eruption of Mount Vesuvius, were discovered in 1754 at Herculaneum. Sophisticated mechanical methods for unrolling the best-preserved scrolls have been applied, with varying success. However, such processes have been abandoned, to prevent risk from irremediable damage or loss and to preserve the integrity of the extremely fragile rolls. Following the development of X-ray based non-invasive techniques, attempts to virtually unroll the scrolls were made. The most common ink in Antiquity was carbon-based, and the main element of carbonized papyrus is carbon, making these investigations difficult. However, some attempts with synchrotron X-ray phase-contrast tomography (XPCT) were successful. Recently, the identification of antique inks containing metals raised hope that if some of the inks contain metal the rolls can be virtually unrolled using conventional CT- technique. We are presenting here the first results of a preliminary analysis, which aimed at identifying scrolls whose ink contains metals.
After a general presentation of the beamline, specifically the workflow for ex-situ CT at BAMline is presented. Although being used in a broad variety of research fields the usual workflow for CT experiments is in most cases similar in terms of sample mounting, tomographic scan and reconstruction. Specific scanning schemes allow for a preview reconstruction carried out during the scan. A detailed description of the used hardware as well as the self-coded programs applied in the data pipeline will be given. This will be accompanied by a practical demonstration of the software involved in the entire process.
After a general presentation of the beamline, specifically the workflow for ex-situ CT at BAMline is presented. Although being used in a broad variety of research fields the usual workflow for CT experiments is in most cases similar in terms of sample mounting, tomographic scan and reconstruction. Specific scanning schemes allow for a preview reconstruction carried out during the scan. A detailed description of the used hardware as well as the self-coded programs applied in the data pipeline will be given. This will be accompanied by a practical demonstration of the software involved in the entire process.
Nuclear magnetic resonance (NMR) with focus on 1H protons is increasingly applied for non-destructive testing applications. Besides mobile NMR, laboratory devices such as the NMR core-analyzing tomograph are used. As their magnetic field is more homogeneous, they enable measurements with higher signal-to-noise ratios (SNR), but with limited sample sizes. The tomograph presented here (8.9 MHz) was constructed for a maximum sample diameter of 70 mm and length of up to 1 m. The resolution, the echo time (min. 50 µs), the SNR and the measurement type can be adjusted by means of exchangable coils. The tomograph enables measurements along the complete sensitive length, slice-selective and even 2- or 3-dimensional measurements. A movable sample lifting system thereby allows a precise positioning of the sample.
The development of more powerful and more efficient lithium-ion batteries (LIBs) is a key area in battery research, aiming to support the ever-increasing demand for energy storage systems. To better understand the causes and mechanisms of degradation, and thus the diminishing cycling performance and lifetime often observed in LIBs, in operando techniques are essential, because battery chemistry can be monitored non-invasively, in real time. Moreover, there is increasing interest in developing new battery chemistries. Beyond LIBs, sodium ion batteries (NIBs) have gained increasing interest in recent years, as they are a promising candidate to complement LIBs, owing to their improved sustainability and lower cost, while still maintaining high energy density.[1] Initial phases of NIB commercialisation have occurred in the past year. However, for the widespread commercialisation of NIBs, there are still challenges that need to be overcome in developing optimized electrode materials and electrolytes. For the development of such materials and greater understanding of sodium storage mechanisms, solid electrolyte interface (SEI) formation and stability, and degradation processes, in operando methodologies are crucial.
Among the techniques available for in operando analysis, nuclear magnetic resonance spectroscopy (NMR) and imaging (MRI) are becoming increasingly used to characterize the chemical composition of battery materials, study the growth and distribution of dendrites, and investigate battery storage and degradation mechanisms. In situ and in operando 1H, 7Li and 23Na NMR and MRI have recently been used to study LIBs and NIBs, identifying chemical changes in Li and Na species respectively, in metallic, quasimetallic and electrolytic environment as well as directly and indirectly studying dendrite formation in both systems.[2-4] The ability of NMR and MRI to probe battery systems across multiple environments can further be complemented by the enhanced spatial resolution of micro-computed X-ray tomography (μ-CT) which can provide insight into battery material microstructure and defect distribution.
Here, we report in operando 1H and 7Li NMR and MRI experiments that investigate LIB performance, and the identification of changes in the Li signal during charge cycling, as well as the observation of signals in both 1H and 7Li NMR spectra that we attribute to diminishing battery performance, capacity loss and degradation. Additionally, recent operando methodology are adapted and implemented to study Sn based anodes in NIBs. 23Na spectroscopy is performed to monitor the formation and evolution of peaks assigned to stages of Na insertion into Sn, while 1H MRI is used to indirectly visualize the volume expansion of Sn anodes during charge cycling. Battery operation and degradation is further explored in these NIBs, using μ-CT, where the anode is directly visualized to a higher resolution and the loss of electrolyte in the cell, during cycling is observed
The BAMline at the synchrotron X-ray source BESSY II (Berlin, Germany) is supporting researchers especially in materials science. As a non-destructive characterization method, synchrotron X-ray imaging, especially tomography with hard X-Rays, plays an important role in structural 3D characterization. The imaging capabilities allow for in-situ and operando experiments. In this presentation the equipment, data handling pipeline as well as various examples from material science are presented.