Scanning Electron Microscopy (SEM) represents the mostly widespread method available in analytical laboratories dedicated to the characterization of physical properties such as morphology of various solid materials from ‘micro-’ down to the nanometre scale. The use of secondary electrons excited by a sharply, nm-focussed primary electron beam enables at any modern SEM to image objects with high in-depth and lateral sensitivity, i.e. with high spatial resolution. Hence, e. g. nanoparticles (NPs) are able to be easily characterized with respect to their individual size and shape, but also to the morphology of their surface.
By preparing the nano-objects on thin membranes as electron transparent samples it is possible to perform electron microscopy in the transmission mode (TEM and TSEM). The corresponding transmission (i.e. mass-thickness) contrast reveals in-depth information, but is also well suited for dimensional measurements in the 2D projection image. Both the surface sensitive mode and the transmission one are meanwhile available at any modern SEM. If an X-ray spectrometer is attached to an electron microscope, it is possible to analyse the characteristic X-rays induced by electron bombardment. Most electron microscopes have attached an energy dispersive X-ray spectrometer (EDX) so that EDX elemental maps can be carried out. Recent technological developments of high throughput EDS detectors and their advantages regarding high-resolution X-ray analysis down to the nm range are reviewed.
High-resolution micrographs (SEM, TSEM, TEM) and corresponding X-ray elemental maps on various representative nanoparticles, but also layered samples prepared in cross-section, will be presented and discussed. The importance of selecting the best suited analysis conditions will be highlighted. Also other, often challenging, topics such as sample preparation and image data processing will be critically addressed by practical examples. Further analytical techniques able to be employed at an electron microscope, like cathodoluminescence (CL) or micro-X-ray fluorescence (µXRF) will be briefly surveyed.
The physico-chemical characteristics of TiO2 coatings can greatly influence their final performance. In SETNanoMetro, different deposition procedures are being set for applying films of TiO2 NPs with defined and homogenous thickness on supports of interest for the applications studied in the project. The selected substrates are the following: (i) Silica glasses for photocatalytic measurements, (ii) Ti-alloys for orthopedic and/or dental prostheses, and for cell cultures, and (iii) Conductive glasses (e.g. Fluorine doped Tin Oxide, FTO) for dye-sensitized solar cells. From the different film deposition procedures studied within the project Self-assembly of TiO2 NPs in multiple layers was selected. For this, surface modification of the substrate and of TiO2 nanoparticles (NPs) with e.g. silane coupling agents is a prerequisite. First attempts to prepare the self-assembled coating on the functionalized glass substrates seem to indicate that the functionalized NPs adhere to the substrates, even if the final coatings were not homogenous and presented agglomerates. ToF-SIMS results support this outcome.
In order to use the layer-by-layer deposition technique for the formation of TiO2 films by controlled self-assembly of the TiO2 NPs, the proper complementary moieties for the functionalization of the NPs were chosen. A first set of NPs has been produced by reaction with (3-aminopropyl)phosphonic acid (APPA) in order to functionalize the surface with free amino-groups. Then, the complementary NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. A proper approach for the functionalization of two types of TiO2, commercial P25 (Evonik) and SETNanoMetro-sample labelled UT001, with APPA was developed. A second set of NPs consisting of three types of TiO2 NPs, P25 and SETNanoMetro NPs (TiO2 NPs with high specific surface area > 150 m2/g and TiO2 NPs with low size < 20 nm) was functionalized with (3-aminopropyl)triethoxysilane (APTS). As for the previous set of NPs, the complementary NP set was obtained through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. EDX, AES and ToF-SIMS spectra were collected and analyzed to demonstrate the presence of the surface functionalization of the different types of TiO2 NPs.
X-ray absorption fine structure (XAFS) spectroscopy is a powerful and widely used tool for material characterization. It is non-destructive, element-sensitive and requires no long-range order of the sample, making it suitable for the investigation of amorphous phases. XAFS includes the X-ray absorption near edge structure (XANES) and the extended X-ray absorption fine structure (EXAFS), providing information about the electronical state of the absorbing atom and the spatial order of the neighboring atoms respectively.
Our new approach presented here is derived from the classical dispersive XAFS setup. The aim is to have a scanningless, stable and reproducible setup for applications, in which dynamic processes occur in the second time scale.
A broad polychromatic beam passes through the sample and is dispersed afterwards by a convexly bent Si (111) crystal. All energies are reflected under different angles and thus spatially separated, allowing a position sensitive detector to record a spectrum over the energy range of the incoming beam in a single shot.
Tests of this setup were performed at the BAMline @ BESSY-II (Berlin, Germany) with different metal foils. First in situ measurements comprised the investigation of the early stages of the zinc(II)2-methylimidazolate (ZIF-8) crystallization. This topic of metal-organic-frameworks (MOF) research is of interest for medical applications. Structural changes with a time resolution of 1 s could be followed. The second dimension of the broad beam can be used for a lateral resolution.
Newly developed methodical approaches with an emphasis on correlative imaging analysis of morphology and chemistry of nanomaterials will be presented. Correlative imaging by high-resolution SEM with STEM-in-SEM as well as with EDS, and further with AFM, or with the new technique TKD (Transmission Kikuchi Diffraction) will be explained on various examples of nanostructures, both as starting materials and as embedded/functionalized nanoparticles in products. The unique analytical benefits of the Auger electron probe as a veritable nano-tool for the local surface chemistry will be highlighted. Examples of hybrid analysis of the bulk of nanomaterials by X-ray Spectroscopy and the highest surface-sensitive methods XPS and ToF-SIMS as advanced surface characterization methods available in the Competence Centre nano@BAM will be showed. Particularly for the spatially resolved analysis of the chemistry of nanostructures, such in-depth and lateral gradients of chemistry within mesoporous thin layers, or the completeness of the shells of core-shell nanoparticles, the latter methods are inherent.
Other dedicated developments like approaches for the quantitative determination of the porosity of thin mesoporous layers by electron probe microanalysis (EPMA) with SEM or the quantitative determination of the roughness of particle surface by high-resolution imaging with electron microscopy will be also presented.