Industrial quality control (QC) nowadays requires the visualization of surface modifications from the macro-scopic to the microscopic or even nanoscopic scale. This is a prerequisite to the evaluation of functionality and reliability, the detection of defects and their separation of artefacts. The diversity of applications ranges from low-E glazings and solar panels, micro- and optoelectronics, micro- and smart devices to sensor-on-chip and lab-on-chip systems [1]. Optical microcopy (light, confocal laser scanning, white light interference) as established QC-tool is operated at normal incidence, i.e. p- and s-polarization are undistinguishable. Either light-intensity in terms of grey scale and colour or intensity-correlated effects of phase shifts are used. In case of ellipsometry, operated at oblique incidence, p- and s-polarization matter, and amplitude ratios and phase shifts upon reflection are measured. Hence, information content must be much higher.
The visualization of surface modifications may be very challenging for coating/substrate systems of either al-most identical optical constants, e.g. transparent films on substrates of the same material, or minor film thick-ness, substance quantity and affected area, e.g. ultra-thin or island films. Ellipsometry gives access to the con-trast of intensity (I), amplitude ratio (Ψ), and phase shift (Δ) with nanometer-scaled vertical and micrometer-scaled lateral sensitivity, one is able to identify tiny changes within an unmodified surface. As both mapping ellipsometry (ME) and imaging ellipsometry (IE) are operated in the optical far-field, surface inspection is also possible on the macroscopic scale. Near the Brewster-angle of the bare, undamaged, clean, and fresh substrate, the contrast to add-on and sub-off features is superior.
Fig. 1 shows three examples of ellipsometric imaging, i.e. a thin SnO:Ni film on SiO2/Si (Fig. 1a), a dried stain of an anti-body solution on cyclo-olefin-polymer (COP) shown in Fig. 1b, and a polyimide film residue on SiO2/Si (Fig. 1c). For all of these examples, ellipsometry provides much better contrast between substrate and surface modification than optical microscopy, sometimes primarily caused by the oblique incidence (Figs. 1a and 1c), in other cases related to the phase sensitivity of ellipsometry (Fig. 1b). Other examples are laser surface modifications and the corrosion of glass. In these cases, optical microscopy and IE yield to similar results, how-ever only ellipsometry gives access to modelling.
Further investigated coating/substrate systems are 100Cr6 steel, native oxide on silicon, borosilicate glass, and the polymer polycarbonate with deposited films of graphene and ta-C:H, printed and dried pattern of liquids such as water, cleaning agents, and dissolved silicone. Besides imaging ellipsometry, referenced spectral ellipsometry (RSE) has been applied, combining the advantages of both optical microscopy (fast measurement) and ellipsometry (high sensitivity to tiny modifications).
Scanning Electron Microscopy (SEM) represents the mostly widespread method available in analytical laboratories dedicated to the characterization of physical properties such as morphology of various solid materials from ‘micro-’ down to the nanometre scale. The use of secondary electrons excited by a sharply, nm-focussed primary electron beam enables at any modern SEM to image objects with high in-depth and lateral sensitivity, i.e. with high spatial resolution. Hence, e. g. nanoparticles (NPs) are able to be easily characterized with respect to their individual size and shape, but also to the morphology of their surface.
By preparing the nano-objects on thin membranes as electron transparent samples it is possible to perform electron microscopy in the transmission mode (TEM and TSEM). The corresponding transmission (i.e. mass-thickness) contrast reveals in-depth information, but is also well suited for dimensional measurements in the 2D projection image. Both the surface sensitive mode and the transmission one are meanwhile available at any modern SEM. If an X-ray spectrometer is attached to an electron microscope, it is possible to analyse the characteristic X-rays induced by electron bombardment. Most electron microscopes have attached an energy dispersive X-ray spectrometer (EDX) so that EDX elemental maps can be carried out. Recent technological developments of high throughput EDS detectors and their advantages regarding high-resolution X-ray analysis down to the nm range are reviewed.
High-resolution micrographs (SEM, TSEM, TEM) and corresponding X-ray elemental maps on various representative nanoparticles, but also layered samples prepared in cross-section, will be presented and discussed. The importance of selecting the best suited analysis conditions will be highlighted. Also other, often challenging, topics such as sample preparation and image data processing will be critically addressed by practical examples. Further analytical techniques able to be employed at an electron microscope, like cathodoluminescence (CL) or micro-X-ray fluorescence (µXRF) will be briefly surveyed.
The physico-chemical characteristics of TiO2 coatings can greatly influence their final performance. In SETNanoMetro, different deposition procedures are being set for applying films of TiO2 NPs with defined and homogenous thickness on supports of interest for the applications studied in the project. The selected substrates are the following: (i) Silica glasses for photocatalytic measurements, (ii) Ti-alloys for orthopedic and/or dental prostheses, and for cell cultures, and (iii) Conductive glasses (e.g. Fluorine doped Tin Oxide, FTO) for dye-sensitized solar cells. From the different film deposition procedures studied within the project Self-assembly of TiO2 NPs in multiple layers was selected. For this, surface modification of the substrate and of TiO2 nanoparticles (NPs) with e.g. silane coupling agents is a prerequisite. First attempts to prepare the self-assembled coating on the functionalized glass substrates seem to indicate that the functionalized NPs adhere to the substrates, even if the final coatings were not homogenous and presented agglomerates. ToF-SIMS results support this outcome.
In order to use the layer-by-layer deposition technique for the formation of TiO2 films by controlled self-assembly of the TiO2 NPs, the proper complementary moieties for the functionalization of the NPs were chosen. A first set of NPs has been produced by reaction with (3-aminopropyl)phosphonic acid (APPA) in order to functionalize the surface with free amino-groups. Then, the complementary NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. A proper approach for the functionalization of two types of TiO2, commercial P25 (Evonik) and SETNanoMetro-sample labelled UT001, with APPA was developed. A second set of NPs consisting of three types of TiO2 NPs, P25 and SETNanoMetro NPs (TiO2 NPs with high specific surface area > 150 m2/g and TiO2 NPs with low size < 20 nm) was functionalized with (3-aminopropyl)triethoxysilane (APTS). As for the previous set of NPs, the complementary NP set was obtained through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. EDX, AES and ToF-SIMS spectra were collected and analyzed to demonstrate the presence of the surface functionalization of the different types of TiO2 NPs.
This talk presents multi-wavelength, multi-material prediction tools serving as useful models for researchers working in the field of laser-induced periodic surface structures (LIPSS). These models explain the role of surface plasmon polaritons (SPPs) in the formation of LIPSS. They particularly consider the cases of (i) “lossy” materials (where the imaginary part of the dielectric permittivity should not be neglected) and (ii) the excitation of SPPs in a thin film configuration (where two film interfaces become plasmonically active and couple to each other).
For many years now, the so-called three layer model (free-surface, bulk-like, and adsorbed layers) has been commonly used, along with other parameters, to explain the deviations seen in glass transition and glassy dynamics for polymers confined into thin films, compared to their bulk value. Nevertheless, due to the hard accessibility of the adsorbed layers in supported films, little is known about the nature of their dynamics and how they really influences the overall dynamics of the thin films. Here, the irreversibly self-assembled adsorbed layer of a low MW Poly (vinyl methyl ether) (PVME) is solvent-leached from a 200 nm film. The thickness and topography of this layer is checked with Atomic Force Microscopy (AFM), to insure no dewetting and low roughness. Further, the dynamics of the adsorbed layer is then in-situ probed with Broadband Dielectric Spectroscopy (BDS). A recently developed nano-structured capacitor arrangement was employed; where a silicon wafer with nanostructured SiO2 nano-spacers, with heights of 35 nm, is placed on top of a thin film spin coated on an ultra-flat highly conductive silicon wafer. All results will be discussed in detail and quantitatively compared to our recent work on the glassy dynamics of PVME thin films (50 nm- 7nm), where BDS measurements showed two thickness-independent relaxation processes. The first process was assigned to the -relaxation of a bulk-like layer. Whereas the second process showed a different temperature dependence and was ascribed to the relaxation of polymer segments adsorbed at the substrate. To our knowledge, this is the first in-situ study of the dynamics of an irreversibly adsorbed layer.
Loss in efficiency of perovskite solar cells may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDX combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDX
spectral maps on cross-sections of the specimen have been measured. The distribution of relevant
elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. By EDX it was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDX that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after two months of illumination.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge for modern analytical techniques and requires approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by spectroscopic ellipsometry (SE).
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films were prepared via dip-coating of a solution containing a triblock-copolymer as structure-directing agent, an iridium precursor as well as a titanium precursor in ethanol. Deposited films with different amounts of iridium (0 wt%Ir to 100 wt%Ir) were synthesized and calcined in air. The thin films were analyzed with SE using the Bruggeman effective medium approximation (BEMA) for modelling. The results were compared with electron probe microanalysis (EPMA) as part of a combined SEM/EDS/STRATAGem Analysis.
Polymers at interfaces play a major role in a broad variety of applications ranging from engineering purposes (for instance polymer based nanocomposites) to high tech implications (for instance light emitting diodes). Here the glass transition and glassy dynamics is considered for epoxy-based nanocomposite with Layered Double Hydroxide nanofiller and for thin films of a misicble polymer blend of PVME/PS with thicknesses down to 7 nm. The materials are investigated by spectroscopic techniques (broadband and specific heat spectroscopy), as well as by fast scanning calorimetry and small- and wide-angle X-ray scattering.
Both essential aspects of the surface of solid matter, its morphology and chemistry, are studied traditionally at BAM starting in the 60’s with different cyclical research focus areas, mostly related either to applicative research or method development. In the recent years, the focus has shifted almost exclusively to the nano-analytics of advanced materials such as complex nanoparticles, (ultra)thin films/coatings, nanocomposites, 2D materials, energy materials, etc. This is also the reason why BAM has established recently the new Competence Center nano@BAM (www.bam.de/Navigation/DE/Themen/Material/Nanotechnologie/sichere-nanomaterialien.html) with the five sub-fields nanoCharacterisation, nanoMaterial, nanoSafety, nanoData and nanoTechnology. The link to the BAM central guidelines to the safety in technology and chemistry is given by the development of reference products such as reference measurement procedures, reference (nano)materials, and newly reference data sets. Thus, an internationally well-networked group in surface analysis has been established @BAM, with regular contributions to integral analytical characterization with metrological and standardization background.
Examples of newly developed methodical approaches will be given with an emphasis on correlative nano-analysis of morphology and chemistry of nanomaterials. Correlative imaging by STEM-in-SEM with high-resolution SEM and EDX, and further with AFM or the new technique TKD (Transmission Kikuchi Diffraction) will be explained on various examples of nanostructures, both as starting materials and embedded/functionalized nanoparticles in products. The unique analytical benefits of the Auger electron probe as a veritable nano-tool for surface chemistry will be highlighted. The panoply of advanced surface characterization methods @BAM is completed by discussing examples of hybrid analysis of the bulk of nanomaterials by X-ray Spectroscopy with the highest surface-sensitive methods X-ray Photoelectron Spectroscopy (XPS) and Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS). Particularly for the analysis of the surface chemistry of nanostructures, such as the completeness of the shells of core-shell nanoparticles or in-depth and lateral gradients of chemistry within mesoporous thin layers, the latter methods are inherent.
Other special developments like approaches for the quantitative determination of the roughness of particle surface by electron microscopy or for the quantitative determination of the porosity of thin mesoporous layers by electron probe microanalysis (EPMA) with SEM will be presented.
The progress in the activities on Microbeam Analysis under VAMAS/TWA 37 is reviewed. Particularly the liaison with the new projects within the ISO technical committee TC 202 is presented and discussed with respect to the possibility of identifying and launching related VAMAS projects/inter-laboratory comparisons. The recently started project FIB sample processing for TEM is presented. Next projects in the pipeline involving EBSD and TKD are shortly announced. The need of more promotion for the engagement of more experts from industry and academia at national, European and international level is highlighted. Also, the competition with the other technical working areas (on 'nano' or materials-related) is critically discussed.