Nickel-iron-alloy modification to enhance additively welded microstructure for subsequent milling
(2021)
The aerospace industry uses nickel-iron-alloys to create moulding tools for composite materials because of the low coefficient of thermal expansion. These tools have a large-sized and complex structure, making them cost-intensive and difficult to manufacture. Therefore, the focus is set on additive manufacturing, which can additionally enable the repair of components in order to eliminate local defects. However, the process usually results in a heterogeneous microstructure and anisotropic mechanical properties. As there is a high demand for a precise and exact fit of the precision moulds and thus the surface quality, the welded components must be subsequently machined. Nickel-iron alloys are difficult to machine and an inhomogeneous microstructure also leads to unstable cutting forces.
Consequently, a refinement and homogenisation of the microstructure morphology is achieved through specific alloy modifications in order to stabilise and improve the subsequent machining process. Studies on the refinement of FeNi 36 based on vacuum arc melting furnaces are used as a starting point. Therefore, titanium and niobium are chosen as modification elements with a maximum 1 % weight percent and are added to nickel-iron base alloy. The elements are alloyed and build-up welded by using plasma-transferred-arc welding. The resulting microstructure morphology of the welded wall structure and the machining properties are then determined. Furthermore, the influence on the coefficient of thermal expansion is investigated in connection with the modification and the welding process itself. It can be shown that even small amounts of niobium have a significant influence on the structural morphology of the welded layers during plasma-transferred-arc welding.
Due to increasing requirements relating to the efficiency of highly stressed components in turbine or plant construction, the use of cost-intensive, difficult to process materials is increasingly necessary today. In this context, cobalt-chromium alloys in particular are highly resistant to thermal and mechanical stress, as well as to corrosive and abrasive loads. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components in many sectors. In order to realise a homogeneous and isotropic microstructure, alloy modifications are made to the alloy CoCr26Ni9Mo5W. For this purpose, hafnium and zirconium are added at 1 % and 0,33 % by mass each, as these elements are supposed to have a positive effect on the microstructure morphology. Plasma-Transferred-Arc is used for the welding tests. Wall structures are welded by multiple single-layer, overlapping welding beads on low-alloyed steel substrate (S355). The results show that the alloying elements hafnium and zirconium have a clear influence on the microstructure. Hardness measurements were also carried out. With each modification, the hardness is increased compared to the original material. The machining analyses show a reduction in cutting forces using ultrasonic assisted milling for high cutting speed and low feed rate.
Alloy 36 is an iron-based alloy with 36% nickel. It is used in applications in which dimensional stability is critical, such as molding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In addition, the manufactured components require subsequent machining surface finishing due to the high requirements. Nickel iron alloys are difficult to machine. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. Alloy modifications are made to the alloy 36. For this purpose, titanium, zirconium and niobium are added up to 1 % by mass each. Plasma-Transferred-Arc is used for the welding tests. The hardness profile is determined on the transverse section. The initial structure as well as the modifications have an austenitic structure. The microstructure of the modifications of Alloy 36 with 1% Ti and 1% Zr is not refined, instead the grain size increases.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. It was developed in 1897 by Guillaume and stands out for its very low thermal expansion coefficient. It is classified as a difficult-to-cut material and is commonly used for the production of fiber-reinforced composites in the field of mold construction. Additive manufacturing (AM) offers many economic advantages regarding the repair, modification and manufacture of entire components. Subsequent machining of the AM components is necessary to account for complex structures, final contours or defined surfaces. This is usually done using a tool with a geometrically defined cutting edge, i.e., milling processes. Surface integrity is determined by metallurgical (e.g., microstructure of the subsurface), topological (e.g., surface defects, roughness) and mechanical (e.g., residual stresses) factors, which is crucial in terms of component safety and performance. Modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), provide potentially improvement of the cutting situation of these components.
In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Nb up to a maximum of 1 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components.
The results show a significant positive influence of ultrasonic assistance on the resulting cutting force of both materials. The modification with 1% Ti shows a positive influence on the surface integrity, as the roughness of the conventional machining processes is lower compared to the initial alloy, which has to be confirmed in further experiments.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. The alloy has a remarkably low thermal expansion coefficient in certain temperature ranges. Therefore, it is used in applications in which dimensional stability is critical, such as moulding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. The results show that PTA welding cause numerous finely distributed precipitates with high silicon content.
Ni alloys are generally classified as difficult-to-cut materials and cost intensive. Additive manufacturing (AM) offers economic advantages. However, machining of these AM components is mandatory to create the final contour or surface. The inhomogeneous and anisotropic microstructure and properties of AM components causes an unstable cutting process. Moreover, undesirable tensile residual stresses are generated due to subsequent machining. In this investigation, the initial alloy 36 is modified with Ti and Nb up to 1.6 wt.-% and build-up welded via gas metal arc welding (GMAW) and plasma-transferred-arc (PTA). Then, finish-milling tests are carried out to investigate the influence of the modification as well as the cutting parameters on the resulting cutting force and the surface integrity. In addition, the conventional milling process (CM) is compared with the ultrasonic-assisted milling process (US), which has a significant influence on the machinability as well as on the surface integrity.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. It was developed in 1897 by Guillaume and stands out for its very low thermal expansion coefficient. It is classified as a difficult-to-cut material and is commonly used for the production of fiber-reinforced composites in the field of mold construction. Additive manufacturing (AM) offers many economic advantages regarding the repair, modification and manufacture of entire components. Subsequent machining of the AM components is necessary to account for complex structures, final contours or defined surfaces. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. Machining tests were carried out, to investigate the influence of ultrasonic assistance and the effects of modification elements Ti, Zr and Hf on the occurring cutting forces, temperatures and resulting surface integrity of the AM components made of alloy 36 and their modifications. The results show a significant positive influence of ultrasonic assistance on the resulting cutting force as well as on the roughness of all materials investigated.