Damage tolerance counts as one of the most widespread approach to fatigue assessment and surely as one of the most promising in understanding the process-structure-property-performance relationships in additively manufactured metallic materials. Manufacturing defects, surface roughness, microstructural features, short and long crack fatigue propagation, residual stresses and applied loads can be taken into consideration in a fracture mechanics-based fatigue assessment. Many aspects are crucial to the reliable component life prediction. Among those a prominent role is played by an accurate measurement and modelling of the short crack fatigue behavior, and reliable statistical characterization of defects and residual stresses.
This work aims at addressing the issues related to both experimental testing, fatigue and fatigue crack propagation, and fracture mechanics-based modelling of fatigue lives. Examples will be provided on an additively manufactured AISI 316 L.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Understanding segregation to grain boundaries, and eventually their defect phase diagrams, is critical to enable rational grain boundary engineering for alloys design. Here, we discuss the progress and challenges one may face when generating such a database of defect-solute interactions, in the context of studying of grain boundary segregation of solutes and impurities in Fe GBs. To compute the large number of relevant defect-solute interactions we have performed high-throughput ab initio calculations using efficient and highly automated workflows using pyiron. We study has been performed across a representative set of coincident-site-lattice (CSL) type tilt GBs. Based on the large ab-initio datasets, we extract and analyse the chemical and structural trends observed in the solute segregation behaviour across the periodic table. The features which are most important in evaluating site segregation are presented and discussed.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. Recent experimental studies show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams in combination with density functional theory provide a natural route to study these chemically driven defects. Our results show, however, that direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation. Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe-Nb solid solutions and to identify in a joint study with experiments conditions in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, they can detect objects with size above a few wavelengths of the radiation.
Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads.
The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models.
We hereby show the application of non-destructive X-ray refraction radiography (SXRR, 2D mapping also called topography) to problems in additive manufacturing:
1) Porosity analysis in PBF-LM-Ti64. Through the use of SXRR, we could not only map the (very sparse) porosity distribution between the layers and quantify it, but also classify, and thereby separate, the filled porosity (unmolten powder) from the keyhole and gas pores (Figure 1).
2) In-situ heat treatment of laser powder bed fusion PBF-LM-AlSi10Mg to monitor microstructure and porosity evolution as a function of temperature (Figure 2). By means of SXRR we indirectly observed the initial eutectic Si network break down into larger particles as a function of increasing temperature. We also could detect the thermally induced porosity (TIP). Such changes in the Si-phase morphology upon heating is currently only possible using scanning electron microscopy, but with a much smaller field-of-view. SXRR also allows observing the growth of some individual pores, usually studied via X-ray computed tomography, but again on much smaller fields-of-view.
Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the defect distribution and the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.