Additive manufacturing (AM) processes enable the efficient production of advanced constructions. Direct energy deposition processes such as wire and arc-based additive manufacturing (DED-arc) are important methods. The wire filler metals enable a wide range of materials. In addition, the arc process provides a high deposition rate compared to laser and powder-based processes. Furthermore, components can be manufactured near-net-shape, offering significant savings in cost, time, and resources. Combined with the use of high-strength steels to reduce wall or component thicknesses in the context of lightweight design, great opportunities for saving energy and resources can be achieved. In a joint project of BAM and Chemnitz University of Technology, the main influences and complex interactions of material, production process, design and processing steps on the residual stress level are investigated. The aim is to develop processing recommendations and a cold cracking test for economical processing and stress-related design of high-strength steels with DED-arc. This study focuses on residual stress analysis by neutron diffraction (ND) and X-ray diffraction (XRD) on defined test specimens. The ND analysis were performed at the Paul Scherrer Institute (PSI) and the XRD analysis at BAM. The study shows a quantitative and qualitative comparison of the residual stress magnitudes and distribution between the component bulk (ND) and surface (XRD) analyses. The ND analysis reveals that in DED-arc AM walls the residual stresses dominate in the direction of welding and are negligibly small in each case transverse to the direction of welding. The topology of the analyzed residual stresses shows almost identical residual stress maps. In addition, the residual stresses are significantly influenced by the solid phase transformation of the material due to low cooling times in the area of the top layer.
High-strength steels offer great potential in weight-optimised modern steel structures. Additive manufacturing processes, such as Wire Arc Additive Manufacturing (WAAM), enable near-net-shape manufacturing of complex structures and more efficient manufacturing, offering significant savings in costs, time, and resources. Suitable filler materials for WAAM are already commercially available. However, the lack of knowledge or technical guidelines regarding welding residual stresses during manufacturing and operation in connection with cold cracking risk limit their industrial application significantly. In a project of BAM and TU Chemnitz, the influences and complex interactions of material, manufacturing process, design and processing steps on residual stress evolution are investigated. By developing process recommendations and a special cold cracking test, economic manufacturing, and stress-appropriate design of high-strength steel WAAM components are main objectives.
The present study focuses on determining the influence of heat control (interpass temperature, heat input, cooling time) and the design aspects of the components on the hardness and residual stresses, which are analysed by X-ray diffraction. Defined reference specimens, i.e., hollow cuboids, are automatically welded with a special WAAM solid wire. The influences of wall length, wall thickness and wall height on the residual stresses are analysed. Geometric properties can be selectively adjusted by wire feed and welding speed but cannot be varied arbitrarily. This was addressed by adapted build-up strategies. The results indicate a significant influence of the heat control and the wall height on the residual stresses. The interpass temperature, wall thickness and wall length are not significant. These analyses allow recommendations for standards and manufacturing guidelines, enabling a safe and economic manufacturing of high-strength steel components.
Influence of machining on residual stresses in additive manufactured high-strength steel components
(2024)
This study focuses on the effect of machining on the residual stresses and distortion of WAAM specimens. Defined specimens were welded fully automatically with a special WAAM solid wire (yield strength >820 MPa) with different geometric designs. The residual stresses state before and after cutting of the AM structure from the substrate plate were analyzed by means of X-ray diffraction on the specimen surface and complementary by 3d deformation analyses using photogrammetry. The results reveal significant influences of the geometry on the relaxation and redistribution of residual stresses.
Diese Studie konzentriert sich auf den Einfluss der Bearbeitung auf die Eigenspannungen und den Verzug von WAAM-Proben. Definierte Proben wurden vollautomatisch mit einem speziellen WAAM-Massivdraht (Streckgrenze >820 MPa) mit unterschiedlichen geometrischen Designs geschweißt. Der Eigenspannungszustand vor und nach dem Abtrennen der AM-Struktur von der Substratplatte wurde mittels Röntgenbeugung an der Probenoberfläche analysiert und durch 3D-Verformungsanalysen mittels Photogrammetrie ergänzt. Die Ergebnisse zeigen einen signifikanten Einfluss der Geometrie auf die Relaxation und Umverteilung der Eigenspannungen.