Damage tolerance counts as one of the most widespread approach to fatigue assessment and surely as one of the most promising in understanding the process-structure-property-performance relationships in additively manufactured metallic materials. Manufacturing defects, surface roughness, microstructural features, short and long crack fatigue propagation, residual stresses and applied loads can be taken into consideration in a fracture mechanics-based fatigue assessment. Many aspects are crucial to the reliable component life prediction. Among those a prominent role is played by an accurate measurement and modelling of the short crack fatigue behavior, and reliable statistical characterization of defects and residual stresses.
This work aims at addressing the issues related to both experimental testing, fatigue and fatigue crack propagation, and fracture mechanics-based modelling of fatigue lives. Examples will be provided on an additively manufactured AISI 316 L.
An unusual microstructure, inherent residual stresses and void formation are the three key aspects to control when assessing metallic parts made by LPBF. This talk explains an experiment to unravel the interlinked influence of the two mechanisms for the formation of residual stresses in LPBF: the temperature gradient mechanism and constricted solidification shrinkage. The impact of each mechanism on the shape and magnitudes of the residual stress distribution is described. Combined results from neutron diffraction, X-ray diffraction, computed tomography and in-situ thermography are presented.
Also, influence of scan strategies as well as surface roughness of subjacent layers on void formation is shown. Results from computed tomography and in-situ thermography of a specimen dedicated to study the interaction of the melt pool with layers of powder underneath the currently illuminated surface are presented.