Atomic force microscopy based Infrared spectroscopy (AFM-IR) is a quickly evolving technique that provides chemical analysis and compositional mapping with spatial resolution far below conventional optical diffraction limits. This is possible since the detection method is based on a very sharp AFM tip which starts to oscillate when the sample starts to thermally expand (the changed is caused by the absorption of IR wavelength) where the thermal expansion is related to the IR absorption. This presentation briefly described the application of that new technique from polymer characterization and utilization of AFM-IR in material research, up to life science applications.
This work investigates the fire phenomena of rigid polyurethane foams (RPUF) in detail. To elucidate structure-property relationships systematically varied sets of foams were prepared. RPUF were synthesized with different densities using water and pentane as blowing agent. What is more, a flame retarded RPUF and rigid polyisocyanurate-polyurethane foams were examined. The comprehensive understanding of the processes taking place during combustion is the foundation of customized development of successful flame retardant approaches.
Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples in the inside of specimens give information about the temperature gradient and temperature of the pyrolysis zone during combustion. Furthermore, fire phenomena were characterized using SEM, LOI and thermal analysis. By using a multi-methodological approach and systematically varied sets of foam materials, new insights into the burning of RPUF were won. The detailed knowledge of fire phenomena is essential for future development of tailored flame retardant strategies for RPUF.
Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking
(2019)
The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials.
This paper is based mainly on the results of two different projects performed in the group of the author recently (2016-2019). The three external partners involved in these two projects are competent in the preparation of FPUF (ICL IP America), RPUF (Department of Industrial Engineering, Padova University), and TPU (Fraunhofer-Institut für Betriebsfestigkeit und Systemzuverlässigkeit LBF, Darmstadt) as well as for the specimen preparation. Systematically varied sets of materials were prepared as the key basic for scientific discussion, varying the kind and combination of flame retardant, PUR structure, density, and blowing agent.
A multimethodical approach based on thermogravimetry (TGA), TGA coupled with evolved gas analysis (TGA-FTIR) and pyrolysis GC-MS was used for investigating the pyrolysis. The flammability was addressed using oxygen index (OI) and testing in UL 94 burning chamber in vertical and horizontal set-up. The fire behaviour was addressed by using a cone calorimeter. Beyond these methods according to the state of the art, key experiments were performed. We addressed the dripping and the two-stage burning of TPU using a self-designed apparatus and specific data evaluation, the foam burning through quenching burning samples, using different special sample holders, and measuring temperature profiles within the burning foams. The investigation is made round by intensive analysis of the fire residues, such as comprehensive investigation of the morphology.
Result on the pyrolysis (TGA-FTIR, Pyrolysis-GC/MS), flammability (UL 94, LOI), and fire behaviour (cone calorimeter) of TPU and flame retardant TPUs are shown. We discuss in detail the characteristic of PUR decomposition: the low tendency to char, and the specific two step decomposition and how these characteristics control the regimes in fire behaviour. We demonstrate that the different burning regimes are controlled by different pyrolysis products and effective heat of combustions. The resulting formation of pool fires as well as the formation of dripping is discussed in detail. The latter quite important to understand the flame retardancy applied with respect to achieve the UL 94 classification V0 nondripping or V0 non-flaming dripping.
Rigid and flexible PUR foams and their flame retarded versions are investigated for different densities. Water and pentane-blown foams are compared as well as PUR and polyisocyanurate-polyurethane (PIR) foams. Horizontal testing in the cone calorimeter is used and the vertical foam specimen holder as well. Self-designed set-ups within the cone calorimeter enable a better inside in the pyrolysis front running through the foam samples as well as the development of the temperature gradient inside the foam during the fire test. The morphology change during burning was characterised by the means of quenching burning foams with liquid nitrogen and investigating the cross sections with scanning electron microscope. In sum, a rather comprehensive study was performed to work out the principle fire phenomena controlling the fire behaviour of PUR foams in a very systematic and significant way.
Promising flame retardancy approaches are discussed. The importance of either combining the drain of fuel and flame inhibition or charring into an effective protection layer/multicellular structure is underlined.
This contribution focusses the general conclusions and trends. It tries to increase the understanding of the specific and demanding challenge to develop flame retardant PUR materials.