The durability of concrete structures and its performance over the lifetime is strongly influenced by many interacting phenomena such as e.g. mechanical degradation due to fatigue loading, loss of prestress, degradation due to chemical reactions or creep and shrinkage. Failure due to cyclic loading is generally not instantaneous, but characterized by a steady damage accumulation.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales. A key limitation is that the models often do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles.
The objective of this paper is the presentation of numerical methods for the simulation of concrete under fatigue loading using a temporal multiscale method.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different time integration schemes.
Accurate models for the long term behavior of concrete structures are important to ensure a durable and reliable design.
A variety of interacting phenomena, such as the loss of prestress, the degradation due to chemical reactions or creep and shrinkage, influence the fatigue resistance. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required.
The presented fatigue model is an extension of a static damage model to allow easy coupling in a multiphysics context. The evolution equation of the damage driving variable is enhanced to allow damage growth below the static limit. The model is defined in the time domain and does not include the number of cycles as a parameter.
Thus, it can capture both static and cyclic failure.
Additionally, this allows calibrating the majority of the model parameters static experiments. The model is integrated by resolving each loading cycle, requiring about ten time steps per cycle. The high computational costs are handled via a time scale separation.
The short time scale describes one cycle with marginal changes in the internal variables. These changes are integrated along the large time scale of material deterioration. Various high-order time integration schemes are compared.
Wöhler curves relate loading amplitudes to the number of cycles that the material endures. They are used to validate the model against experimental data.
Fatigue models that accurately resolve the complex three-dimensional failure mechanisms of concrete are numerically expensive. Especially the calibration of fatigue parameters to existing Wöhler lines requires solving for thousands or millions of cycles and a naive cycle-by-cycle integration is not feasible.
The proposed adaptive cycle jump methods provide a remedy to this challenge.
They greatly reduce the numerical effort of fatigue simulations and provide the basis for a development of those models.