Investigation of core-shell nanoparticles using scanning transmission x-ray microscopy (STXM)
(2017)
A scanning transmission x-ray microscopy (STXM) based methodology is introduced for determining the dimensions (shell thickness, core and total diameter) of core-shell nanoparticles which exhibit a strong x-ray absorption contrast and a well-defined interface between core and shell material. A low radiation dosage during data acquisition and, therefore, less x-ray beam induced damage of the sample is achieved by recording STXM images only at two predetermined energies of maximum absorption contrast, instead of recording a stack of images across the whole absorption edge. A model core-shell nanoparticle, polytetrafluoroethylene (PTFE) cores with polystyrene (PS) shell, is used for demonstration. Near edge x-ray absorption fine structure (NEXAFS) spectroscopy confirms the significant difference in x-ray absorption behavior between PTFE and PS. Additionally, due to the insolubility of styrene in PTFE a well-defined interface between particle core and shell is expected. In order to validate the STXM results, both the naked PTFE cores as well as the complete core-shell nanoparticles are examined by scanning electron microscopy (SEM). The introduced STXM based methodology yields particle dimensions in good agreement with the SEM results (deviation equal or less than 10%) and provides additional information such as the position of the particle core which cannot be extracted from a SEM micrograph.
Investigation of core-shell nanoparticles using scanning transmission x-ray microscopy (STXM)
(2018)
A scanning transmission x-ray microscopy (STXM) based methodology is introduced for determining the dimensions (shell thickness, core and total diameter) of core-shell nanoparticles which exhibit a strong x-ray absorption contrast and a well-defined interface between core and shell material. A low radiation dosage during data acquisition and, therefore, less x-ray beam induced damage of the sample is achieved by recording STXM images only at two predetermined energies of maximum absorption contrast, instead of recording a stack of images across the whole absorption edge. A model core-shell nanoparticle, polytetrafluoroethylene (PTFE) cores with polystyrene (PS) shell, is used for demonstration. Near edge x-ray absorption fine structure (NEXAFS) spectroscopy confirms the significant difference in x-ray absorption behavior between PTFE and PS. Additionally, due to the insolubility of styrene in PTFE a well-defined interface between particle core and shell is expected. In order to validate the STXM results, both the naked PTFE cores as well as the complete core-shell nanoparticles are examined by scanning electron microscopy (SEM). The introduced STXM based methodology yields particle dimensions in good agreement with the SEM results (deviation equal or less than 10%) and provides additional information such as the position of the particle core which cannot be extracted from a SEM micrograph.
A scanning transmission x-ray microscopy (STXM) based methodology is introduced for determining the dimensions (shell thickness, core and total diameter) of core-shell nanoparticles which exhibit a strong x-ray absorption contrast and a well-defined interface between core and shell material. A low radiation dosage during data acquisition and, therefore, less x-ray beam induced damage of the sample is achieved by recording STXM images only at two predetermined energies of maximum absorption contrast, instead of recording a stack of images across the whole absorption edge. A model core-shell nanoparticle, polytetrafluoroethylene (PTFE) cores with polystyrene (PS) shell, is used for demonstration. Near edge x-ray absorption fine structure (NEXAFS) spectroscopy confirms the significant difference in x-ray absorption behavior between PTFE and PS. Additionally, due to the insolubility of styrene in PTFE a well-defined interface between particle core and shell is expected. In order to validate the STXM results, both the naked PTFE cores as well as the complete core-shell nanoparticles are examined by scanning electron microscopy (SEM). The introduced STXM based methodology yields particle dimensions in agreement with the SEM results and provides additional information such as the position of the particle core which cannot be extracted from a SEM micrograph.
Mit dem stetigen weltweiten Anstieg der Nachfrage nach Polymerprodukten nimmt auch die potenzielle Menge an Kunststoffabfällen in der Umwelt zu. Problematisch ist, dass viele der wirtschaftlich relevantesten Kunststoffe sehr lange brauchen, um in der Umwelt abzubauen, sich dort akkumulieren und in kritisch betrachtetes Makro- und Mikroplastik zu zerfallen. Auf der Grundlage des Vorsorgeprinzips fordert die Europäische Kommission daher die Entwicklung neuer polymerer Materialien, die diesem Problem der Persistenz entgegenwirken und unter natürlichen Umweltbedingungen schneller abgebaut werden können. 1,2
Um dieses Problem anzusprechen, wurden mittels additiver Fertigung Polymerblends aus photooxidationsempfindlichem Polystyrol (PS) und hydrolyseempfindlicher Polymilchsäure (PLA) hergestellt. Die Hypothese war, dass sich die beiden Thermoplaste aufgrund ihrer unterschiedlichen Abbauprozesse gegenseitig in ihrem Abbau unterstützen, wenn sie unter moderaten, realitätsnahen Umweltalterungsbedingungen (45 °C) abwechselnd der Photooxidation und Hydrolyse ausgesetzt werden.
In der Praxis zeigten die Ergebnisse, dass die Degradation von PLA durch die Anwesenheit von PS deutlich beschleunigt worden ist – wohingegen die Degradation von PS gehemmt wurde. In diesem Vortrag werden die detaillierten Ergebnisse der Oberflächen- (ATR-FTIR, REM) und Bulk-Analysen (DSC, TGA, FTIR-Transmission, TED-GC/MS) der Blends sowie ergänzende Mikroplastik-Ergebnisse des umgebenden Wassermediums (TED-GC/MS) erörtert.