BAM is the federal institute for materials research and testing in Germany. One of our tasks is to evaluate the safety of casks designed for transport and/or storage of radioactive waste. As elastomeric seals are used in the containers as safety-relevant parts, it is our goal to be able to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. For this reason, an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) was started. Ageing was performed at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to 2 years. For assessing properties related to the sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates. For comparison, uncompressed O-rings were aged as well. The aged materials were characterized with conventional polymer analysis methods such as hardness and tensile tests, but also with more seal-specific methods such as compression stress relaxation (CSR, reflecting the loss of sealing force of a compressed seal over time), and compression set (CS, representing the recovery behaviour of a seal after release from compression). CS is chosen as the property for lifetime prediction as it is both sensitive to degradation and related to the seal performance. CS data is extrapolated to 60 °C, which yields lifetimes of approximately 5 years for HNBR and 64 years for EPDM for a criterion of 85 % CS respectively, and approx. 40 years for FKM for a criterion of 65 % CS (the highest value measured so far).
Characterisation of degradation and determination of end-of-lifetime criterion for O-ring seals
(2017)
The ageing of polymers, including elastomers, is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurence of critical failure is desired.
In order to investigate the degradation of material properties and to determine the lifetime of elastomers used as seals, an ageing programme was started with hydrogenated acrylonitrile butadiene rubber (HNBR), ethylene propylene diene rubber (EPDM) and fluorocarbon rubber (FKM) [1-3]. Both O-ring seals (uncompressed and compressed by 25 %) with a cord diameter of 10 mm as well as sheets with a thickness of 2 mm were aged at 75 °C, 100 °C, 125 °C and 150 °C for up to two years. The changes of material properties during ageing were characterised for each material using the sheets by means of e.g. dynamic-mechanical analysis and tensile tests, while sealing properties such as compression stress relaxation (CSR), compression set (CS) and leakage rate were determined on O-rings. The experimental results indicate that while material properties, CSR and CS show considerable degradation effects, the static leakage rate stays constant or even decreases before failure occurs quite suddenly at advanced degradation levels. This reveals that static leakage rate has only limited sensitivity for the degradation of the seal material.
Our approach to determine a suitable end of lifetime criterion, which involves a partial decompression of the seal during the leakage test, is presented and discussed.
Geogenic gases such as CH4 or CO2 from natural sources, gases (CCS-CO2, H2, Natural
gas, City gas …) from a geological repository, or a leaking gas pipeline can present serious
risks in industrial and urban areas where the density of infrastructural elements increases as
well as above and below ground. To extend the lead time for risk treatment in such critical
regions, reliable detection of gases within the shallow subsurface is required to observe
critical gas accumulations before degassing into the atmosphere.
A near real-time monitoring approach is introduced to determine the volumetric expansion of
such a gas escaping from a leak in the subsurface. Considering the pressure relaxation with
the ambient air pressure, the approach enables the forecasting of the final size of a
pressurized gas body in terms of characteristic lengths. According to theoretical basics, such
a characteristic length, which allows to perform a gas (safety) measurement based on a
purely geometrical measure, behaves independently of subsurface properties, i.e., it enables
a reliable quantification of the escaping gas, irrespective of its heterogeneous flow path
distribution. A field test for a 10 l/min pinhole leakage of CO2 injected in an unsaturated Chernozemic soil (agricultural test field Bad Lauchstädt)that was equipped with linear gas sensors demonstrates the lateral-vertical volumetric gas expansion along the environment of these gas sensors, and confirms the applicability of the new characteristic length approach.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore, it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal.
In this work, we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness or catastrophic seal failure of O-ring rubber seals. This is required as material properties of rubbers are strongly temperature dependent but their temperature application range is not always clearly defined.
Based on previous investigations which considered the physical material properties and the seal behaviour under purely static conditions we widen the focus on the sealing performance after a fast partial relief of compressed seals and additional materials.
For the investigations, different typical rubber seal materials were used as e.g. fluorocarbon (FKM), ethylene propylene diene (EPDM) and hydrogenated acrylonitrile-butadiene (HNBR) rubber.
The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the performance during/after fast partial relief of seals at low temperatures.
Due to their high versatility and recovery potential under several load conditions, seals made from elastomers are widely used as barrier seals in containers for low and intermediate level radioactive waste and as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). In DPC, elastomer seals allow leakage rate measurements of metal barrier seals for demonstration of their proper assembly conditions and performance.
For spent fuel and high level waste as well as for low and intermediate level waste, long time periods will be required before final disposal will be available. Therefore, the long-term behavior of elastomer seals can be an important issue when the cask’s suitability for an extended interim storage period has to be assessed.
During the licensed interim storage duration, the requested leakage rate has to be maintained under any static and dynamic load conditions. A sufficient resilience, the capability of seals to compensate a (rapid) partial release was identified as an important end-of-lifetime criterion.
In the framework of extensive aging and testing programs at BAM, specimen made from representative types of elastomer (EPDM, FKM) were aged for several years at different temperatures ranging from 23 °C to 150 °C. One aim of the experiments was to determine an end-of-lifetime criterion correlated to leakage as the point of seal failure. As the seals remained leak-tight under static conditions even after advanced material degradation, a more demanding leakage test set-up was constructed that allowed a rapid partial release of the seal. This device enables a release of the O-ring by approx. 0.2 mm from 25 % to 23 % compression in less than one second during the pressure rise measurement. If the resilience of the seal has decreased past a certain point, the seal cannot follow the decompression fast enough and a leak path can open. Using a finite element (FE) material model derived earlier from different material tests, this process was simulated with a 3D FE model, reproducing the essential characteristics of the test device.
The FE-model enables the analyzation of the occurring global mechanisms if a leak path opens. The capability of the seals to follow the lifted flange and the subsequent run of compression force depending on the current state of aging are illustrated. The findings of the simulation are correlated and discussed with respect to the pressure rise measurements.
The excellent mechanical properties of elastomer seals at a wide range of temperatures as well as their high versatility and recovery potential under several load conditions make these materials well suitable for the application in containers designed for transport and disposal of negligible heat generating radioactive waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered which prohibit an avoidable cask handling. An extensive knowledge of the change of the elastomer properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the safe enclosure of the radioactive material for the required time are mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have already been made and are still ongoing to scientifically support this task.
Among other representative types of elastomers, specimen made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the with respect to application most important of their complex mechanical properties.
Exemplary results of these investigations were used to calibrate material models implemented in the commercial finite element software ABAQUS/Standard®. The finite element model already presented in previous works uses a sequential temperature displacement coupling. The calculated compression stress relaxation (CSR) and compression set (CS) values do satisfactorily match the experimental results.
In many investigations performed at BAM both values (CSR and CS) were identified as key indicators of elastomer’s long-term performance.
However, the possibility to correlate these equivalent indicators with performance values such as tightness and leakage rate, measurable in the mounted state, is an important goal of our future work. In the presented study the ABAQUS® feature of “pressure penetration” is introduced in the suggested finite element model for this purpose. It provides the possibility to simulate the penetration of a gas into a possible gap between flange and O-ring causing an opening of a leakage path. Three dimensional and axis-symmetric finite element models were generated to represent flat and grooved flanges of different dimensions.
The sensitivity of the feature to several input parameters is investigated and the observed behavior of the O-ring is correlated with the results of performed leakage tests.
The subject of permeation of hoses according to ISO 3821 for
hydrogen was discussed for a long time in ISO/TC 44/SC 8. The reason
is a considerable leakage of hydrogen diffused into the hose material
over the end face of the hose. Because of this unsolved, safety-related
problem of hoses sold on the market, measurements should be carried
out in order to be able to better assess the problem. BAM has declared
its attendance to provide a required fast solution to this issue.