Dripping and melt flow of the pyrolysing polymer melt can be both a benefit and a detriment during a fire. Well-adjusted melt flow and dripping are regularly beneficial to pass small-scale fire tests. Flame retardants often significantly change the melt viscosity of polymeric materials. The influence of certain flame retardants on the dripping behaviour of four commercial polymers is analysed based on experimental monitoring of the mass loss due to dripping, drop size and drop temperature as a function of the furnace temperature applied to a rod-shaped specimen. Investigating the thermal transition, thermal and thermo-oxidative decomposition, as well as the viscosity of the polymer and collected drops accomplish the work and connects dripping and melt flow with physical and chemical processes. Various flame retardant mechanisms affect the dripping behaviour in the UL 94 test. A changed viscosity and reduction in decomposition temperature also play a major role.
In North America certain hazardous materials are transported in rail tank cars that must be able to survive an engulfing liquid hydrocarbon pool fire for 100 minutes without rupture. To meet this requirement these tanks are normally equipped with pressure relief valves (PRV) and some form of thermal insulation or thermal protection (TP).
These tanks sometimes have non-accident releases (NAR) due to unwanted activation of, or leakage from the pressure relief valves (PRV). These NARs are a nuisance for Industry and for this reason, the industry now wants to remove the PRVs from certain tanks. This is known as total containment and is common practice in Europe. However, Europe does not have a 100 minute fire survival requirement. This paper is about a series of fire tests of 1/3 rd linear scale US DOT 111 Tanks cars. The 2.4 m3 vessels were subjected to fully engulfing fires generated by liquid propane fueled burners.
Carbon fibre (CF) and glass fibre (GF) reinforced polymers are used for diverse applications such as electronics/electrical engineering, transportation (railway vehicles, shipping, aviation) and construction. The fire behaviour of composites differs in comparison to polymers. Fibres behave often inert with respect to pyrolysis, but they change the melt flow and dripping behaviour, the heat absorption and transfer, the amount and properties of the fire residue and so on. Flame and fire retardancy concepts are needed not only suitable for the different fire protection goals typical for each application, but also tailored for composites. The field is illuminated by examples taken from different projects carried out in the group of the author in the recent years. The examples target on different applications through achieving V0 in UL 94 testing (reaction to small flame controlling the fire risks in the beginning of a fire), reducing heat release rate and fire load in the cone calorimeter (fire risks under forced flaming combusting controlling the contribution to developing fires) and investigating the fire stability when a severe flame is directly applied (key property in fully developed fires). Approaches to halogen-free flame retardancy in GF reinforced thermoplastics and CF reinforced thermosets are presented as well as building up a bench and intermediate scale testing of composites in fire applying mechanical load and direct flame exposure simultaneously.
The understanding of fire behaviour and flame retardancy mode of actions in composites is a promising basis for target-oriented development. The role of flame inhibition, charring and protective layer formation is discussed in composites. Successful concepts are presented for flame retardancy tailored for different application as well as general guidelines for future development. Different phosphorus flame retardants are proposed to achieve halogen-free flame retardancy in applications demanding limited fire risks with respect to ignition and developing fires. Different protective approaches are sketched for addressing the fire resistance of composite that is the most important fire risk for structural applications.
This presentation focusses on the thermal test of a typical storage container design for the German final storage repository KONRAD. The preparation of the container, the conduction of the fire test itself and results like the temperature evolution and as-sumptions for thermal material properties are shown.
As thermal test final storage containers have to be exposed to a fire of 800 °C (1472 °F) for 1 hour according to the final storage conditions provided by the federal com-pany for radioactive waste disposal (BGE). The here discussed cask contains a steel covered concrete layer of a thickness of 100/150 mm. Heating up concrete is a highly nonlinear process since the vaporization of residual water consumes high amounts of thermal energy and produce vast amounts of steam.
The constantly measured temperatures provide the basis to adjust common models of thermal properties for concrete esp. for FEAs. Finally in a later step this will allow predictions of similar designed container with different sizes.
Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m³ was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed.
The presentation gives an overview of actual research adtivities in the field of flame retardant polymers. Details are selected illuminating the scientific topic beyond the state of the art. Different concepts are illustrated with own results obtained in different Research projects over the last 15 years.
In order to investigate the heat fluxes over a wide range of surface temperatures during a propane gas fire test and to get information about local fire impact a fire reference package, representing the outer geometry of a specific type of transport cask for radioactive waste, was designed. A closed steel sheet cylinder with a wall thickness of 10 mm was chosen as fire reference package. The cylinder was filled with refractory insulation material and instrumented with thermocouples distributed all over the cylinder. The local steel sheet temperatures measured allow the determination of local as well as global heat fluxes as a function of time and surface temperature.
With this fire reference package three open-air propane gas fire tests were performed at BAM’s open air fire test stand. The flame exposure time period was changed for the different fire tests. Furthermore, the wind conditions changed between and during the tests. Test stand parameters like wind shield location and propane gas volume flow were chosen constant for the three tests. The test results were used to determine the changes of heat flux into the fire reference package in relation to the package surface temperature. This data also allows the calculation of local characteristics of the propane gas fire as there are the flame temperature, the fire convection coefficient and the radiation exchange coefficient in a first approach. The recently conducted tests provide an initial picture of local fire characteristics of the propane gas fire test facility. The test shows that the propane gas fire covers the IAEA-fire over a wide range of surface temperatures with the chosen test stand parameters.