A laser induced breakdown spectroscopy (LIBS) system was combined with the Gas Tungsten Arc (TIG) Welding process for the in situ monitoring of chemical compositions in austenitic stainless steels during welding. The purpose of this project is to develop a prototype of an online chemical composition control system for welding applications. One of the use cases of this new LIBS-based measurement system can be the controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions.
The Tungsten Inert Gas (TIG) welding process was combined with a Laser-Induced Breakdown Spectroscopy (LIBS) system for the in situ measurement of chemical compositions in austenitic stainless steels. The main aim of this project was the development of a prototype for a real-time chemical composition analysis system for welding applications. In principle, the measurement of the weld pool composition allows governing the weld pool solidification behaviour by controlling the welding parameters. This control loop allows avoiding weld defects.
Chemical compositions of the weld seam is from a metallurgical point of view the most critical parameter for the occurrence of weld defects. Additionally, this new LIBS-based measurement system can be used for the monitoring and controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions. Preliminary investigations show that the chemical composition measurement of welds with LIBS is possible during and after welding.
Chemical composition of the welding seam and HAZ has significant effect on weld quality. Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects.
Chemical compositions of the welds have significant effect on weld quality. Current inspection methods for the weld seams employ mostly post factum methods and cannot prevent weld defects.Elemental burn offs may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects.
Chemical composition of the welding seam and HAZ has significant effect on weld quality.
Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. “Industry 4.0” is the current trend of automation and data exchange in manufacturing technologies. With this trend “intelligent” welding machines will be developed. LIBS can provide significantly important online data for such systems.
In this presentation tribological investigations on steels, polymers and coatings in gaseous and liquid hydrogen are shown. For steels the results of show that although martensitic steel may suffer from hydrogen embrittlement, application e.g. in roller bearings is possible. On the other hand, martensitic transformation of austenitic steels may cause problems in the application of these materials. Furthermore, the tribological performance of polymer composites with and without solid lubricant fillers in gaseous and liquid hydrogen was investigated. In particular, PEEK- and PTFE-matrix compounds showed low friction and sufficient low wear under these conditions. Among the solid lubricants, carbon-based materials are appropriate for hydrogen applications. Several variants of DLC and ta-C materials were tested. Beside the results for hydrogen, also a comparison with CH4-environment is shown.