Biocide leaching was investigated for acrylate and polymer based coatings containing biocides either as liquid formulations or microcapsules. Laboratory and field tests indicate similar relations of results on carbendazim, diuron, terbutryn and OIT from different coatings in laboratory and field experiments. Emissions were higher in EN 16105 laboratory tests than from vertically installed test specimens exposed to weathering, and slower for microencapsulated biocides. Competing processes that cause losses of active substances can occur in both tests, but to a higher degree in field experiments. Emission curves related to runoff water were similar in repeated field experiments. Relative humidity, temperature and global radiation were identified as meteorological factors that affect leaching by complex interaction besides the amount of driving rain.
SETNanoMetro, a European Seventh Framework project, seeks to develop standard synthetic routes and metrological characterisation methods for the development and production of TiO₂ nanoparticles and nano-sized coatings with highly-defined, homogeneous and reproducible characteristics, including bulk structure, size, shape and surface structure. These materials are being tested for their potential in selected technological applications, including as coatings on bone-substituting prostheses. The objective of this study was to assess how variations in morphology and chemistry of nano-sized TiO₂ coatings affect their biocompatibility in vitro.
Geothermal brine is considered to be an aggressive
environment as it contains various dissolved salts.
Even though carbon steel is commonly used as a
construction material due to its machinability and
economical reason, it is susceptible to uniform and
localized corrosion in a high temperature and high
pressure system. Therefore, a coating system is
introduced to protect the carbon steel against
corrosion in such environment.
1. Carbon steel is susceptible to uniform corrosion in presence of oxygen, with corrosion rate of immersion at 150 °C of 0.39 mm/a.
2. Exposure test of carbon steel at 150°C and 10 bar (pressurized by Ar) results in pitting corrosion with depth of 19 µm and width 4 µm on average.
3. OCP measurement shows that the stability of measurement is reached after 40 hours of immersion in the solution.
4. EIS measurement is useful to observe the effect of temperature, immersion time, and coating composition on the corrosion processes of coated metals for use in geothermal application.
High-Resolution Continuum Source Molecular Absorption Spectrometry (HR-CS-MAS) with graphite furnace atomizers has been successfully used for the analytical determination of non-metals. The use of permanent modifiers (or coatings) for molecule formation is necessary, but their mechanisms of action remain unclear. In order to understand and improve the current analytical methods, we present a comprehensive mechanistic study of molecule formation in graphite furnaces: a key step into the recovery of analytical signals. Therefore, a well-known system for fluorine determination was studied: the molecule formation of CaF, with Zr as permanent modifier. Through a kinetic approach, an Arrhenius plot showed a pseudo first order reaction respect to F-. By spectroscopic methods (XPS, XAS, EDX) it was possible to elucidate an intermediate state. Here a mechanism is proposed, where ZrO2 works as heterogeneous catalyst: after a pyrolytic step, it is activated to the intermediate state of ZrO(OCaF) and at higher temperatures, CaF(g) is released from the zirconium-coated graphite surface. With this analytical information, improved surface modifications and coatings for graphite furnaces can be designed and some of them, for example with Zr nanoparticle and Zr xerogels are here presented.
Intumescent coatings are used for decades to increase the fire resistance of steel or wood constructions. Intermediate and full scale tests are used to assess their protection performance. For the product development and screening, cheaper and faster bench-scale tests are demanded that provide information about thermal protection, foaming dynamics and mechanical resistance. In the recent years, we have developed several bench-scale fire resistance tests and used them in different research and developing projects. The influence of distinct binders and fillers, respectively, was studied in intumescent coatings using the Standard Time Temperature modified muffle furnace (STT Mufu+). This bench-scale test evaluates the fire resistance (by means of temperature measurements) and the foaming behaviour (by means of a high-temperature endoscope) during a standard time-temperature exposure. The fire residues were suitable for advance residue analysing techniques like nondestructive μ-computed tomography (μ-CT). Also, scanning electron microscopy was used to investigate the microscopic structure of the surface and inside of the residues. The mechanical resistance of the residues was tested by an impact resistance experiment.
The binder influence on the insulation of the coating was small for the investigated systems. Nevertheless, it was interestingly noted, that coatings with high expansion did not provide the best protection. The great influence of the binder material on the inner structure of the foamed residues was revealed by the μ-CT images. Clear differing morphologies were observed. These led to distinct mechanical resistance properties of the tested coatings. Also the change of a low amount of fillers, such as fibres and clay was investigated with similar effects. What is more, a transition of the residue from black, carbonaceous foam with closed cells into an inorganic, residual open cell sponge occurs at high temperatures during the test. This transition is due to the loss of carbon; the change in microstructure is analysed by scanning electron microscopy.
The bench-scale tool presented outreaches screening; the investigation based on the STT Mufu+ delivers a deeper understanding of the phenomena controlling the performance of intumescent coatings.
Geothermal brine is a complex system containing a wide variety of dissolved salts resulting from the condition s in a geothermal well. These fluids lead to corrosion in pipes and other parts of geothermal system construction and necessitate intense research efforts in finding new suitable materials. Carbon steel is susceptible to corrosion in geothermal brine especially when it is exposed to a high temperature and high-pressure medium, which is considered to be an aggressive environment. An artificial geothermal water, bas ed on a brine composition found in Indonesia, was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO4 2-, 15 mg/l HCO3 -, 200 mg/l Ca 2+, 250 mg/l K+, and 600 mg/l Na+. In order to protect the bare material in geothermal application, it is necessary to either use high alloyed material s or coatings. In this research, a coating system consisting of polyaniline and silicon dioxide was investigated regarding its behavior to protect carbon steel. In detail, the effect of SiO2 and polyaniline (PANi) addition was evaluated by exposure and electrochemical tests for 7 days, i.e. electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP) at room temperature and 150 °C with 1 MPa pressure.
According to the results of the experiments carried out, the following points can be concluded:
1. Exposure tests showed that specimens with the addition of SiO2 particles and polyaniline particles exhibit better corrosion resistance than specimens with the addition of only polyaniline particles or binder only.
2. Open circuit potential measurements showed that in the beginning of the experiments, both coatings had an open circuit potential 100 mV higher than carbon steel. Within one day of immersion, the potential of carbon steel increased significantly, indicating the formation of oxide layer. After extended exposure the carbon steel potential sat between PS1 (which had higher potential) and PS2 (which had a lower potential) and all three were in the range –600 mV to –500 mV vs Ag/AgCl.
3. Both coatings PS-1 and PS-2 were degraded with increasing exposure time, shown by the decrease of absolute impedance value at low frequency range after 2, 4, and 6 days exposure.
4. Potentiodynamic test was performed after 3 hours and 6 days exposure, and it was shown that the coating in the initial stage exhibited more passive behavior than the specimens exposed for 6 days.
Lanthanide-based upconversion nanoparticles (UCNPs) like hexagonal 𝛽-NaYF4 UCNPs doped with Yb3+ and Er3+, which efficiently convert 976 nm light to ultraviolet, visible, and near infrared photons, offer new strategies for luminescence-based sensing, barcoding, and Imaging. Their upconversion (UC) luminescence (UCL) features like UCL intensity, quantum yield, relative spectral distribution / UCL luminescence color, and luminescence decay kinetics are, however, strongly influenced by particle size, dopant ion concentration, particle architecture, surface chemistry including presence and thickness of surface passivation and shielding shells, microenvironment/presence of quenchers with high energy vibrations, and excitation power density (P).
We present here a comprehensive study of the influence of excitation power density on the UCL features of different types of UCNPs, focusing on Yb3+ and Er3+ co-doped NaYF4 core-only and core-shell nanostructures with different sizes and doping ion concentration, which underlines the importance of P-dependent optimum dopant concentrations for UCNP performance and the potential of P-tuning of UCL.