Radiation induced attenuation in perfluorinated polymer optical fibres for dosimetry applications
(2016)
Real-time measurement of radiation-induced attenuation (RIA) in a commercial perfluorinated polymer optical fibre (PF-POF) is performed with regard to on-line radiation monitoring purposes. Spectral character and dose dependence of fibre’s RIA is measured in 450-900 nm spectral region. Fibre exhibited high radiation sensitivity in the visible region with strong increase towards the UV wavelengths. Good linearity and high sensitivity reaching up to 130 dBm-1/kGy was demonstrated in the VIS region for a low dose range. This of the shelf PF-POF could be therefore interesting for on-line remote dosimetry applications.
Impact of gamma radiation on transmission of a commercial Cytop polymer optical fibre (Lucina, Asahi Glass Company) is investigated. Spectral dependence of radiation induced attenuation in the investigated fibre is measured in the VIS-NIR spectral region. Besides attenuation increase, radiation is found to increase fibre susceptibility to water as well. While pristine Cytop fibre is rather humidity insensitive, strong humidity related absorption in the NIR region is observed after fibre irradiation. Selective irradiation of separate fibre sections is proposed as a way of fibre humidity sensitization and quasi-distributed water detection is demonstrated using optical time domain reflectometry at 1310 nm.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer.
Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.